Monolitik zirkonya restorasyonlarının tekrarlayan fırınlamaları ile renk, yüzey özelliği ve faz değişiminin incelenmesi
The investigation of color, surface properties, and phase transformation in monolithic zirconia restorations after repeated firings
- Tez No: 930267
- Danışmanlar: PROF. DR. GÖKHAN AKGÜNGÖR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Monolitik Zirkonya, Tekrarlayan Fırınlama, Translusentlik, Renk, Monolithic Zirconia, Repeated Firing, Translucency, Color
- Yıl: 2025
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Karadağ E., (2025). Monolitik zirkonya restorasyonlarının tekrarlayan fırınlamaları ile renk, yüzey özelliği ve faz değişiminin incelenmesi. İstanbul Üniversitesi Sağlık Bilimleri Enstitüsü, Protetik Diş Tedavisi ABD. Doktora Tezi. İstanbul. Monolitik zirkonya restorasyonlar günümüzde hem posterior hem de anterior bölgelerde yaygın olarak kullanılmaktadır. Mevcut araştırmanın amacı anterior bölgelerde daha iyi bir estetik başarı yakalamak için monolitik zirkonya restorasyonlarda cut-back işlemi uygulamasına bağlı olarak restorasyonun tekrarlayan düşük ısı fırınlamaları ile renk değişimini, faz değişimini ve yüzey özelliklerini değerlendirmektir. Materyal olarak 4Y-TZP içerikli monokromatik iki farklı monolitik zirkonya blok; Vita YZ/ST Color (Vita Zahnfabrik, Almanya) ve Amanngirrbach Ceramill Zolid HT (Amanngirrbach/ Avusturya) kullanılmıştır. Exocad (Exocad Dentalcad 3.0 Galway, Almanya) programı ile hazırlanan tasarım CAD/CAM sistemine aktarılarak monolitik zirkonya bloklardan örnekler hazırlanmıştır. Hazırlanan 72 adet disk şeklindeki örnek üretici firmanın belirttiği talimatlar doğrultusunda sinterleme protokollerine göre Hızlı sinterleme ve Standart sinterleme işlemine tabi tutulmuştur. Sinterleme işlemine göre gruplara ayrılan örnekler sonrasında 1, 2 ve 3 defa düşük ısı fırınlaması olacak şekilde gruplara ayrılmıştır. Hazırlanan bütün gruplar spektrofotometre cihazı ile siyah ve beyaz zeminde ölçülerek (CIE) L*, a* ve b* renk koordinatları not edilmiş ve TP00 değerleri hesaplanmıştır, ayrıca nötral gri zeminde de ölçüm yapılarak ∆E00 değerleri tespit edilmiştir. Gruplar içerisinden rastgele seçilen birer adet örnek taramalı elektron mikroskobu (SEM) ile analiz edilmiştir. Tetragonal-monoklinik faz değişimleri de X ışını kırınım tekniği (XRD) ile hesaplanmıştır. Tekrarlayan fırınlamalar ile örnekler arasında ΔE değerinde farklılıklar olduğu ancak bu değişikliklerin göz ile algılanabilir değerin (ΔE <1) altında bir değerde olduğu tespit edilmiştir. Materyallerin sinter sonrası TP değerleri ile 1.fırınlama sonrası TP değerleri karşılaştırıldığında bütün gruplardan anlamlı bir değişim gerçekleşmemiştir. 1.fırınlama ile 2.fırınlama sonrası TP değerlerini karşılaştırıldığında bütün gruplarda TP de anlamlı bir düşüş gerçekleşmiştir (AmannGirrbach Hızlı Sinter p<0,028*, AmannGirrbach Standart Sinter p<0,001*, Vita Hızlı Sinter p<0,012*, Vita Standart Sinter p<0,008*). Elde edilen bulgular monolitik zirkonyum restorasyonlarının optik özelliklerinin iyileştirilmesi için fırınlama işlemlerinin optimize edilmesi gerektiğini ortaya koymaktadır.
Özet (Çeviri)
Karadağ E. (2025). Investigation of Color, Surface Properties, and Phase Changes of Monolithic Zirconia Restorations with Repeated Firings. Istanbul University, Institute of Health Sciences, Department of Prosthetic Dentistry. Doctoral Thesis. Istanbul. Monolithic zirconia restorations are widely used in both posterior and anterior regions today. The purpose of this study is to evaluate the color changes, phase changes, and surface properties of monolithic zirconia restorations subjected to repeated low-temperature firings after the cut-back process, aiming for better aesthetic success in the anterior regions. As materials, two different monolithic zirconia blocks with 4Y-TZP content Vita YZ/ST Color (Vita Zahnfabrik, Germany) and Amann Girrbach Ceramill Zolid HT (Amanngirrbach/ Austria) were used. Samples were prepared from monolithic zirconia blocks using designs created with the Exocad (Exocad DentalCAD 3.0 Galway, Germany) software and transferred to a CAD/CAM system. A total of 72 disk-shaped samples were prepared and subjected to sintering protocols according to the manufacturer's instructions, namely, Fast Sintering and Standard Sintering. The samples, divided into groups based on the sintering protocol, were further subdivided into groups for 1, 2, and 3 rounds of low-temperature firings. All groups were measured using a spectrophotometer on black and white backgrounds, and the L*, a*, and b* color coordinates were recorded according to the CIE system. TP00 values were calculated, and ∆E00 values were determined by measurements on a neutral gray background. One randomly selected sample from each group was analyzed using Scanning Electron Microscopy (SEM). Tetragonal-to-monoclinic phase changes were also calculated using X-ray Diffraction (XRD). It was found that there were differences in ∆E values among the samples with repeated firings, but these differences remained below the visually perceptible threshold (ΔE <1). When the TP values of the materials after sintering were compared with the TP values after the first firing, no significant changes were observed in any group. However, when comparing the TP values after the first and second firings, a significant reduction in TP was observed in all groups (Amann Girrbach Fast Sinter p<0.028*, Amann Girrbach Standard Sinter p<0.001*, Vita Fast Sinter p<0.012*, Vita Standard Sinter p<0.008*). The findings indicate that the firing processes of monolithic zirconia restorations need to be optimized to improve their optical properties.
Benzer Tezler
- Translüsent monolitik zirkonya seramik sistemlerinde düşük ısı bozunmasının iki eksenli bükülme dayanıklılığı ve faz değişimine etkisinin incelenmesi
Evaluation of the effect of low temperature degradation on biaxial flexural strength and phase change of translucent monolithic zirconia ceramic systems
GÜLSÜM DOĞRU
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HANDAN YILMAZ
- Tekrarlanan fırınlama işleminin zirkonya kronların marjinal uyum ve optik özelliklerine etkisinin araştırılması
Investigation of the effect of repeated firing on the marginal fit and optical properties of zirconia crowns
AYŞEGÜL ÜÇDAL ASLAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiUşak ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BENGİSU YILDIRIM
- Zirkonya materyallerinin farklı yüzey bitirme işlemleri sonrası renk değişiminin karşılaştırılması
Comparison of color change of zirconia materials after different surface finishing processes
SERAP FALCI
Doktora
Türkçe
2025
Diş HekimliğiBaşkent ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SELİM ERKUT
- Monolitik zirkonya ve zirkonyum destekli posterior köprü restorasyonlarının bir yıllık klinik takibi
One-year clinical follow-up of monolithic zirconia and zirconia supported posterior bridge restorations
ELÇİN KESKİN ÖZYER
Doktora
Türkçe
2019
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ERKUT KAHRAMANOĞLU
- Posterior üç üyeli monolitik zirkonya köprü restorasyonlarının çiğneme simülasyonu sonrası faz dönüşümünün değerlendirilmesi
Evaluation of phase transformation of posterior three-unit monolithic zirconia bridge restorations after chewing simulation
GÜLBAHAR ERDİNÇ
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiEskişehir Osmangazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MEHMET BÜLBÜL