Taşlama sonrası kalın camsı metalde oluşan kalıntı gerilmenin delik delme yöntemiyle incelenmesi
Study of grinding induced residual stresses with hole drilling method
- Tez No: 323913
- Danışmanlar: DOÇ. DR. MUSTAFA BAKKAL
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Camsı metaller, Gerilme dağılımı, Gerilme gevşemesi, Kalıntı gerilmeleri, Taşlama, Glass metals, Stress distribution, Stress relaxation, Residual stresses, Grinding
- Yıl: 2012
- Dil: Türkçe
- Üniversite: İstanbul Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme ve İmalat Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada Zr52,5Ti5Cu17,9Ni14,6Al10 bileşimine sahip 10 mm çapında çubuk şeklindeki Zr-esaslı kalın camsı metal malzemenin 2000 dev/dak anamil hızı, 1000 mm/dak ilerleme hızı, 0.01 mm paso ve CBN taş kullanılarak taşlanmasından sonra taşlanan yüzeyde delik delme yöntemiyle kalıntı gerilmeler incelenmiştir. Delik derinliği boyunca yapılan kalıntı gerilme hesaplamaları 0.22 mm delik derinliğine kadar kalıntı gerilmelerin basma 0.22 mm'den sonra çekme şeklinde olduğunu göstermiştir. Kalıntı gerilmenin basma olarak başlayıp sonradan çekmeye dönmesinin sebebi, işleme sırasındaki taşın parça yüzeyinde meydana getirdiği plastik şekil değişimi kaynaklıdır. Parça yüzeyindeki plastik şekil değişimi yüzeyden 0.22 mm derinliğe kadar etkisini azaltarak devam etmiştir. Bu derinlikten sonra sıcaklık plastik şekil değişimine göre daha baskın hale gelerek kalıntı gerilmenin çekme şeklinde olmasını sağlamıştır. Diğer bir deyişle plastik şekil değişimi kaynaklı mekanik gerilmeler 0.22 mm derinliğe kadar sıcaklık artışı kaynaklı ısıl gerilmelerden daha büyük olduğu için kalıntı gerilme basma karakterli oluşmuş, 0.22 mm üzeri derinlikte ise ısıl gerilmeler plastik şekil değişimi kaynaklı mekanik gerilmelerden daha büyük olduğundan kalıntı gerilme çekme karakterli oluşmuştur.
Özet (Çeviri)
In this study 10 mm diameter bar shape Zr52,5Ti5Cu17,9Ni14,6Al10 bulk metallic glass is machined using parameters 2000 rpm cutting speed, 1000 mm/min feed and 0.01 mm depth of cut with CBN grinding wheel and after grinding residual stress is measured on the grinded surface. Residual stress measurements through hole depth showed that residual stresses are compressive until 0.22 mm hole depth and after 0.22 mm residual stresses became tensile. The reason of having compressive residual stress on surface till 0.22 mm hole depth is due to plastic deformation caused by grinding wheel on workpiece surface. After 0.22 mm hole depth effect of plastic deformation on workpiece surface has been diminished and grinding temperature became more dominant which caused tensile residual stresses.In other words till 0.22 mm hole depth mechanical stresses resulted from plastic deformation is greater than thermal stresses resulted from grinding temperature which caused compressive residual stresses. After 0.22 mm thermal stresses became bigger than mechanical stresses which caused tensile residual stresses.
Benzer Tezler
- Türkiye'de serebral hareket bozukluklarının etiyolojisi epidemiyolojisi ve bazı klinik özellikleri
Başlık çevirisi yok
AŞER BENSUSAN
Tıpta Uzmanlık
Türkçe
1986
Çocuk Sağlığı ve Hastalıklarıİstanbul ÜniversitesiÇocuk Sağlığı ve Hastalıkları Ana Bilim Dalı
- Çocuklarda akut stres hiperglisemisinde hormonal değişikliklerin ve kısa süreli prognozun incelenmesi
Başlık çevirisi yok
AYGÜN DİNDAR
Tıpta Uzmanlık
Türkçe
1987
Çocuk Sağlığı ve Hastalıklarıİstanbul ÜniversitesiÇocuk Sağlığı ve Hastalıkları Hemşireliği Ana Bilim Dalı
DOÇ. DR. HÜLYA GÜNÖZ
- İzmir pazarlarında satılan taze köy peynirlerinin bazı nitelikleri ve özellikle zehirlenmeye neden olan bakteri içerikleri üzerinde araştırmalar
Başlık çevirisi yok
NURSEL VAPURCU
Yüksek Lisans
Türkçe
1985
Gıda MühendisliğiEge ÜniversitesiSüt Teknolojisi Ana Bilim Dalı
DOÇ. DR. HASAN YAYGIN
- Laboratuvarda üretilen lasioderma serricorne (F) (Col.Anobii dae)'nin biyolojisi üzerinde bir araştırma
A Research on the biology of lasioderma serricorne (F.)
MÜJGAN GÖKTAY
- Mikrobilgisayar kullanarak tarım işletmesi analizi üzerine bir çalışma
Başlık çevirisi yok
BÜLENT MİRAN