Gümüş ve çinko oksit nanopartikül ilavesinin akrilikrezinin yüzey pürüzlülüğü, renk değişimi ve antifungal özelliği üzerine etkisi
The effect of silver and zinc oxide nanoparticle additionof acrylic resin on surface roughness, color and antifungal properties
- Tez No: 856280
- Danışmanlar: DR. ÖĞR. ÜYESİ BURCU DİKER, DOÇ. DR. ŞULE TUĞBA DENİZ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Protez stomatiti, Akrilik rezin, Nanopartikül, Denture stomatitis, Acrylic resin, Nanoparticle
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Bezm-İ Alem Vakıf Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, ısı ile polimerize olan dental akrilik rezine farklı oranlarda (%1, %2, %5, %10) gümüş ve çinko oksit nanopartikülü ilavesinin akrilik rezinin renk değişimi, yüzey pürüzlülüğü ve C.albicans adezyonuna etkisini değerlendirmektir. Deneyler için nanopartikül tipi ve konsantrasyonuna bağlı olarak dokuz farklı grup oluşturulmuştur. Gümüş (Ag) ve çinko oksit (ZnO) nanopartikülleri ısı ile polimerize olan akrilik rezinin likitine %1, %2, %5 ve %10 oranlarında ilave edilmiş ve 10x2 mm kalınlığında disk şeklinde örnekler üretilmiştir. Örneklerin renk ölçümü kolorimetre (Chroma Meter CR-400, Konica Minolta, Japonya) ile yapılmıştır. Bir yıllık kullanımı taklit edecek şekilde örnekler termal yaşlandırmaya tabii tutulmuştur. Örneklerin renk ölçümleri yaşlandırma sonrası tekrarlanmıştır. Renk değişimi (∆E00) CIEDE 2000 formülü kullanılarak hesaplanmıştır. Örneklerin yüzey pürüzlülüğü ölçümleri kontak profilometre (Mahr, MarSurf M 300C) ile yapılmıştır. C.albicans adezyon testi için koloni oluşturan birim (CFU/ml) sayımları yapılmıştır. Yüzey topografisinin analizi için AFM analizi ve C.albicans'ın hücre yapılarını gözlemlemek için SEM analizi yapılmıştır. Çalışmanın sonucunda yüzey pürüzlülüğü ve CFU sayımı değerleri arasında gruplar arasında anlamlı bir farklılık bulunmamıştır. Ag ve ZnO nanopartiküllerinin C.albicans adezyonu üzerinde anlamlı bir etkisi görülmemiştir. Nanopartikül tipi ve konsantrasyonunun akrilik rezinin renk değişimini etkilediği görülmüştür. Akrilik rezine %1 oranında ZnO nanopartikülü ilavesi algılanabilir eşik değerin (∆E00<1,30) altında renk değişimi göstermiştir. %2, %5 ve %10 oranında ZnO; %1 ve %2 oranında Ag nanopartikülü ilavesi algılanabilir ve klinik olarak kabul edilebilir eşik değerin (∆E00<2,25) altında renk değişimi göstermiştir. %5 ve %10 oranlarında Ag nanopartikülü ilavesi, akrilik rezinin renginin klinik olarak kabul edilebilir seviyenin üzerinde değişmesine neden olmuştur. Termal yaşlandırma sonrası %1 oranında Ag ve ZnO nanopartikülü içeren gruplarda kontrol grubundan anlamlı derecede farklı renk değişimi gözlenmezken, %2 ve üzerinde Ag nanopartikülü ilavesinin akrilik rezinde kontrol grubuna kıyasla klinik olarak kabul edilebilir eşik değerin üzerinde renk değişimine neden olduğu görülmüştür. İleriki çalışmalarda farklı konsantrasyonlarda ve farklı nanopartiküllerin ilavesi ile klinik çalışmalar yapılabilir.
Özet (Çeviri)
The aim of this study to evaluate the effect of silver and zinc oxide nanoparticle addition to acrylic resin at different concentrations (1%, 2%, 5%, 10% of the liquid) on colour change, surface roughness and C.albicans adhesion. Nine different groups were prepared depending on the nanoparticle type and concentration. Silver (Ag) and zinc oxide (ZnO) nanoparticles were added to the heat- polymerized acrylic resin liquid at the rates of 1%, 2%, 5% and 10%. The disk-shaped samples with a thickness of 10x2 mm were fabricated. Color of the samples was measured with a colorimeter (Chroma Meter CR-400, Konica Minolta, Japan). The samples were subjected to thermal aging to simulate a 1-year clinical application. Color measurements of the samples were repeated after aging. Color change (ΔE00) was calculated using the CIEDE 2000 formula. Surface roughness measurements of the samples were performed with a contact profilometer (Mahr, MarSurf M 300C). Colony Forming Unit (CFU/ml) counts were conducted for the C.albicans adhesion test. AFM analysis was performed to analyze the surface topography and SEM analysis was performed to observe the cell structures of C.albicans. As a result of the study, no significant difference was found between the groups in surface roughness and CFU count values. No significant effect of Ag and ZnO nanoparticles on C.albicans adhesion was observed. It was observed that nanoparticle type and concentration affected the color change of acrylic resin. The addition of 1% ZnO nanoparticles to acrylic resin showed a color change below the perceptible threshold value (ΔE00<1.30). The addition of 2%, 5% and 10% ZnO and 1% and 2% Ag nanoparticle showed a color change below clinically acceptable threshold value (ΔE00<2.25). The addition of 5% and 10% Ag nanoparticles caused the color of the acrylic resin to change above the clinically acceptable threshold. While no significantly different color change was observed in the groups containing 1% Ag and ZnO nanoparticles after thermal aging compared to the control group, it was observed that the addition of 2% or more Ag nanoparticles caused a color change in the acrylic resin above the clinically acceptable threshold value compared to the control group. Further studies may focus on clinical studies using different nanoparticles at different concentrations.
Benzer Tezler
- Nanokompozit ambalaj filmi üretimi ve bazı gıdaların ambalajlanmasında kullanım olanaklarının araştırılması
Nanocomposite film production and investigation of its possible usage on some foods packaging
SÜLEYMAN POLAT
Doktora
Türkçe
2016
Gıda MühendisliğiÇukurova ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. HASAN FENERCİOĞLU
- Çinko oksit (zno) ve gümüş (ag) nanopartiküllerinin galleria mellonella (l.) (lepıdoptera: Pyralıdae) üzerindeki toksik etkilerinin belirlenmesi
Determination of toxic effects of zinc oxide (zno) and silver (ag) nanoparticles on galleria mellonella (l.) (lepidoptera: Pyralidae)
ATA ESKİN
Doktora
Türkçe
2017
ZoolojiMarmara ÜniversitesiBiyoloji Ana Bilim Dalı
PROF. DR. ZAHİDE ULYA NURULLAHOĞLU
- Titanyum dioksit(TiO2), çinko oksit(ZnO) ve gümüş (Ag) nanopartiküllerinin TK-6 lenfoblast hücrelerindeki toksik etkilerinin belirlenmesi
Determination of toxic effects of titanium dioxide (TiO2) zinc oxide (ZnO) and silver (Ag) nanoparticles on TK-6 lymphoblast cells
BURCU AKSOY
Yüksek Lisans
Türkçe
2022
Tıbbi Biyolojiİstanbul ÜniversitesiBiyoloji Ana Bilim Dalı
PROF. DR. TUNCAY ORTA
- Çinko Oksit (ZnO) nanopartiküllerinin antifungal aktivitesinin belirlenmesi
Determination of antifungal activity of Zinc Oxide (ZnO)nanoparticles
İZEL BAHADIR
Yüksek Lisans
Türkçe
2020
BiyolojiEskişehir Teknik ÜniversitesiBiyoloji Ana Bilim Dalı
DOÇ. DR. RASİME DEMİREL
PROF. DR. ENDER SUVACI
- Çinko, titanyum ve alüminyum katkılı bakır oksit nanoparçacıkların antibakteriyel etkilerinin karşılaştırılması
Comparison of antibacterial effects of zinc, titanium and aluminum doped copper oxide nanoparticles
MUSTAFA YILMAZ
Yüksek Lisans
Türkçe
2024
Fizik ve Fizik MühendisliğiYıldız Teknik ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. ÇİĞDEM ORUÇ