HII çelik levhasının kaynak kabiliyetine soğuk plastik deformasyon miktarının etkisi
Effect of cold working rate on the weldability of HII steel plate
- Tez No: 93571
- Danışmanlar: YRD. DOÇ. DR. YUSUF ÖZÇATALBAŞ
- Tez Türü: Yüksek Lisans
- Konular: Eğitim ve Öğretim, Metalurji Mühendisliği, Education and Training, Metallurgical Engineering
- Anahtar Kelimeler: Soğuk plastik deformasyon, Kaynak kabiliyeti, ITAB, Mekanik Özellikler, Isıl işlem, Plastik deformasyon, Çelik levhalar, Cold working, weldability, Heat Affected Zone, Mechanical properties, Heat treatment, Welding ability, Plastic deformation, Steel plates
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
HII ÇELİK LEVHASININ KAYNAK KABİLİYETİNE SOĞUK PLASTİK DEFORMASYON MİKTARININ ETKİSİ ( Yüksek Lisans Tezi) Remzi KANBURELOĞLU GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ MART 2000 ÖZET Bu çalışmada, farklı oranlarda soğuk plastik deformasyon uygulanan HII çelik levhasının kaynak kabiliyeti araştırılmıştır. MAG Kaynak yöntemiyle birleştirilen deforme edilmiş malzemelerin ITAB bölgelerindeki mikroyapı değişimleri ve mekanik özellikleri incelenmiştir. Ayrıca kaynak öncesi ve sonrası uygulanan 450°C, 600°C ve 900°C daki ısıl işlemlerin ITAB ve mekanik özelliklere etkisi araştırılmıştır. Artan deformasyon miktarıyla birlikte ITAB genişliği, iri ve ince tane bölgesi genişliği ve iri tane boyutunda artış belirlenmiştir. Deformasyon miktarındaki artış kaynaklı birleştirmenin mekanik özelliklerini düşürmüştür. Kaynak öncesi ve sonrası uygulanan bütün ısıl işlemlerin mekanik özellikleri arttırıcı etkisi belirlenmiştir. Bilim Kodu :225. 01. 00. 225. 01. 01
Özet (Çeviri)
EFFECT OF COLD WORKING RATE ON THE WELDABILITY OF HH STEEL PLATE ( Msc. Thesis) Remzi KANBURELOGLU GAZI UNIVERSITY INSTITUTE OF SCIENCE OF TECHNOLOGY MARCH 2000 ABSTRACT In this study, weldability of HII steel plate which had been cold worked at different rates was investigated. Mechanical proerties and micro scructural changes in the heat affected zone (HAZ) of cold worked materials welded by MAG welding technique were exemined. In addition, the effect of heat treatments, applied the materials before and after welding at 450°C, 600°C and 900 °C, on HAZ and mechanical properties were investigated. Increasing in deformation rate resulted in the increasing of the width of HAZ, fine and coarse grained regions and also the rate of grain corsening. Increasing in the high cold worked rate has decreased the mechanical praperties of welded joint. It was determined that all heat treatments applied the samples before and after welding increased mechanical properties. Science code : 225. 01. 00. 225.01.01
Benzer Tezler
- HI, HII, 17 Mn 4 ve 19 Mn 5 kazan çeliklerinin kaynağında ITAB'nin tokluğuna ısı girdisinin ve gerilme giderme tavlamasının etkileri
The Effects of heat input and stress-relief tempering on the toughness of the HAZ in the welding of type HI, HII, 17 Mn 4 and 19 Mn 5
ADNAN DİKİCİOĞLU
- High temperature corrosion of boiler plant flues
Kazan bacalarının yüksek sıcaklık korozyonu
İLKER ATİK
Yüksek Lisans
İngilizce
1998
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSHAK KARAKAYA
- Gemi levhalarının elasto-plastik olarak incelenmesi
Elasto-plastic analysis of the ship plates
MEHMET ÇEVİK
- Endüstriyel kurutma sistemleri
Başlık çevirisi yok
AHMET ERDAL FERALAN
Yüksek Lisans
Türkçe
1989
Endüstri ve Endüstri MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. RECEP YAMANKARADENİZ
- Karasu havzasında taşkın analizleri
Başlık çevirisi yok
REŞAT ACAR
Yüksek Lisans
Türkçe
1992
İnşaat MühendisliğiAtatürk Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. NEVRUZ YARDIMCI