Yüksek sıcaklık süperiletken malzemelerin üretimi ve fiziksel özelliklerinin tayini
Preparation and physical characterization of high temperature superconductors
- Tez No: 95792
- Danışmanlar: DOÇ. DR. ALİ GENCER
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: İletkenlik ve sûperiletkenlik, Bi(Pb)-Sr-Ca- Cu-O sistemi, Üretim Yöntemleri, AC Direnç, V-I Karakteristik, X- ışım toz difraksiyonu, SEM(Scanning Electron Microscope), Süper iletken bileşikler, Süper iletkenler, Sıcaklık, Conductivity and superconductivity, Bi(Pb)-Sr-Ca-Cu-0 system, fabrication methods, AC Resistivity, V-I Characteristic, powder x-ray diffraction, SEM(scanning electron microscope), Superconductor compounds, Superconductors, Temperature, Production methods
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi YÜKSEK SICAKLIK SÜPERİLETKEN MALZEMELERİN ÜRETİMİ VE FİZİKSEL ÖZELLİKLERİNİN TAYİNİ Ahmet KILIÇ Ankara Üniversitesi Fen Bilimleri Enstitüsü Fizik Anabilim Dalı Danışman: Doç. Dr. Ali GENCER Bu tez çalışmasında, saf Bi203, PbO, SrC03) CaCO^ CuO başlangıç maddeleri ve amonyum nitrat kullanılarak“bulk”şeklinde 110 K 'Iik kritik sıcaklığa sahip Bi(Pb)-Sr-Ca-Cu-0 s öperi let ken bileşikler, katı- hal reaksiyon ve sıvı amonyum nitrat yöntemleri ile değişik tavlama sıcaklıklarında üretildi ve karakterizasyonu yapıldı. Üretilen numunelerde, AC elektriksel direnç ölçümleri ve V-I karakteristikleri genelde 133 Hz sabit frekansta alındı. Bu ölçümlerden mükemmel dia manyetizmaya başlangıç sıcaklıkları tesbit edildi. Numunelerin X- ışını toz difraksiyon desenleri alınarak piklerin şiddetlerinden istenilen yüksek sıcaklık fazı(Bi-2223) ve Bİ-2212 fazının oranları belirlendi ve oluşan fazlara ait birim hücre sabitleri tespit edildi Numunelerin iç yapısı, yapraksı taneleri SEM mikrografından gözlendi. İki method arasmda karşılaştırma yapılarak, 840 °C* de 100 saat tavlan anarak üretilen numunelerin en iyi özelliklere sahip oldukları gözlendi. 2000, 88 Sayfa
Özet (Çeviri)
ABSTRACT Master's Thesis PREPARATION AND PHYSICAL CHARACTERIZATION OF HIGH TEMPERATURE SUPERCONDUCTORS Ahmet KILIÇ Ankara University Graduate School of Natural and Applied Sciences Department of Physics Supervisor: AssocProf. Dr. Ali GENCER In this thesis, from pure powders of Bi203, PbO, SrC03, CaCOj, CuO and ammonium nitrate, Bi(Pb)-Sr-Ca-Cu-0 superconducting compounds with transition temperature near 110 K were fabricated by using the solid-state reaction and liquid ammonium nitrate methods. The characterization of produced samples were carried out by X-Ray Diffraction(XRD) pattern, ac Resistivity (ACR),V-I Characterisation measurements and scanning electron microscope (SEM) studies. From the analysis of XRD patterns, the ratio of High-Tc (2223) and Bi-2212 phases and their lattice parameters have been determined. ACR and V-I Characterisation measurements were performed on the samples with f = 133 Hz. It is made possible that superconductive properties of the samples including the critical temperature Tc have been determined and flake-like grains of these granular superconductors were also observed from SEM micrographs. Comparison between two methods has been made. Samples prepared at 840 °C with annealing time 100 h appears to be good quality. 2000, 88 pages
Benzer Tezler
- Oxidative coupling of methane using superconductor and semiconductor type catalytic materials
Metanın süperiletken ve yarıiletken tipi katalitik malzemeler kullanılarak oksidasyonu
YEŞİM ERARSLANOĞLU
Doktora
İngilizce
1995
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiPROF.DR. IŞIK ÖNAL
PROF.DR. TİMUR DOĞU
- HISC superconducting edge-transition infrared detectoa; Principle, fabrication and characterization
HISC süperiletken ayrıt geçişli kızılötesi seziciler: İlkeler, üretim ve karakterizasyon
RIZMAN AKRAM
Yüksek Lisans
İngilizce
2000
Elektrik ve Elektronik Mühendisliğiİhsan Doğramacı Bilkent ÜniversitesiElektrik-Elektronik Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MEHDİ FADMANESH
- Yüksek sıcaklık süperiletken malzemelerin hazırlanması ve incelenmesi
Preperation and investigation of high temperature superconducting materials
AYTEN KAYNAR
Yüksek Lisans
Türkçe
1992
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HALUK MUTLU
- Yüksek sıcaklık süperiletken malzemelrin elektriksel ve magnetik özelliklerinin incelenmesi
Investigation of electrical and magnetic properties of high temperature superconducting materials
YAKUP KALAYCI
Yüksek Lisans
Türkçe
1997
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
DOÇ. DR. HALUK MUTLU
- İleri teknoloji yüksek sıcaklık süperiletken malzemelerin hazırlanması ve karakterizasyonu
Preparationand characterization of advanced technological high temperatures superconducting materials
ÖZER ÖZOĞUL
Doktora
Türkçe
1997
Fizik ve Fizik MühendisliğiAnkara ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. ARSIN AYDINURAZ