Mikrostructural and consolidation studies of air-atomized Al-Fe-V-Si and Al-Cr-Fe alloy powders
Hızlı soğutulmuş Al-Fe-V-Si ve Al-Cr-Fe alaşımlarının mikroyapı ve sinterleme çalışması
- Tez No: 93304
- Danışmanlar: YRD. DOÇ. DR. BİLGEHAN ÖGEL, YRD. DOÇ. DR. ALİ KALKANLI
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Hızlı katılaşma, Al-Fe-V-Si ve Al-Cr-Fe alaşım tozlan, mikroyapı, sıcak haddeleme. VI, Alaşımlar, Haddeleme, Katılaşma, Presleme, Sıcak presleme, Sıcaklık, Rapid solidification, Al-Fe-V-Si and Al-Cr-Fe alloy powders, microstructure, hot rolling. IV, Alloys, Rolling, Solidification, Pressing, Hot pressing, Temperature
- Yıl: 2000
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz HIZLI SOĞUTULMUŞ Al-Fe-V-Si VE Al-Cr-Fe ALAŞIMLARININ MİKROYAPI VE SİNTERLEME ÇALIŞMASI Gencel, Özgür Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Danışman: Doç.Dr. Bilgehan Ögel Yardımcı Danışman: Doç. Dr. Ali Kalkanlı Eylül 2000, 100 sayfa Bu çalışmada, Al-Fe-V-Si ve Al-Cr-Fe alaşım tozlarının içyapı incelemeleri gerçekleştirilmiştir. İnceleme, hem atomize durumdaki, hem de ısıl işlem görmüş tozların içyapılanm kapsamaktadır. Al-Fe-V-Si tozlan yüksek sıcaklıklara ısıtıldığında, içyapısal değişimin 600 °C civarında başladığı gözlenmiştir. Buna karşın Al-Cr-Fe tozlarında değişim 550 °C gibi düşük bir sıcaklıkta başlamaktadır. İçyapı çalışmalarından elde edilen ve içyapıda değişime neden olan sıcaklıklar üst limit olarak Kabul edilmiş ve sıcak presleme & haddeleme işlemleri, bu sıcaklıklar dikkate alınarak gerçekleştirilmiştir. Al- Fe-V-Si tozlan 560 °C ve 100 Mpa'da yapılan bir sıcak presleme işleminde ince levhalara çatlamadan sıcak haddelenmiştir. Al-Cr-Fe alaşımlarının sıcak haddelenmesi ise herhangi bir presleme sıcaklığı ve zamanı kombinasyonunda elde edilememiştir. Al-Fe-V-Si alaşım tozlannın sinterlenmiş ve sıcak haddelenmiş levhalarına ait çekme test sonuçlan literatürde raporlananlardan düşüktür.
Özet (Çeviri)
ABSTRACT MICROSTRUCTURAL AND CONSOLIDATION STUDffiS OF AIR-ATOMIZED Al-Fe-V-Si AND Al-Cr-Fe ALLOY POWDERS Gencel, Özgür M.S., Metallurgical and Materials Engineering Department Supervisor: Assoc. Prof. Dr. Bilgehan Ögel Co-Supervisor: Assoc. Prof. Dr. Ali Kalkanh September 2000, 100 pages In this study, the microstructures of Al-Fe-V-Si and Al-Cr-Fe alloy powders were investigated. The study covered both as-atomized and heat treated powders. Then, the results obtained from microstructure - temperature relationships were applied to hot consolidation of the powders. When Al-Fe-V- Si alloys are exposed to high temperatures, it has been found that the microstructural change starts at around 600 °C. On the other hand, for Al-Cr-Fe alloy the critical temperature is much lower, i.e. 550 °C. The relavant temperatures are assumed as the high limits and used in hot consolidation. After a hot pressing operation at 560 °C and at 100 MPa, the Al-Fe-V-Si powders could be hot rolled to thin sheets without any cracking. The hot rolling of Al-Cr-Fe alloys could not be achieved at any hot pressing temperature and time combination. The tensile test results of consolidated and hot rolled sheets of Al-Fe-V-Si alloy powder is lower than the reported in literature. m
Benzer Tezler
- Toz metalurjisi yöntemleri ile üretilen çeşitli W-Ni-Fe ve W-Ni-Cu ağır alaşımların mikroyapısal ve fiziksel karekterizasyonu
Microstructural and physical characterization of various W-Ni-Fe and W-Ni-Cu heavy alloys manufactured via powder metallurgy methods
GÜNKUT ERNAS
- Mekanik alaşımlanmış intermetalik toz ve sinter Ti-47-5Al-3Cr alaşımının analitik elektron mikroskop ve x-ışınları teknikleri ile karakterizasyonu
Analytical election microscope and x-ray diffraction characterization of mechanically alloyd intermetallic Ti-47-5Al-3Cr powder and sinter
ARDA GENÇ
- Synthesis of the BN-AIN composites by carbothermal reduction and nitridition of B4C-Al2O3 mixtures
AIN-BN kompozitlerinin reaksiyon sinterlenmesi yöntemiyle üretimi
CEM ÇELİKER
Yüksek Lisans
İngilizce
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı (disiplinlerarası)
PROF. DR. ADNAN TEKİN
- Mechanical properties of PM AI-Sic compasides produced by conventional hot-pressing method
Geleneksel sıcak presleme yöntemi ile üretilmiş TM AI-Sic kompozitlerin mekanik özellikleri
GÜRLER KAYA
Yüksek Lisans
İngilizce
1999
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. RIZA GÜRBÜZ
- Metal infiltre edilmiş mikro poroz karbon kompozitlerin aşınma ve sürtünme davranışının karakterizasyonu
Başlık çevirisi yok
GÜLTEKİN GÖLLER
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. ADNAN TEKİN