Tekrarlayan fırınlamanın gelişmiş lityum disilikatla güçlendirilmiş cam seramikler ve rezin siman arasındaki makaslama dayanımına etkisi ve mikro-BT analizi
the effect of repeated firing on the shear bond strength between advanced lithium disilicate-reinforced glass ceramics and resin cement and micro-CT analysis
- Tez No: 1015543
- Danışmanlar: DOÇ. DR. RAFAT SASANY
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Lityum disilikat, Lithium disilicate
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Biruni Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez geleneksel lityum disilikat cam seramik IPS e.max CAD ile gelişmiş lityum disilikatla güçlendirilmiş cam seramik CEREC Tessera CAD materyallerde tekrarlayan fırınlama işlemlerinin rezin siman ile mikro makaslama bağlanma dayanımı üzerindeki etkisini incelemek ve ara yüzey özelliklerini mikro-BT ile değerlendirmek amacıyla planlanmıştır. ISO 6872 standardına uygun olarak hazırlanan toplam 80 örnek; materyal türü, pişirme protokolü ve tekrarlayan fırınlama durumuna göre sekiz gruba ayrılmıştır. Örnek yüzeylerine %5 hidroflorik asit ve Monobond uygulanmış, ardından dual-cure rezin siman standart ölçülerde polimerize edilmiştir. Makaslama bağlanma dayanımı MPa cinsinden hesaplanmış; örnekler ayrıca mikro-BT ile porozite, ara yüzey adaptasyonu ve siman film kalınlığı açısından değerlendirilmiştir. İstatistiksel analizlerde marka ve işlem ana etkilerinin tek başına anlamlı olmadığı, ancak marka ile işlem arasında anlamlı etkileşim bulunduğu saptanmıştır. Gruplar arası karşılaştırmada yalnızca çift aşamalı glaze ve üç kez tekrarlayan fırınlama uygulanan protokolde materyaller arasında anlamlı fark belirlenmiş; bu grupta IPS e.max CAD'in bağlanma dayanımı CEREC Tessera'ya göre daha yüksek bulunmuştur. Kopma tipi dağılımı materyale göre anlamlı farklılık göstermiş; E-max grubunda adeziv, Tessera grubunda ise koheziv kopma tipi daha baskın izlenmiştir. Sonuç olarak, tekrarlayan fırınlamanın seramik-rezin siman bağlanmasına etkisinin materyal türü ve uygulanan pişirme protokolüne bağlı olarak değiştiği gösterilmiştir. Bulgular, klinik ve laboratuvar uygulamalarda fırınlama ve yüzey işlem protokollerinin materyale özgü planlanmasının önemini ortaya koymaktadır.
Özet (Çeviri)
The aim of this thesis was to evaluate the effect of repeated firing procedures on the micro-shear bond strength between resin cement and two ceramic materials: the conventional lithium disilicate glass ceramic IPS e.max CAD and the advanced lithium disilicate-reinforced glass ceramic CEREC Tessera CAD. The study also assessed interfacial characteristics using micro-computed tomography (micro-CT). A total of 80 specimens prepared according to the ISO 6872 standard were divided into eight groups based on material type, firing protocol, and the presence or absence of repeated firing. After surface treatment with 5% hydrofluoric acid and Monobond, dual-cure resin cement was applied and polymerized. Shear bond strength values were calculated in megapascals (MPa), and specimens were evaluated by micro-CT for porosity, interfacial adaptation, and cement film thickness. Statistical analysis revealed no significant main effects of material brand or treatment alone, but a significant interaction between these factors was observed. A significant difference between the materials was found only in the protocol involving two-step glaze firing and three repeated firing cycles, where IPS e.max CAD showed higher bond strength than CEREC Tessera. Failure mode distribution also differed significantly according to material, with adhesive failures predominating in the E-max group and cohesive failures in the Tessera group. In conclusion, the effect of repeated firing on ceramic–resin cement bonding depended on both the ceramic material and firing protocol applied, highlighting the importance of material-specific firing and surface treatment strategies in clinical and laboratory procedures.
Benzer Tezler
- Çoklu fırınlamanın farklı itriyum oranlarına sahip monolitik zirkonyanın eğilme dayanımı ve faz dönüşümü üzerine etkisi
Effect of multiple firing on flexural strength and phase transformation of monolithic zirconia with different ratios of yttrium
TUĞÇE KÜÇÜKTUNCAY GÖZEN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BURCU DİKER
- Farklı yöntemler ve kalınlıklarda hazırlanan implant üstü metal altyapıların kenar ve iç uyumlarına tekrarlanan fırınlamanın etkisi
Effect of repeated firings on the marginal and internal adaptation of implant supported metal ceramic restorations fabricated with different thicknesses and fabrication method
ABDURRAHMAN ÖĞÜNÇ
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş Hekimliğiİnönü ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜLER YILDIRIM AVCU
- Tekrarlanan fırınlamanın farklı tip yüksek translusens monolitik zirkonya materyallerinin translusensi ve iki eksenli bükülme dayanımına olan etkisi
Effect of repeated firing on the translucency and biaxial flexural strength of different types of high translucency monolithic zirconia materials
SEDA YILDIZLAR
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve mekanik özellikleri üzerindeki etkisi
Effect of repeated firing on color and mechanical properties of different types of lithium disilicate ceramics
GÜLER SAFRAN ÇİÇEK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MERYEM GÜLCE SUBAŞI
- Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi
In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia
SİNEM SAVRAN ÇAKIR
Doktora
Türkçe
2011
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BÜLENT ŞERMET