Potasyum katkısının YbCO yüksek sıcaklık süperiletkenlerinin elektriksel ve magnetik özellikleri üzerine etkisi
The Effect of potassium doping on electrical and magnetic properties of YbCO high temperature superconductors
- Tez No: 83326
- Danışmanlar: DOÇ. DR. SELAHATTİN ÇELEBİ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: YBCO Yüksek Sıcaklık Süperiletkenleri, K-katkısı, Aktivasyon Enerjisi, Kritik Akım, Isıl Destekli Akı Akışı (TAFF), AC Alınganlık, Elektriksel özellikler, Manyetik özellikler, Potasyum, Süper iletkenler, YBCO High Temperature Superconductors, K-doping, Activation Energy, Critical Current, Thermally Activated Flux Flow (TAFF), AC Susceptibility. VI, Electrical properties, Magnetic properties, Potassium, Superconductors
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, YBCO (123) yüksek sıcaklık süperiletkenlerinde potasyum (K) katkısının etkisi, XRD, elektriksel özdirenç ve kritik akım yoğunluğu ölçümleri ile araştırıldı. Yı_0>2xBa2-o,2xKxCu3Oy (x=0 ve x=0,4) kompozisyonlu numuneler katı hal tepkime yöntemi ile hazırlandı. Süperiletken numuneler XRD ölçümleri ile karakterize edildi. XRD verilerinden saf YBCO ve K-katkılı YBCO'nun ortorombik yapıya sahip olduğu görüldü. Elektriksel özdirenç ölçümleri, kritik sıcaklık Tc'nin K-katkı işleminden dolayı, bir miktar düşük sıcakhğa kaydığını gösterdi. Bu işlem aynı zamanda ısıl destekli akı akışı (TAFF) için aktivasyon enerjisini ve kritik akım yoğunluğunu azalttı. Her iki numune için, 0-760 mT magnetik alan aralığında özdirenç geçişleri, sıfir alan altoda soğutma işlemi uygulanarak gerçekleştirildi. TAFF için aktivasyon enerjileri, bu magnetik alan aralığı altında ölçülen sıcakhğa karşı özdirenç eğrilerinin Arrhenius çiziminden elde edildi. Kritik akım yoğunluğunun magnetik alan bağlılığı 77 K'de, sıfır alan allında soğutmadan sonra, uygulanan magnetik alan artırılırken ve azaltılırken ölçüldü. Saf YBCO numunesi için, alanı artırma ve uygulanan 6 mT'lık bir alandan sonra azaltma yönünde kritik akım histeresizi gözlendi. AC alınganlık ölçümünden, saf YBCO numunesi için geçiş sıcaklığı belirlendi ve sıcakhğa bağlı kritik akım yoğunluğu Clem modeli kullanılarak hesaplandı. Bu değerlerin dört nokta yöntemi ile 77 K'de elde edilen kritik akım yoğunluğu değerleri ile uyum içinde olduğu görüldü.
Özet (Çeviri)
The Effect of Potassium Doping on Electrical and Magnetic Properties of YBCO High Temperature Superconductors In this study, the effect of potassium (K) doping on YBCO (123) high temperature superconductors has been investigated in terms of XRD, electrical resistivity and critical current density measurements. The samples with nominal compositions Y1^2xBa2-o,2XKxCu30y (x=0 and x=0,4) were prepared by solid state reaction method. The superconducting samples were characterized by XRD measurements. It was seen from XRD data that the pure YBCO and K-doped YBCO had orthorombic structure. The electrical resistivity measurements showed that the critical temperature Tc shifted slightly to lower temperature due to K-doping process. This process also decreased the activation energy for thermally activated flux flow (TAFF) and the transport critical current density. The resistive transitions in the magnetic field range of 0-760 mT were performed employing zero field cooling procedure for both samples. The activation energy values for TAFF were obtained from the Arrhenius plot of the resistivity versus temperature curves which were measured under this magnetic field range. The magnetic field dependence of the critical current density was measured at 77 K after zero field cooling when the applied magnetic field was impressed and removed. For the pure YBCO sample, the transport critical current hysteresis was observed in the field increasing and decreasing direction after an excursion of the field to 6 mT. From AC susceptibility measurement, the transition temperature was determined and the temperature dependent critical current density was calculated using Clem model for the pure YBCO sample. It was seen that these values were in agreement with the values of the critical current density obtained from four probe tecnique at 77 K.
Benzer Tezler
- Kurbağa izole özofagus sirküler düz kas preparatlarında potasyum gevşemeleri ve nitrerjik sistem
Relaxations caused by potassium ion of isolated frog oesophageal sircular smooth muscle preparations and nitrergic system
YUSUF KARATAŞ
- Sıçan deneysel adjuvan artrit modelinde evre farklılığına göre izole torasik aortta vasküler yanıt değişiklikleri
Başlık çevirisi yok
BUKET DEMİRCİ
Tıpta Uzmanlık
Türkçe
2001
Eczacılık ve FarmakolojiEge ÜniversitesiFarmakoloji Ana Bilim Dalı
DOÇ.DR. SİBEL ÜLKER GÖKSEL
- Farkılı bitkisel yağların eritme peyniri yapımında kullanım imkanları üzerine bir araştırma
A Study on use possibilities of different vegetable oils in processed cheese production
HÜSEYİN TÜRKOĞLU
Doktora
Türkçe
2000
Gıda MühendisliğiAtatürk ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DOÇ.DR. ABDULLAH ÇAĞLAR
- Sağlam, pişirilmiş ve çimlendirilmiş çeşitli baklagil katkılarıyla, mayasız ve maya ilavesiyle fermente edilen tarhananın bazı fiziksel, kimyasal ve besinsel özellikleri üzerine bir araştırma
Başlık çevirisi yok
SELMAN TÜRKER
Doktora
Türkçe
1991
Gıda MühendisliğiAtatürk ÜniversitesiGıda Bilimi ve Teknolojisi Ana Bilim Dalı
PROF.DR. ADEM ELGÜN