Dolgu maddelerinin ve çevresel faktörlerin EPDM kauçuğun mekanik özelliklerine olan etkilerinin incelenmesi

Investigation of the effects of fillers and environmental factors on the mechanical properties of EPDM rubber

PDF İndir

  1. Tez No: 982013
  2. Yazar: OĞUZ AKSEL
  3. Danışmanlar: PROF. DR. EROL FEYZULLAHOĞLU
  4. Tez Türü: Yüksek Lisans
  5. Konular: Makine Mühendisliği, Mechanical Engineering
  6. Anahtar Kelimeler: Döngüsel Tuz Testi, EPDM, Mekanik Özellikler, Yağ Direnç Testi, Cyclic Salt Spray Test, EPDM, Mechanical Properties, Oil Resistance Test
  7. Yıl: 2025
  8. Dil: Türkçe
  9. Üniversite: Kocaeli Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalışmada Etilen Propilen Dien Monomer (EPDM) kauçuk hamurunda mevcut katkıların oranları değiştirilerek ana karışım dahil toplam 4 farklı reçete hazırlanmıştır. 4 farklı reçete ile üretilmiş olan numuneler JASO M609 Otomotiv Standardına göre (720 saat) tuz testine maruz bırakılmış, ISO 4892-2 Method A' ya göre UV gün ışığı (720 saat) testine maruz bırakılmış ve ISO-1817 yağ (72 saat) testine maruz bırakılmıştır. Çevresel faktör öncesi ve sonrasında 4 farklı EPDM karışımının Shore A, ASTM D 575-91 standardına göre yay sabitleri, ISO 815-1 Standardına göre kalıcı deformasyonları, JIS K 6251 standardına göre çekme dayanımları, kopma uzamaları, elastisite modül sonuçları karşılaştırılmıştır. UV testi sonrası numunelerin çekme dayanımları -%2,46 ile %2,73 oranında çok az değişmiş, kopma uzamaları %30 ile %40 oranında düşmüş, elastisite modülleri %66 ila %70 oranında artmış, kalıcı deformasyonları -%4 ila -%15 oranında azalmış, sertlikleri %8 ila %18 oranında artmış ve yay sabitleri ise %1 ila %45 oranında artmıştır. Kısaca tüm reçeteler gevrek davranış göstermiş, plastikleştirici katkı maddesi (kauçuk oranı arttırılmış) 4. Reçete diğer reçetelere göre daha az etkilenmiştir. Tuz testi sonrası numunelerin tüm mekanik özelliklerinde %0,8 ila % 6 oranında ciddi bir değişim olmamış, kalıcı deformasyonları -%5 ila -%26 oranında azalmış, sertlik ve yay sabitleri ise %5 ila % 18 oranında artmıştır. Yağ testi sonrası numunelerin çekme dayanımları, kopma uzamaları, elastik modülleri, yay sabiti ve kalıcı deformasyonları -%20 ila -%60 oranında genel olarak azalmış, kalıcı deformasyonları %2 ile % 50 oranında artmıştır. Katkı maddeleri açısından 3. Reçete (Fef oranı artırılmış) ve 2. Reçete (Yağ oranı azaltılmış) daha iyi mekanik özellikler göstermiş, 3. Reçete 2. Reçete' den farklı olarak daha fazla kalıcı deformasyon ve daha düşük kopma uzaması davranışı sergilemiştir. 4. Reçete ise diğer reçetelere göre daha sünek davranış göstermiştir.

Özet (Çeviri)

In this study, a total of four different formulations, including the base compound, were prepared by varying the proportions of the additives in the Ethylene Propylene Diene Monomer (EPDM) rubber compound. The samples produced from these four formulations were subjected to a 720-hour salt spray test in accordance with the JASO M609 Automotive Standard, a 720-hour UV exposure test based on ISO 4892-2 Method A, and a 72-hour oil resistance test according to ISO 1817. Before and after exposure to these environmental conditions, the Shore A hardness, spring constants (in accordance with ASTM D 575-91), permanent deformation (ISO 815-1), tensile strength, elongation at break, and modulus of elasticity (JIS K 6251) of the four EPDM formulations were compared. Following the UV test, the tensile strength of the samples showed minimal variation, ranging from -2.46% to +2.73%. However, elongation at break decreased by 30% to 40%, modulus of elasticity increased by 66% to 70%, permanent deformation decreased by 4% to 15%, Shore A hardness increased by 8% to 18%, and the spring constant increased by 1% to 45%. In summary, all formulations exhibited a more brittle behavior; among them, Formulation 4, which had an increased rubber content due to the addition of a plasticizer, was the least affected. After the salt spray test, no significant changes (ranging from 0.8% to 6%) were observed in the mechanical properties of the samples. However, permanent deformation decreased by 5% to 26%, while Shore A hardness and spring constants increased by 5% to 18%. Post oil exposure, the samples generally exhibited a reduction of 20% to 60% in tensile strength, elongation at break, elastic modulus, spring constant, and permanent deformation, while permanent deformation increased by 2% to 50%. From the perspective of additive content, Formulation 3 (with increased carbon black content) and Formulation 2 (with reduced oil content) demonstrated better mechanical performance. However, compared to Formulation 2, Formulation 3 exhibited higher permanent deformation and lower elongation at break. Formulation 4, on the other hand, displayed more ductile behavior than the other formulations.

Benzer Tezler

  1. Tez No

    987002

    Development of sustainable nanocomposites withcarbon-based hybrid nano-additives

    Karbon tabanlı hibrit nano-katkılarla sürdürülebilirnanokompozitlerin geliştirilmesi

    SENA ÇAYLAK

    Doktora

    İngilizce

    İngilizce

    2025

    Mühendislik Bilimleriİstanbul Teknik Üniversitesi

    Nanobilim ve Nanomühendislik Ana Bilim Dalı

    PROF. DR. LEVENT TRABZON

  2. Tez No

    948776

    Processing of polylactide nanofibrous and film structures: Effects of polymer blending and bio-additives on structure-property relationships

    Polilaktit nanolif ve film yapılarının işlenmesi: Polimer karışımı ve biyo-katkıların yapı-özellik ilişkileri üzerine etkisi

    HANDAN PALAK

    Doktora

    İngilizce

    İngilizce

    2025

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Tekstil Mühendisliği Ana Bilim Dalı

    PROF. DR. BURÇAK KARAGÜZEL KAYAOĞLU

  3. Tez No

    192306

    Mobil telefon kullanımına bağlı oluşan 900-1800 mhz radyo frekans dalgalarının meydana getirdiği elektromanyetik alanın iliak kanat kemik mineral yoğunluğuna etkisi

    The effect of electromagnetic fields on bone mineral density of iliac bone produced by 900-1800 mhz radio frequency waves dependent on cellular phone usage

    BEŞİR ANDAÇ AKSOY

    Tıpta Uzmanlık

    Türkçe

    Türkçe

    2006

    Ortopedi ve TravmatolojiSüleyman Demirel Üniversitesi

    Ortopedi ve Travmatoloji Ana Bilim Dalı

    PROF.DR. NEVRES HÜRRİYET AYDOĞAN

  4. Tez No

    660472

    Türkiye'de su hakkı

    The right to water in Turkey

    YILDIZ AKEL ÜNAL

    Doktora

    Türkçe

    Türkçe

    2021

    HukukGalatasaray Üniversitesi

    Kamu Hukuku Ana Bilim Dalı

    PROF. DR. ERDOĞAN BÜLBÜL

  5. Tez No

    154615

    Effect of various stabilizer mixtures on mechanical and physical properties of CaCO3 filled polypropylene composite in different environmental conditions

    Çeşitli stabilizatör karışımlarının farklı çevresel koşullara maruz bırakılmış CaCO3 dolgulu polipropilen kompozitinin mekanik ve fiziksel özelliklerine etkisi

    NESLİŞAH UYAR

    Yüksek Lisans

    İngilizce

    İngilizce

    2004

    Polimer Bilim ve Teknolojisiİstanbul Teknik Üniversitesi

    Polimer Bilim ve Teknolojisi Ana Bilim Dalı

    PROF. DR. AYŞEN ÖNEN

Geri Dön