Farklı yüzey aşındırma işlemlerinin monolitik zirkonya materyalinin yaşlandırma öncesi ve sonrası bükülme direncine ve faz dönüşümüne etkisi
The effects of different surface treatments on flexure strength and phase transformation of monolithic zirconia material before and after aging protocol
- Tez No: 826795
- Danışmanlar: DOÇ. DR. NAZMİYE ŞEN
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Y-TZP, Monolitik Zirkonya, Yüzey İşlemleri, Bükülme Direnci, Faz Dönüşümü, Aşındırma, Dental materyaller, Dental stres analizi, Protetik diş tedavisi, Zirkonyum, Y-TZP, Monolithic Zirconia, Surface Treatments, Flexural Strength, Phase Transformation, Abrasion, Dental materials, Dental stress analysis, Prosthetic dental treatment, Zirconium
- Yıl: 2023
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Kuron-Köprü Protezi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, monolitik zirkonya restorasyonların ağız içi oklüzal uyumlandırılmasında uygulanan yüzey aşındırma ve mekanik cila işlemlerinin bükülme direncine kısa ve uzun dönemli etkilerini incelemektir. Çalışmamızın birinci hipotezi,“ Yüzey işlemleri sonucu oluşan faz dönüşümleri materyalin bükülme direncine anlamlı ölçüde etki eder”; İkinci hipotezi,“ Yüzey işlemleri sonucu oluşan yüzey pürüzlülüğü materyalin bükülme direncine anlamlı ölçüde etki eder.”şeklindedir. Çalışmamızda 15mm çap ve 1.2mm kalınlığa sahip 140 adet disk şeklinde monolitik zirkonya örnek kullanıldı, Örneklere sırasıyla yüzey aşındırma ve mekanik cila işlemleri uygulandı. Aşındırma işlemlerinde 107-181µ ve 27-76µ elmas partikül boyutuna sahip frezler kullanıldı. Mekanik cila işlemi için Diapol W16Dg mekanik cila seti kullanıldı. Yaşlandırma işlemi, ISO 1335 standartlarına uygun olarak otoklavda 134 ⁰C'de 2 bar basınç altında 1 saat süre ile gerçekleştirildi. Yüzey işlemleri sonrasında örneklere X Işını difraksiyon analizi, biaksiyal bükülme direnci testi ve yüzey pürüzlülük analizi uygulandı. Yapılan analizler sonucunda, deney grupları arasında bükülme direnci ve yüzey pürüzlülük değerlerinin istatistiksel olarak anlamlı farklılık gösterdiği tespit edilmiştir (p=0,001; p<0,01). X Işını difraksiyon analizi verilerine göre deney gruplarına ait pik noktalardaki değişimler incelenmiş ve grafikler üzerinde rapor edilmiştir. Çalışmamızda elde ettiğimiz veriler doğrultusunda ince grenli elmas frezler ile aşındırma ve mekanik cila uygulaması, yüzey pürüzlülüğünü azaltmış, kalın grenli elmas frezlerin kullanımı ise arttırmıştır. İnce grenli elmas frezlerin kullanımı bükülme direncini arttırmış, kalın grenli frezlerin kullanımı bükülme direncini azaltmıştır. Yaşlandırma uygulaması öncesi ve sonrası materyalde monoklinik faz dönüşümü gözlenmemiştir.
Özet (Çeviri)
The aim of this study is to investigate the short-term and long-term effects of surface grinding and mechanical polishing procedures applied for the intraoral occlusal adjustments of monolithic zirconia restorations on flexural strength and phase transformation.The first null hypothesis of the study is“Phase transformations that occur as a result of surface treatments have a significant effect on the flexural strength of monolithic zirconia material”; Second null hypothesis is,“Surface roughness resulting from surface treatments significantly affects the biaxial flexural strength of monolithic zirconia material.”In the present study, a total of 140 disc-shaped monolithic zirconia specimens with a diameter of 15mm and a thickness of 1.2mm were used. Surface grinding and mechanical polishing procedures were applied to the test specimens. Burs with diamond particle sizes of 107-181µ and 27-76µ were used for the grinding procedure. Diapol W16Dg mechanical polishing set was used during mechanical polishing procedures. The artificial aging process was applied in an autoclave for 1 hour under 2 bar athmospheric pressure at 134 ⁰C in accordance with the guidance of ISO 1335 standard. Then, biaxial flexural strength, surface roughness and X-Ray Diffraction analysis were applied to test specimens. Biaxial flexural strength and surface roughness values of test groups showed statistically significant differences (p=0.001; p<0.01). According to the results of X-Ray diffraction analysis, the changes in the peak points among the groups were determined on the graphs. In the light of the data obtained in the present study, grinding with fine-grained diamond burs and mechanical polish application decreased the surface roughness, and the use of coarse-grained diamond burs increased the surface roughness of monolithic zirconia. The use of fine-grained diamond burs increased the biaxial flexural strength, while the use of coarse-grained burs decreased the strength values. Monoclinic phase transformation was not observed in the material before and after the artificial aging application.
Benzer Tezler
- Farklı itriyum içerikli monolitik zirkonya materyaline uygulanacak farklı bitirme işlemlerinin materyalin mekanik özelliklerine etkisi
The effect of different finishing processes applied to monolithic zirconia material with different yttrium content on the mechanical properties of the material
RUMEYSA BAYKAN
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiKaradeniz Teknik ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ELİF AYDOĞAN AYAZ
- Sinterizasyon hızının ve klinik uyumlamanın monolitik zirkonya restorasyonların optik, mekanik, mikro yapısal ve yüzey özellikleri üzerindeki etkisinin ı̇ncelenmesi
Impact of sintering speed and clinical adjustment on translucency, mechanical, microstructural, and surface properties of monolithic zirconia restorations
ÖZGE GÜLMEZ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ESRA KUL
- Farklı yüzey parlatma sistemlerinin çeşitli monolitik zirkonyum materyallerinin yüzey özellikleri ve faz değişimleri üzerindeki etkisinin incelenmesi
The effect of different surface polishing systems on surface properties and phase changes of various monolithic zirconium materials
HARUN REŞİT BAL
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. NURAN YANIKOĞLU
- Zirkonyum esaslı 3 farklı tüm porselen sisteminde, yüzey işlemlerinin, ortalama yüzey pürüzlülüğüne ve bükülme dayanıklılığına etkisinin araştırılması ve X-ray difraktometre yüzey analizleri ile incelenerek değerlendirilmesi
The effect of surface treatment of 3 different zirconia based full ceramics on mean surface roughness and flexural strength and the determination of the effects of surface treatment of the zirconia systems by X-ray difractometer surface analyse
SEÇİL KARAKOCA
Doktora
Türkçe
2008
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HANDAN YILMAZ
- Monolitik yüksek translusent itriya parsiyel stabilize zirkonya sistemlerinde farklı yüzey işlemlerinin, yüzey pürüzlülüğü ve iki eksenli bükülme dayanımına etkisinin incelenmesi
Evaluation of the effect of different surface treatments on monolithic high translucent yttria partially stabilized zirconia systems on surface roughness and biaxial flexural
EZGİ GÜRSOY TAN
Doktora
Türkçe
2024
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HANDAN YILMAZ