Manyetik nano toz katkılı filament üretimi ve 3 boyutlu yazıcı ile basılan yumuşak mıknatısların özelliklerinin araştırılması
Fabrication of magnetic nanoparticle-reinforced filaments and investigation of the properties of 3D-printed soft magnets
- Tez No: 979913
- Danışmanlar: DOÇ. DR. MUSTAFA ASLAN
- Tez Türü: Doktora
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Polimer Bilim ve Teknolojisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, Zn–Ni ferrit esaslı manyetik tozların PLA'ya katkılanmasıyla kompozit filamentler hazırlanmış ve bu filamentler kullanılarak üç boyutlu baskı yöntemiyle toroidal çekirdekler üretilmiştir. Çalışmada hem ticari hem de sol-jel destekli çözelti yakma yöntemiyle sentezlenen Zn–Ni ferrit tozları PLA içine %2,5, %5, %10, %15 ve %20 oranlarında katkılanmış, elde edilen filamentler morfolojik, termal, mekanik ve elektriksel açıdan incelenmiştir. SEM–EDS analizleri, ferrit partiküllerinin matris içerisinde belirli oranlarda homojen dağılım göstermiş, TGA sonuçları ise artan katkı oranı ile bozunma sonu kalıntının yükseldiğini ortaya koymuştur. Mekanik testlerde düşük katkı oranlarında matris sürekliliği korunurken yüksek katkılarda dayanımda azalma gözlenmiştir. Sentezlenen tozlara, üretilen kompozit filamentlere ve basılan numunelere manyetik özelliklerin karakterize edilebilmesi için VSM analizi gerçekleştirilmiştir. VSM analizleri, katkı oranı arttıkça doygun manyetizasyon değerlerinin yükseldiğini, ancak histerezis eğrilerinin ticari ferrit çekirdeklere kıyasla daha düşük kaldığını göstermiştir. Üretilen toroidal çekirdekler manyetik alan altında basılmış, ancak tane – tane temasın yetersizliği nedeniyle ticari ferrit çekirdeklere kıyasla sınırlı elektromanyetik performans sergilemiştir.
Özet (Çeviri)
In this study, Zn–Ni ferrite-based magnetic powders were incorporated into PLA to fabricate composite filaments, from which toroidal cores were subsequently manufactured via three-dimensional printing. Both commercial and sol–gel assisted solution combustion synthesized Zn–Ni ferrite powders were added to the PLA matrix at 2.5, 5, 10, 15, and 20 wt.% loadings, and the resulting filaments were investigated in terms of their morphological, thermal, mechanical, and electrical properties. SEM–EDS analyses revealed that ferrite particles exhibited a relatively homogeneous distribution within the polymer matrix, while TGA results indicated that the residual mass after degradation increased with higher filler content. Mechanical tests showed that at low filler concentrations, the continuity of the polymer matrix was preserved, whereas at higher concentrations a decrease in tensile strength was observed. To characterize the magnetic properties of the synthesized powders, composite filaments, and printed samples, vibrating sample magnetometry (VSM) analysis was performed. VSM results demonstrated that increasing filler content enhanced the saturation magnetization values, although the hysteresis loops remained lower compared to commercial ferrite cores. The fabricated toroidal cores were printed under a magnetic field; however, due to insufficient grain-to-grain contact, their electromagnetic performance remained limited in comparison to commercial ferrite cores.
Benzer Tezler
- Manisa-Demirci-Köseler plaserinden titan minerallerinin kazanılması ve pigment üretimine katkı araştırmaları
Recovery of the titanium minerals from Manisa-Demirci-Köseler plocer sands and examination of their use in prgment production
SADULLAH ERTEKİN
Yüksek Lisans
Türkçe
1985
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. NİYAZİ DELİORMANLI
- A Bound polaron under a magnetic field in two-dimensionality confined semiconductor systems
Başlık çevirisi yok
BASSAM SAQQA
Yüksek Lisans
İngilizce
1987
Fizik ve Fizik MühendisliğiOrta Doğu Teknik ÜniversitesiDOÇ. DR. ATİLLA ERÇELEBİ
- Ni-B ikili alaşım sisteminde Ni zengin bazı ara fazların manyetik özellikleri
Magnetic properties of some Ni rich intermediate phases in Ni-B binary alloy system
R.HALUK MUTLU
Doktora
Türkçe
1987
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
DOÇ. DR. ARSIN AYDINURAZ
- Nükleer magnetik rezonansın kuvantum ilkelerine giriş
Başlık çevirisi yok
H.HANDAN GÜRBÜZ
Yüksek Lisans
Türkçe
1985
Fizik ve Fizik Mühendisliğiİstanbul ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. HAYATİ BUDAK