Farklı yüzey pürüzlendirmeleri yapılmış monolitik zirkonya, feldspatik porselen ve hibrit porselen materyali ile ortodontik metal ataşman arası bağlantı direncinin ve debonding sonrası yüzey özelliklerinin in-vitro incelenmesi
An in-vitro evaluation of shear bond strength between orthodontic attachment and monolithic zirconia, feldspathic porcelain, hybrid porcelain after different surface conditioning methods and surface properties after debonding
- Tez No: 437437
- Danışmanlar: DOÇ. DR. ÇAĞLA ŞAR
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental porselen, Dental çimentolar, Mine, Ortodontik braketler, Profilometre, Yüzey pürüzlülüğü, Dental bonding, Dental materials, Dental porcelain, Dental cements, Enamel, Orthodontic brackets, Profilometer, Surface roughness
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Başkent Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı feldspatik porselen, hibrit seramik ve monolitik zirkon yüzeylerine farklı yüzey pürüzlendirme teknikleri uygulanarak yapıştırılan ortodontik ataşmanların bağlanma dirençlerinin değerlendirilmesi ve bu yüzeylerde kabul edilebilir bağlanmayı sağlayacak en uygun yöntemin tespit edilmesidir. Ayrıca debonding yapılan restorasyon yüzeylerinin artık kompozitin temizlenmesi sonrası yüzey özelliklerinin değerlendirilmesi de amaçlanmıştır. Çürüksüz 30 adet insan 2. küçük azı dişi, 56 adet feldspatik porselen, 56 adet monolitik zirkon ve 56 adet hibrit seramik çalışmada kullanılmıştır. Materyaller randomize olarak 4 deney grubuna ayrılmıştır (n=14): 1. Hidroflorik asit ile pürüzlendirme + silan; 2. Al2O3 ile kumlama + silan; 3. SiO2 ile kumlama; 4. Elmas frez ile pürüzlendirme + silan. Diş grubu için yalnızca ortofosforik asit ile pürüzlendirme yapılmıştır. Restorasyonu tamamlanan dişler ve materyaller 37°C'deki distile suda 7 gün bekletildikten sonra 5-55°C aralığında 1000 devir termal siklus uygulaması yapılmıştır. Örnekler, Universal test cihazına sokularak bağlanma dirençleri ölçülmüştür. Butonları sökülen örneklerdeki artık kompozit fiber kompozit frezlerle (stainbuster) temizlenip porselen kiti ile parlatılmıştır. Daha sonra optik profilometre cihazına sokularak 3 boyutlu yüzey pürüzlülük ölçümleri yapılmıştır. Buton kaidelerinde ise SEM'de ARI skorlaması hesaplanmıştır. Veriler istatistiksel olarak Kolmogorov Smirnov, Levene, Mann Whitney U ve Kruskal Wallis testleriyle değerlendirilmiştir. Materyallerin birbirleriyle ve diş kontrol grubuyla yapılan kaşılaştırmaları sonucunda en yüksek bağlanma direnci feldspatik porselen grubunun HF asit ile pürüzlendirmesinde elde edilmiştir (p<0.001). HF asit uygulanan materyal gruplarında bağlanma dirençleri diğer alt gruplardan ve kontrol diş grubundan yüksek bulunmuştur (p<0.001). Ortalama pürüzlülük değerleri (Ra) incelendiğinde; en yüksek sonuçlar seramik+Al2O3, enamic+Al2O3 ve elmas frezin bütün materyallerle kombinasyonu için bulunmuştur (p<0.0038).
Özet (Çeviri)
The aim of this study is to evaluate shear bond strength between orthodontic attachment and monolithic zirconia, feldspathic porcelain, hybrid porcelain after different surface conditioning methods in order to find out the best bonding method on surfaces and to evaluate surface properties after debonding and polishing. Non-carious 30 human second premolar teeth, 56 feldspathic porcelain, 56 monolithic zirconia and 56 hybrid porcelain were randomly divided into 4 subgroups (n=14/each): 1. Hydrofloric acid etch + silane; 2. Al2O3 air abrasion + silaen; 3. Silicoating (SiO2); 4. Diamond bur + silane. Control teeth group is etched with orthophosphoric acid gel. The specimens were stored in deionized water at 37°C for seven days and then subjected to thermocycling. The specimens were tested in Universal Instron machine to evaluate the shear bond strengths. Residual composite were removed after debonding with fiber composite burs (stainbuster) and polished with the porcelain polishing kit. Then the specimens tested on three dimensional white light interferometry to evaluate surface properties by taking 3D images. Scanning electron microscobe is used to evaluate ARI scores on button mesh bases. Data analysis was performed by using Kolmogorov Smirnov, Levene, Mann Whitney U ve Kruskal Wallis tests statistically. The highest shear bond strength value was found for HF acid etched feldspathic porcelain group (p<0.001). When HF acid etched subgroups were compared with other surface conditioning methods in all material and teeth groups, the shear bond values were found higher (p<0.001). According to the average surface roughness (Ra) values; the highest results were obtained for ceramic+Al2O3, enamic+Al2O3 and all diamond bur subgroups (p<0.0038).
Benzer Tezler
- Porselen restorasyonların tamirinde kullanılan farklı tamir materyallerinin çeşitli yüzey preparasyonları uygulanarak; kopma, bağlama, kırılma dirençlerinin in vitro ve in vivo olarak karşılaştırmalı değerlendirilmesi
The in vitro and in vivo evaluation of shear-bond strengths of different porcelain repair materials after various surface treatments
TOMURCUK ÖVÜL KÜMBÜLOĞLU GÖKTÜRK
- Endodontik tedavi görmüş dişlerde kavite temizleme tekniklerinin çeşitli adeziv sistemlerin dentine bağlantısına etkileri
Effects of cavity cleaning techniques on various adhesive systems to bond of dentin in endodontically treated teeth
FEHİME ALKAN
Doktora
Türkçe
2017
Diş HekimliğiGazi ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
DOÇ. DR. HACER DENİZ ARISU
- Zirkonyum oksit esaslı seramik ile rezin simanın bağlantısına farklı yüzey işlemlerinin etkileri
The effects of different surface treatments on the bond strength of zirconium-oxide ceramic and adhesive resin
SELMA ŞEN
Doktora
Türkçe
2010
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÖZLEM CEYLAN
- Farklı pürüzlendirme teknikleri ile uygulanan iki farklı fissür örtücü materyallerinin kopma-bağlanma değerlerinin karşılaştırılması
Effect of Er:YAG laser on shearbond strength of two different fissür sealant
BERNA MERCANGÖZ
Yüksek Lisans
Türkçe
2010
Diş HekimliğiYeditepe ÜniversitesiPedodonti Ana Bilim Dalı
PROF. DR. NÜKET SANDALLI
- Farklı mine pürüzlendirme yöntemleri ile oluşabilecek renk değişikliklerinin in vitro olarak değerlendirilmesi
In vitro evaluation of possible color changes associated with enamel etching methods
NEŞE GÖNÜL
Doktora
Türkçe
2011
Diş HekimliğiYeditepe ÜniversitesiOrtodonti Ana Bilim Dalı
DOÇ. DR. FULYA IŞIK ÖZDEMİR