Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve mekanik özellikleri üzerindeki etkisi
Effect of repeated firing on color and mechanical properties of different types of lithium disilicate ceramics
- Tez No: 1008103
- Danışmanlar: DOÇ. DR. MERYEM GÜLCE SUBAŞI
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Bükülme Dayanım, Fırınlama, Kontrastlık Oranı, Lityum Disilikat Seramik, Renk Değişim, SEM, Translüsensi, Flexural Strength, Firing, Contrast Ratio, Lithium Disilicate Ceramic, Color Change, SEM, Translucency
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kütahya Sağlık Bilimleri Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Tekrarlanan fırınlamanın farklı tip lityum disilikat seramiklerin renk ve bükülme dayanımı üzerindeki etkisinin incelenmesidir. Gereç ve Yöntem: Lityum disilikat (LD), nano lityum disilikat (NLD), virgilit içeren lityum disilikat (VLD) seramik (n=45) kesildi (18x4x1,2 mm). Kristalizasyon fırınlaması sonrası 1'er örnek SEM ile incelendi. Örnekler 4 gruba [kontrol (K), fırınlama (F) (1, 2, 3)] (n=11) ayrıldı. Her gruptan 1'er örnek SEM ile incelendi. Başlangıç ve fırınlamalar sonrası renk (ΔE, başlangıç ve fırınlama sonrası TP ve KO, TP fark) ve bükülme dayanım verileri elde edildi (n=10). ΔE, TP fark ve fırınlama sonrası KO değerleri 2 yönlü Robust ANOVA ile, başlangıç TP ve KO değerleri Kruskal-Wallis H testi ile, fırınlama sonrası TP değerleri 2 yönlü ANOVA ile, bükülme dayanım değerleri 2 yönlü Robust ANOVA ve Weibull analizi ile ve gruplar arasındaki ilişki Spearman ve Pearson korelasyon analizi ile incelendi. Bulgular: Kristalizasyon fırınlaması sonrası LD düzgün, NLD ve VLD pürüzlü yüzeye sahipti. Fırınlama sonrası seramiklerde delik gözlendi. ΔE değerleri, seramik, fırınlama ve seramik*fırınlama tipinden (p<0,001), başlangıç TP ve KO, TP fark ve bükülme dayanım verileri seramik tipinden (p≤0,017), fırınlama sonrası TP değerleri seramik ve fırınlama tipinden (p≤0,002) ve fırınlama sonrası KO değerleri seramik ve seramik*fırınlama tipinden etkilendi (p<0,001). Başlangıç ve fırınlama sonrası TP ve CR değerleri arasında, LD-K, VLD-1F, VLD-2F ve VLD-3F'in ΔE ile TP fark değerleri arasında, VLD-3F'in ΔE ile bükülme dayanım değerleri arasında ve NLD-1F'nin TP fark ile bükülme dayanım değerleri arasında negatif anlamlı korelasyon belirlendi. ΔE ve TP fark değerleri için NLD-1F'de pozitif anlamlı korelasyon belirlendi. Sonuç: Klinik uygulamada translüsensi önemli ise NLD ve VLD, bükülme dayanımı önemli ise LD'nin kullanılması önerilebilir. VLD'de tekrarlanan fırınlamalardan kaçınılmalıdır.
Özet (Çeviri)
Aim: To investigate the effect of repeated firing on the color and flexural strength of different types of lithium disilicate ceramics. Material and Method: Lithium disilicate (LD), nano lithium disilicate (NLD), and virgilite containing lithium disilicate (VLD) ceramics (n=45) were cut (18×4×1.2 mm). After crystallization firing, 1 specimen was examined with SEM. Specimens were divided into 4 groups [control (C), firing (F) (1, 2, 3)] (n=11). One specimen from each group was examined with SEM. Before and after firings, color (ΔE, initial and post-firing TP and CR, TP difference) and flexural strength data were obtained (n=10). ΔE, TP difference, and post-firing CR values by 2-way Robust ANOVA, initial TP and CR values by Kruskal-Wallis H test, post-firing TP values by 2-way ANOVA, flexural strength values by 2-way Robust ANOVA and Weibull analysis, and relationship between groups by Spearman and Pearson correlation analyses were analyzed. Results: After crystallization firing, LD had smooth, NLD and VLD had rough surface. After firing, pores were observed in ceramics. ΔE values were affected by ceramic, firing, and ceramic*firing type (p<0.001), initial TP and CR, TP difference, and flexural strength values were affected by ceramic type (p≤0.017), post-firing TP values were affected by ceramic and firing type (p≤0.002), and post-firing CR values were affected by ceramic and ceramic*firing type (p<0.001). Negative significant correlations were determined between initial and post-firing TP and CR values, between ΔE and TP difference values of LD-C, VLD-1F, VLD-2F, and VLD-3F, between ΔE and flexural strength values of VLD-3F, and between TP difference and flexural strength values of NLD-1F. For ΔE and TP difference values, positive significant correlation in NLD-1F was determined. Conclusion: In clinical practice, if translucency is important, NLD and VLD, and if flexural strength is important, LD can be recommended. Repeated firings should be avoided in VLD.
Benzer Tezler
- İdrar kültürlerinden izole edilen coag (-) staphylococcus (s. epidrmidis ve s. saprophyticus)'ların idrar yolu enfeksiyonlarındaki yeri
The Place of coag (-) staphylococcus to the urinary tract infectron which are isolated from the urine cultures
SUMRU ÇITAK(KORMAN)
- Yahya Kemal'de bedii tefekkür unsurları: 1 Kendi Gök Kubbemiz'de duygu
Başlık çevirisi yok
MUSTAFA ÖZBALCI
Yüksek Lisans
Türkçe
1985
Türk Dili ve EdebiyatıGazi ÜniversitesiTürk Dili ve Edebiyatı Ana Bilim Dalı
DOÇ. DR. SADIK K. TURAL
- Gemlik çeşidi zeytinlerden kaliteli ve az tuzlu siyah sofralık zeytin üretimi üzerinde bir araştırma
A Study on the production of quality black table olives by useing Gemlik variety olives
DİLEK BAŞER
Yüksek Lisans
Türkçe
1986
Gıda MühendisliğiUludağ ÜniversitesiGıda Bilimi ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. OĞUZ KILIÇ
- Canavarotuna (Orobanche spp.) dayanıklılık ve canavarotunun ırkları üzerine araştırmalar
Başlık çevirisi yok
M.ARZU ÖZKANER
- Sakız koyunlarında emiştirme dönemi süt verimi ve kuzuların gelişmesi
Başlık çevirisi yok
CÜNEYT KEMİKLİ