YBa2Cu3O7-x/polimer karışım numunelerinin yapısal ve fiziksel özelliklerinin incelenmesi
The research of microstructual and physical properties of YBa2Cu3O7-x/polymer composite samples
- Tez No: 96811
- Danışmanlar: PROF. DR. EKREM YANMAZ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: YBa2Cu307-x, Polimer, Brinell Sertlik Ölçme Yöntemi, Magnetik Kaldırma Kuvveti, Kaldırma kuvveti, Polimerler, Sertlik ölçme, YBa2Cu3O7-x, YBa2Cu307.x, Polymer, Brinell Hardness Measuring Method, Magnetic Levitation Force VI, Lift force, Polymers, Hardness measurement, YBa2Cu3O7-x
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fen Bilimleri Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, YBa2Cu307-x /Polimer karışım numunelerinin yapısal, magnetik ve fiziksel özellikleri XRD, optik, sertlik, magnetik kaldırma ve indüktans değişim ölçümleri ile incelendi X-ışını kınmrn desenleri incelendi, numunelerin içerdiği fazlar tespit edildi. Numune içinde YBa2Cu30?-x miktarı arttıkça 123 süperiletken piklerin sayısı ve şiddetinde artma görüldü. Brinell Sertlik Ölçme Yöntemi ile belirlenen serlik değerlerinde, karışım numunelerinde YBa2Cu307.x oranı arttıkça numunenin sertliğinin arttığı bulundu. YBa2Cu307-x /Polimer karışım numunelerinin magnetik kaldırma kuvveti, uzaklığa karşı kuvvet ölçümü ile belirlendi. Karışım numuneleri saf sinterlenmiş süperiletkenlerle benzer bir kaldırma özelliği gösterdi. YBa2Cu307-x /Polimer karışım numunelerinin magnetik alan altındaki davranışları sıcaklığa bağlı indüktans değişim ölçümleriyle belirlendi. Karışımlar geniş diamagnetik duyarlılık ve şiddet gösterdi
Özet (Çeviri)
SUMMARY The Research of Microstructual and Physical Properties of YBa2Cu307-x /Polymer Composite Samples In this study the rnicrostructural, magnetic and physical properties of YBa2Cu307-x /Polymer composite samples were examined with optical, hardness, magnetic levitation and change of inductance. X-ray diffraction patterns were analysed and phases that composite samples contain were determined. As YBa2Cu307-x quantity increase, it was seen that the number and strength of 123 superconductor phases increased. Hardness values of composite samples were determined with Brinell Hardness Measuring Method. It is observed that in composite samples as YBa2Cu3O7.xra.te increased, hardness of samples also increased. The magnetic levitation force of YBa2Cu307.x /Polymer composite samples were determined with force versus distance measurement technique. Composite sample showed similar levitation properties as pure sintered superconductors. The behaviours of YBa2Cu307.x /Polymer composite samples under magnetik field were determined with inductance variation measurements. It is determined that composites present wide diamagnetflc sensitive and intensity.
Benzer Tezler
- YBa2Cu3O7-X'in oksijen stokiyometrisinin katıhal elektrokimyasal yöntemle tayini
Başlık çevirisi yok
HÜSEYİN ERAY BERTİZLİOĞLU
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Ana Bilim Dalı
PROF.DR. TEZER FIRAT
- YBa2Cu3O7-x süperiletkenlerinin“eritme-hızlı soğutma-büyüme”yöntemi ile üretilmesi, fiziksel ve yapısal özelliklerinin incelenmesi
The preparation of YBa2Cu3O7-x superconductors by“flame-quench-melt-growth”(FQMG) method, investigation of microstructure and physical properties
ALEV ATEŞ
Yüksek Lisans
Türkçe
1998
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. EKREM YANMAZ
- Titanyumdioksit (TiO2) katsayısının YBa2Cu3O7-x süperiletkenlerinin yapısal, fiziksel ve manyetik özellikleri üzerine etkisi
Magnetic, physical and structural properties of melt textured YBa2Cu3O7-x with TiO2 doped
SÜLEYMAN BALCI
Yüksek Lisans
Türkçe
2000
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. EKREM YANMAZ
- Yüksek sıcaklık süperiletken malzemelerin hazırlanması ve incelenmesi
Preperation and investigation of high temperature superconducting materials
AYTEN KAYNAR
Yüksek Lisans
Türkçe
1992
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HALUK MUTLU
- Effect of nickel and titanium substitution on the superconducting properties of YBa2 Cu3O7-x system
Başlık çevirisi yok
M.ALİ AKBAŞ