Titanyumdioksit (TiO2) katsayısının YBa2Cu3O7-x süperiletkenlerinin yapısal, fiziksel ve manyetik özellikleri üzerine etkisi
Magnetic, physical and structural properties of melt textured YBa2Cu3O7-x with TiO2 doped
- Tez No: 96786
- Danışmanlar: PROF. DR. EKREM YANMAZ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Ayrıştırma, Manyetik özellikler, Süper iletkenler, Titanyum dioksit, High-Tc Superconductors, TİO2 substitution, decomposition, Magnetic Properties, Levitation Force. VI, Superconductors, Titanium dioxide
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET YBa2Cu3Ö7-s bulk numuneler, 0-10 wt% aralığında titanyum katkı yapılarak FQMG yöntemiyle üretildi. Numunelerin mikroyapılan XRD analizi ve optik mikroskopla belirlendi. Y123 içerisine TİO2 katkı miktarının %1'den %5'e artırılmasıyla, geçiş sıcaklığının bir miktar düştüğü, %7 ve 10 oranlarındaki katkılarda ise önemsenmeyecek kadar bir artışa sebep olduğu gözlendi. Manyetik ölçümler, farklı manyetik alanlarda, sıfır alanda soğutma(ZFC) ve alan altında soğutma(FC) rejimlerinde, 77-300 K sıcaklık aralığında 1 kHz' de çalışan indüktansmetre yardımıyla gerçekleştirildi. Numunelerin tipik itici ve çekici manyetik kuvvetleri, Nd-Fe-B mıknatıs ile numune arasındaki uzaklığın fonksiyonu olarak sıfır alanda soğutma işlemiyle gerçekleştirildi. Anahtar Kelimeler Yüksek Sıcaklık Süperiletkenler, TİO2 Katkısı, Kaldırma Kuvveti dekompozisyon, Manyetik özellikler.
Özet (Çeviri)
SUMMARY Magnetic, Phsical and Structural Properties of Melt Textured YBa2Cu307-x Superconductors with TİO2 Doped Bulk YBa2Cu307-x samples, doped with TİO2 in the range 0-10 wt.% have been prepared by the Flame-Quench-Melt-Growth (FQMG) method and their microstructures have been defined by XRD analysis and optical microscopy. It was found that increasing the content of TİO2 in Y123 from 1% to 5% caused a decrease of superconducting transition temperature, and from 7-10% wt. caused a slight increase of transition temperature. Magnetic measurements in the zero field cooled (ZFC) and field cooled (FC) regimes for different magnetic fields have been performed on these samples in the temperature range 77-300 K using an inductance-meter operating at 1 kHz. Typical repulsive and attractive magnetic forces as a function of distance, and magnetic history between a permanent magnet and YBCO sample cooled with and without magnetic field are described.
Benzer Tezler
- Effect of ionic species on the photocatalytic removal of humic substances in natural waters
İyonların doğal sularda bulunan humik maddelerin fotokatalitik giderimine olan etkileri
GONCA AKDOĞAN
- Fotodegredasyon ile lineer alkil benzen sülfonat (LAB) ve fenol giderimi
Başlık çevirisi yok
FERYAL ÖZTÜRK
Yüksek Lisans
Türkçe
1994
Çevre MühendisliğiOndokuz Mayıs ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DOÇ. DR. A. NUR ONAR
- TiO2 photocatalytic degradation of substituted resorcinols: Kinetic and mechanistic studies
Takılandırılmış resorsinollerin TiO2 yarıiletkeni ile fotokatalitik degradasyonu: Kinetik ve mekanistik çalışmalar
AYŞE NEREN ÖKTE
- TiO2 ince filmlerinin optik parametrelerinin tayini
Başlık çevirisi yok
NURTEN ÖNCAN
Doktora
Türkçe
1985
Fizik ve Fizik Mühendisliğiİstanbul ÜniversitesiFizik Ana Bilim Dalı
DOÇ.DR. ÜLKÜ CANTÜRK
- ZrO2-TiO2 ince filmlerinin oluşturulması ve karakterizasyonu
Preparation and characterization of ZrO2-TiO2 thin films
SEMA TIĞLI