Sade karbonlu çeliklerin borlanmasında, borür tabakası özelliklerine, karbon miktarının etkisi
The Effect of carbon quantity to the boride layer in the boriding of steels with simple carbon
- Tez No: 85782
- Danışmanlar: DOÇ. DR. REMZİ GÜRLER
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Sade karbonlu çelikler, Borlama, Fe2B fazı, Mikrosertlik, Karbon, Çelik-metal, Steels with simple carbon, Boriding, Fe2B phase, Microhardness Number of pages : 91 Thesis Instructor : Asst. Prof. Remzi GÜRLER, Carbon, Microhardness, Steel-metal
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
SADE KARBONLU ÇELİKLERİN HORLANMASINDA, BORÜR TABAKASI ÖZELLİKLERİNE, KARBON MİKTARININ ETKİSİ (Yüksek Lisans Tezi) Cengiz CİFCİ GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Ocak 1999 ÖZET Borlama malzeme yüzeyinde belirli sıcaklık ve sürelerde, bor yayındırma işlemidir. Borlama ile yüksek sıcaklıklarda çelik malzeme yüzeyine, bor yayındınlarak Fe2B ve/veya FeB fazlan içeren boriir tabakaları elde edilir. Çeliklerde bor yayınımıyla elde edilen tabakaların sertlik, aşınma ve korozyon dirençleri önemli miktarlarda arttınlabilmektedir. Borlu tabakaların özellikleri, borlanan malzemenin kimyasal bileşimine, borlama ortamı bileşimineâşlem sıcaklığına, işlem süresine, uygulanan ısıl işlemlere göre değişmektedir. Bu çalışmada sade karbonlu çeliklerin, sıvı ortam borlamasıyla elde edilen, borür tabakalarının yapı ve özelliklerine, karbon miktarının etkisi araştırılmıştır. Sade karbonlu çeliklerde alaşım elementi olarak karbon miktarının, borür tabaka kalınlığına, borür tabakası faz ve mikroy apışma, borür tabaka sertliğine olan etkileri araştırılarak incelenmiştir. Deneylerde elektrolitik demir, Ç.1010, Ç.1020, Ç.1030, Ç.1040, Ç.1050, Ç.1060, Ç.1090 çelik malzemeleri kullanılmıştır. Hazırlanan numuneler % 65 susuz boraks ve % 35 silisyum karbür, bileşimli sıvı banyoda 1000°C sabit sıcaklık ve 6 saatlik işlem süresince borlama işlemine tabi tutulmuştur. Daha sonra mikroyapı incelemeleri, mikrosertlik ve X- ışınları analizi yapılarak borlanan numunelerin özellikleri tesbit edilmiştir. Sonuçlar, deneysel ve teorik olarak karşılaştınlmıştır. Bilim Kodu : 6040202
Özet (Çeviri)
THE EFFECT OF CARBON QUANTITY TO THE BORIDE LAYER IN THE BORIDING OF STEELS WITH SIMPLE CARBON (M.Sc. Thesis) Cengiz CİFCİ GAZI UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY January 1999 ABSTRACT Bonding is the bor diffusing treatment on the material surface with certain temperatures and periods. In boriding, bor is diffused on through the steel material surface with high temperatures and boride layers including Fe2B and/or FeB phases are obtained. In steels, the roughness, wear and corrosion resistance of the layers obtained via bor diffusion can be considerably increased. The characteristics of the borided layers vary with respect to chemical composition of the borided material, boriding medium composition, operation temperature, operation period and thermal operations applied. In this study, the effect of carbon quantity on the structure and characteristics of the boride layers obtained via boriding of the steels with simple carbon in liquid medium is searched. Moreover, the effect of the carbon quantity as an alloy element in the steels with simple carbon on the thickness phase and microhardness, and roughness of boride layer is searched and examined. In the experiments, electrolitic iron and steel materials as Ç.1010, Ç.1020, Ç.1030, Ç.1040, Ç.1Ö50, Ç.1060 and Ç.1090 were used. The prepared samples were treated with boriding operation in liquid bath with 65 % dry borax and 35 %silisiumcarbur compound under 1000°C temperature for 6 hours. Then, microhardness examinations and micro-roughness and X-rays analysis war performed and the characteristics of the borided samples were determined. The results were compared both experimentally and theoretically. Science Code : 6040202
Benzer Tezler
- Sade karbonlu çeliklerin mekanik özellikleri ve sertlikleri arasındaki ilişkinin belirlenmesi
Başlık çevirisi yok
OLCAYTO ARİF ERENBERK
Yüksek Lisans
Türkçe
1997
Metalurji MühendisliğiEskişehir Osmangazi ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ABDULLAH ÖZSOY
- Düşük karbonlu çeliklerde kaynak edilebilirlikle ısıl işlem arasındaki ilişkilerin mekanik özelliklere etkisi
Başlık çevirisi yok
ABDURRAHİM YAŞA
- Pulluk uç demirlerinin aşınmaya dayanımlarının belirlenmesi ve iyileştirme imkanları üzerinde araştırmalar
The Determination and possibility of improvement of wear resistance of plow iron
CEMİL ÇETİNKAYA
Doktora
Türkçe
1994
Makine MühendisliğiGazi ÜniversitesiMakine Eğitimi Ana Bilim Dalı
PROF.DR. BİLGE ERDİLLER
- Jominy deneyi ve deney parametrelerinin deney üzerindeki etkileri
Jominy test and the effect of the test parameters on the test
SERDAR ÖZDEN KARACA
Yüksek Lisans
Türkçe
1999
Makine MühendisliğiYıldız Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET ULVİ AVCI