Hızlı soğutulmuş Cu-Sn ve Cu-Zn-Sn alaşımlarında şekil hatırlama özelliklerinin incelenmesi

Başlık çevirisi mevcut değil.

PDF İndir

  1. Tez No: 50938
  2. Yazar: RAŞİT ZENGİN
  3. Danışmanlar: PROF. DR. MEHMET CEYLAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
  6. Anahtar Kelimeler: Hızlı katılaştırma fırını, Cu-Sn ve Cu-Zn-Sn alaşımları, termal analiz ölçümleri, dönüşüm sıcaklıkları, yapı tayini, Alaşımlar, Bakır, Kalay, Çinko, Şekil hatırlama özelliği, Fast Solidification Furnace, Cu-Sn and Cu-Zn-Sn Alloys, Thermal Analysis Measurements, Transformation Temperatures, Structure Designation, Alloys, Copper, Tin, Zinc, Shape memory property
  7. Yıl: 1996
  8. Dil: Türkçe
  9. Üniversite: Fırat Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Belirtilmemiş.
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Şekil hatırlamalı alaşımlar soğutma veya zor uygulama ile martensit faz dönüşümlerine uğrarlar ve martensitik şartlarda içten kusurlu yapılara sahiptirler. Soy metal bazlı Cu-Sn alaşımlarında, martensitik dönüşüm, D03 düzenine sahip kübik bir yapıdan uzun periyotlu 18R yapıya geçişle meydana gelir. Bununla birlikte Cu-Zn-Sn alaşımlarında ise bu dönüşüm D03 ( veya B2) düzeninden 18R (veya 9R) yapısına dönüşerek gerçekleşir. Metal ve alaşımların eritildikten sonra hızlı soğutulup ince plaka şeklinde elde edilmesini sağlayacak bir fırın sistemi imal edilmiştir. Bu sistem kulanılarak şekil hatırlamalı Cu-%24.2Sn alaşımı ince plaka şeklinde ve Cu-%33.8Zn- %3. 1Sn a'aşımı da külçe şeklinde elde edilmiştir. Eldo edilen alaşımlar üzerinde; makroskobik şekil hatırlama olayı gözlemleri, lermogravimetrik analiz (TGA); diferansiyel termal analiz (DTA); diferansiyel taramalı kalorimetre (DSC), x-ışınlan difraksiyonu ve metalografik gözlemler yapılmıştır.Bu gözlemler sonucunda Cu-Sn alaşımı makroskobik şekil hatırlama olayı göstermiş, Cu-Zn-Sn alaşımı göstermemiştir. TGA Ölçümlerinde numunelerin kütlelerindeki artış oksitlenmeden kaynaklanmıştır. DTA ölçümlerinde katı -> katı faz dönüşümlerinin olduğu belirlenmiştir. DSC ölçümleri sonucunda da austenit başlama (A,,) ve austenit bitiş (Af) sıcaklıkları ölçülmüştür. Bu alaşımlar oda sıcaklığında austenit yapıda olduğundan. x-ışınları difraktogramlarından elde edilen pikler de austenit faza ait piklerdir.

Özet (Çeviri)

Shape memory alloys undergo to the martensitic transformation on cooling or applying stress, and have internally defects structures in martensitic conditions. In noble metal Cu-Sn alloys, martensitic tranformation occurs from a cubic structure with D03 order to a long period layered structure 18R, while this transformation realizes from D03 ( or B2 ) order tol8R ( or 9R ) structure in Cu-Zn-Sn alloys. A furnace system has been constructed to obtain metal and alloys as thin ribbons by means of rapid cooling after melting. By using the system, shape memory Cu-%24.2Sn alloy has been obtained in thin ribbon form and Cu-%33.8Zn-%3, ISn alloy also has been obtained in bulk form. On the formed alloys, the following procedures have been done; the observations of macroscopic shape memory effects and metalographic, the measurement of thermogravimetric analysis ( TGA ), differential thermal analysis ( DTA ), differential scanning calorimeter ( DSC ) and the analysis of x-ray diffraction. In the measurement of TGA, increament in the mass of samples has occured due to oxidation. In the measurement of DTA it has been determined that solid -> solid phase transformation has occured. Austenite starting ( Ag ) and austenite finishing ( Af ) temperatures have been measured by means of DSC.measurement. The peaks evaluated from x-ray diffraction belong to austenite phase since these alloys are in the form of austenite at room temperature.

Benzer Tezler

  1. Tez No

    39201

    Ejection from rapidly depressurized vessels containing bubbly - liquid two - phase fluid

    Gaz kabarcıklı sıvı iki fazlı akışkan tanklarından ani basınç düşüşü yaratarak fışkırma

    ŞÜKRÜ BALTA

    Yüksek Lisans

    İngilizce

    İngilizce

    1993

    Makine Mühendisliğiİstanbul Teknik Üniversitesi

    PROF. DR. HASAN FEHMİ YAZICI

  2. Tez No

    28691

    Controlling of cooling rate to improve the flotation behavior of copper slags at Samsun copper plant

    Samsun'daki bakır tesisi curuflarının flotasyon özelliklerini düzeltmek amacıyla soğutma hızının kontrolu

    YUSUF ZİYA AKGÖK

    Yüksek Lisans

    İngilizce

    İngilizce

    1993

    Maden Mühendisliği ve MadencilikOrta Doğu Teknik Üniversitesi

    Maden Mühendisliği Ana Bilim Dalı

    PROF. DR. GÜLHAN ÖZBAYOĞLU

  3. Tez No

    68781

    Microstructure and high temperature phase studies of rapidly solidified AI-Fe-V-Si alloy

    Hızlı soğutulmuş AI-Fe-V-Si alaşımının mikroyapı ve yüksek sıcaklık faz çalışması

    SUAT KEMAL ANGI

    Yüksek Lisans

    İngilizce

    İngilizce

    1997

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. ALİ KALKANLI

  4. Tez No

    93304

    Mikrostructural and consolidation studies of air-atomized Al-Fe-V-Si and Al-Cr-Fe alloy powders

    Hızlı soğutulmuş Al-Fe-V-Si ve Al-Cr-Fe alaşımlarının mikroyapı ve sinterleme çalışması

    ÖZGÜR GENCEL

    Yüksek Lisans

    İngilizce

    İngilizce

    2000

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    YRD. DOÇ. DR. BİLGEHAN ÖGEL

    YRD. DOÇ. DR. ALİ KALKANLI

  5. Tez No

    1430

    Nötronlarla ışınlamanın ve su vermenin p-tipi silisyumun özdirenci ve taşıyıcı yoğunluğu üzerine etkileri

    Başlık çevirisi yok

    MUHAMMET YILDIRIM

    Yüksek Lisans

    Türkçe

    Türkçe

    1987

    Fizik ve Fizik MühendisliğiAtatürk Üniversitesi

    Fizik Ana Bilim Dalı

    DOÇ.DR. YAHYA KEMAL YOĞURTÇU

Geri Dön