YBa2Cu3O7-x süperiletkenlerinin“eritme-hızlı soğutma-büyüme”yöntemi ile üretilmesi, fiziksel ve yapısal özelliklerinin incelenmesi
The preparation of YBa2Cu3O7-x superconductors by“flame-quench-melt-growth”(FQMG) method, investigation of microstructure and physical properties
- Tez No: 78095
- Danışmanlar: DOÇ. DR. EKREM YANMAZ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: YBa2Cu307_x, FQMG Yöntemi, Ag Katkısı, Oksijen Tavlama, Kritik Sıcaklık AC Alınganlık, Kritik Akım Yoğunluğu, Aktivasyon Enerjisi, TAFF. VI, Elektriksel direnç, Erime, Soğutma, Süper iletkenler, İnce filmler, YBa2Cu307_x, FQMG Method, Ag Addition, Magnetic Field, Oxygen Annealing, Critical Temperature, AC Susceptibility, Critical Current Density, Activation Energy, TAFF. VII, Electrical resistance, Melting, Cooling, Superconductors, Thin films
- Yıl: 1998
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, Eritme-Hızlı Soğutma-Büyütme (FQMG) metodu kullanılarak hazırlanan YBCO-123 süperiletkenlerinin yapısal ve fiziksel özellikleri XRD, optik, elektriksel özdirenç ve AC alınganlık ölçümleri kullanılarak araştırıldı. Büyük taneli, magnetik alana dayanıklı YBa2Cu307.x süperiletkeni için uygun kristal büyütme sıcaklığının 1050°C ve büyütme süresinin ise 10 saat ve üzeri olduğu bulundu. Uygun miktarda gümüş katkısı süperiletken fazın oluşumunu artırdı ve süperiletkenliğe geçiş sıcaklığım az miktarda yükseltti. Ag katkılı süperiletkenler üzerinde oksijen tavlamamn etkisi incelendi, süperiletkenliğe geçişin daha keskin ve Tc^ero'nin belirgin bir şekilde arttığı görüldü. Gümüş katkılı ve katkısız numunelerin magnetik alan altındaki davranışları dış magnetik alan altında özdirenç ölçümleri ile belirlendi. Magnetik alan altında gümüş katkılı numunelerin daha düşük sıcaklıkta süperiletkenliğe geçtiği görüldü. TAFF bölgesi için aktivasyon enerjileri, tüm numunelerin magnetik alan altında ölçülmüş, lnp'nun T"1 'e göre çizilmiş özdirenç eğrilerinin eğimli kısmından hesaplandı. Aktivasyon enerjisinin gümüş miktarı ve magnetik alan artarken azaldığı görüldü.
Özet (Çeviri)
SUMMARY The Preparation of YBa2Cu307.s Superconductors by“Flame-Quench-Melt- Growth”(FQMG) Method, Investigation of Microstructure and Physical Properties In this work, the microstructural and physical properties of YBCO-123 superconductors prepared by the Flame-Quench-Melt-Growth (FQMG) method have been investigated in terms of XRD, optical, electrical resistivity and AC susceptibility measurements. It was found that the optimum growth temperature and time were to be 1050°C and over 10 h for YBa2Cu307.x superconductors with large grain and enduring in high magnetic field. The appropriate amount of silver addition enhances the formation of the superconducting phase and slightly increases the transition temperatures. The effect of oxygen annealing on the Ag-added samples was examined and the curves of resistive transition were became sharper and Tc>zero significantly increased. The magnetic behaviour of YBCO with silver and without silver were determined by measurements of the resistivity in an external magnetic field. It was found that samples with silver showed a lower transition temperature in a magnetic field. The activation energy, U0, for TAFF was estimated for all samples from the slope of the Arrhenius plot of lnp versus T1 which measured under magnetic field. It was found that the activation energy of the samples decreases with increasing silver content and magnetic field.
Benzer Tezler
- Titanyumdioksit (TiO2) katsayısının YBa2Cu3O7-x süperiletkenlerinin yapısal, fiziksel ve manyetik özellikleri üzerine etkisi
Magnetic, physical and structural properties of melt textured YBa2Cu3O7-x with TiO2 doped
SÜLEYMAN BALCI
Yüksek Lisans
Türkçe
2000
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. EKREM YANMAZ
- Gümüş difüzyonunun YBaCuO süperiletkenlerinin yapısal ve süperiletkenlik özelliklerine etkisi
Başlık çevirisi yok
UĞUR KÖLEMEN
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. MUSTAFA ALTUNBAŞ
- YBa2Cu3O7-X'in oksijen stokiyometrisinin katıhal elektrokimyasal yöntemle tayini
Başlık çevirisi yok
HÜSEYİN ERAY BERTİZLİOĞLU
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Ana Bilim Dalı
PROF.DR. TEZER FIRAT
- YBa2Cu3O7-x/polimer karışım numunelerinin yapısal ve fiziksel özelliklerinin incelenmesi
The research of microstructual and physical properties of YBa2Cu3O7-x/polymer composite samples
BURCU KOÇHAN
Yüksek Lisans
Türkçe
2000
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFen Bilimleri Eğitimi Ana Bilim Dalı
PROF. DR. EKREM YANMAZ
- Yüksek sıcaklık süperiletken malzemelerin hazırlanması ve incelenmesi
Preperation and investigation of high temperature superconducting materials
AYTEN KAYNAR
Yüksek Lisans
Türkçe
1992
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HALUK MUTLU