Metal ve seramik braketlerin hibrit seramik CAD-CAM materyali üzerinde yapılan farklı yüzey pürüzlendirmelerinde makaslama dirençlerinin değerlendirilmesi
Evaluation of shear bond strength of metal and ceramic brackets on different surface roughenings on hybrid ceramic CAD-CAMmaterial
- Tez No: 493315
- Danışmanlar: DOÇ. GÜVENÇ BAŞARAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Dental bonding, Dental materyaller, Dental porselen, Dental stres analizi, Ortodonti, Ortodontik braketler, CAD/CAM, Dental bonding, Dental materials, Dental porcelain, Dental stress analysis, Orthodontics, Orthodontic brackets
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Dicle Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
AMAÇ Ortodontik tedavi görmek isteyen yetişkin birey sayısındaki artış karşısında ortodontistler sabit ortodontik tedavi yaparken braketlerini hastalarında bulunan amalgam, kompozit, porselen gibi protetik materyallere yapıştırmak zorunda kalmaktadırlar. Gelişen teknoloji ile birlikte diş hekimliğine her geçen gün yeni materyaller eklenmektedir. Hibrit seramik CAD-CAM blokları da yeni nesil bir protetik tedavi materyalidir. Bizim çalışmamızın amacı yeni nesil bu materyale 6 farklı pürüzlendirme tekniği uygulayıp (Hidroflorik asit (HFA), Ortofosforik asit (OFA), Cojet (CJ), Er-YAG Lazer, Nd-YAG Lazer ve Femtosaniye Lazer (FSL)) metal ve seramik braketlerdeki bağlanım dayanımını görebilmek için makaslama testi uygulayıp çıkan sonuçları taramalı elektron mikroskobu (SEM) ve optik profilometre ile karşılaştırmaktır. GEREÇ VE YÖNTEM 50 adet hibrit seramik CAD-CAM bloğundan yaklaşık 2 şer mm kalınlığında kesilerek 216 adet hibrit seramik numuneler elde edildi. Numunelere 600, 800, 1000 grit silikon karbid su zımparası (3MTM WetordryTM, 3M, St. Paul, MN, A.B.D) ile yüzey düzleştirilmesi işlemi uygulandı. Numuneler ultrasonik su banyosundan sonra metal ve seramik grupları olarak 2 ana gruba ayrıldı. Bu gruplar daha sonra 6 farklı alt gruba (HFA, OFA, CJ, Er-YAG, Nd-YAG, FSL) ayrıldı böylelikle alt gruplar 18 sayısında sabitlendi. Pürüzlendirme işlemini takiben örneklere sağ üst kesici braketleri yapıştırıldı. Örnekler oda sıcaklığında distile suda bekletildikten sonra, örneklere termal siklus cihazında 1000 devir tamamlandı. Numunelere makaslama testi uygulandı. Pürüzlendirme yapılıp ve braket yapıştırılmayan her gruptan 2 şer adet örnek taramalı elektron mikroskobu ve optik profilometre ile yüzey pürüzlülüğü açısından değerlendirildi. Braketlerin materyal yüzeyinden kopma ve porselen kırılma şekilleri incelendi. İstatistiksel değerlendirme için tek yönlü varyans analizi, Tukey'in HSD testi, ki kare testi ve Kruskal-Wallis testi kullanıldı (p<0.05). BULGULAR VE SONUÇLAR Pürüzlülük değerleri profilometre de ölçülen grupların tamamı birbirinden istatistiksel olarak farklı çıkmıştır (p<0.05). En fazla pürüzlülük değeri sırasıyla Er-YAG, FSL, CJ, Nd-YAG, HFA, OFA ve işlem görmemiş yüzey olarak sıralanmıştır. Bağlanım dayanım testi (SBS) sonuçları tüm gruplar için klinik olarak kabul edilebilir bağlanım dayanımı (SBS) değerinde ya da üzerindedir. Metal braketlerde Nd-YAG grubu istatistiksel olarak CJ, Er-YAG ve HFA'dan yüksek SBS değeri göstermiştir. Metal braketler porselen braketlere göre daha yüksek SBS değeri vermiştir, bu değerler Nd-YAG grubunda istatistiksel olarak anlamlıdır.
Özet (Çeviri)
In view of the increase in the number of adult patients seeking orthodontic treatment, orthodontists have to stick their braces to prosthetic materials such as amalgam, composite, and porcelain in their patients while performing fixed orthodontic treatment. With the developing technology new materials are added every day to the dentistry. Hybrid ceramic CAD-CAM blocks are a new generation of prosthetic treatment materials. The aim of our work is to apply 6 different roughening techniques such as Hydrofluoric acid, Orthophosphoric acid, Cojet, Er-YAG Laser, Nd-YAG Laser and Femtosecond Laser to CAD-CAM blocks to see the bonding strength in metal and ceramic brackets. We will apply a shear test to see the bond strength on the brackets and compare the results with a scanning electron microscope and an optical profilometer. MATERIAL AND METHODS Sections of approximately 2 mm thickness were cut from 50 hybrid ceramic CAD-CAM blocs and 216 hybrid ceramic samples were obtained. The samples were abraded with 600,800,1000 grit silicon carbide abrasive (3MTM WetordryTM, 3M, St. Paul, MN, U.S.A). Surface smoothing with carbide abrasive was applied. The samples were divided into two main groups as metal and ceramic groups after ultrasonic water bath. These groups were then divided into 6 different subgroups (HFA, OFA, CJ, Er-YAG, Nd-YAG, FSL). Thus, the number of subgroups was fixed at 18. Following the roughening process, the upper right incisor brackets were bonded to the specimens. Samples were stored in distilled water at room temperature and then 1000 cycles were completed in the thermal cycling device. The samples were subjected to a shear test. Two samples from each group with roughening but without brackets were evaluated in terms of surface roughness with a scanning electron microscope and an optical profilometer. The breakage of the brackets from the material surface and the shape of the porcelain fracture were examined. One-way analysis of variance, Tukey's HSD test and chi square test and Kruskal-Wallis test were used for statistical evaluation (p<0.05). RESULTS AND CONCLUSIONS The roughness values of the groups measured in the profilometer were statistically different from each other (p<0.05). The most roughness values are listed as Er-YAG, FSL, CJ, Nd-YAG, HFA, OFA and untreated surface respectively. Bond strength value (SBS) test results are the clinically acceptable bond strength value (SBS) or more for all groups. In metal brackets, the Nd-YAG group statistically showed higher SBS values than CJ, Er-YAG and HFA. Metal brackets gave higher SBS values than porcelain brackets. These values are statistically significant in the Nd-YAG group.
Benzer Tezler
- Farklı yüzey pürüzlendirmeleri yapılmış monolitik zirkonya, feldspatik porselen ve hibrit porselen materyali ile ortodontik metal ataşman arası bağlantı direncinin ve debonding sonrası yüzey özelliklerinin in-vitro incelenmesi
An in-vitro evaluation of shear bond strength between orthodontic attachment and monolithic zirconia, feldspathic porcelain, hybrid porcelain after different surface conditioning methods and surface properties after debonding
İREM KURT
- Metal ve seramik braketlerin rezin nanoseramik cad/cam materyali üzerinde yapılan farklı yüzey pürüzlendirme işlemlerinde makaslama dirençlerinin değerlendirilmesi
Evaluation of Bond Strength of Metal and Ceramic Brackets on ResinNanoceramic CAD/CAM Material With Different Surface Treatments
MEHMET KARA
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiDicle ÜniversitesiOrtodonti Ana Bilim Dalı
YRD. DOÇ. MEHMET DOĞRU
- Ortodontik metal ve seramik braketlerin yapıştırılmasında kullanılan primersiz tek adımlık sistemin mikrosızıntı ve bağlanma dayanımlarının farklı adeziv sistemleri ile in vitro olarak karşılaştırılması
In vitro comparison of microleakage and bond strength of one-step sysyem without primer used in bonding of orthodontic metal and ceramic brackets with different adhesive systems
HANDAN BAYAR BİLEN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiPamukkale ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SERPİL ÇOKAKOĞLU
- Metal ve farklı tip seramik braketlerin sökümü sonucu mine yüzeyinde oluşan hasarın in vitro incelenmesi
The investigation of the damage that occurs on enamel surface as a result of the removal of metal and different type ceramic brackets: An in vitro study
HASAN GÜNDAL
- Farklı yüzey değişikliği uygulamalarıyla metal ve seramik braketlerin farklı protetik restorasyon yüzeylerine bağlanma dayanımının değerlendirilmesi
Shear bond strength of metal and ceramic brackets to different prosthetic restoration surfaces with different surface modification
ÖMER FARUK UÇAR
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiCumhuriyet ÜniversitesiOrtodonti Ana Bilim Dalı
PROF. DR. ERCAN CENK DORUK