Farklı doldurucu oranına sahip akışkan kompozitlerin renk stabilitelerinin ın vitro değerlendirilmesi
In vitro evaluation of the color stability of flowable composites with various filler content
- Tez No: 758165
- Danışmanlar: DR. ÖĞR. ÜYESİ NASİBE AYCAN YILMAZ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Akışkan Kompozit Rezin, Renk Analizi, Renk Stabilitesi, Spektrofotometre, Dental materyaller, Dental restorasyon, Diş renk değişikliği, Kompozit malzemeler, Spektrofotometri, İn vitro, Flowable Composite Resin, Color Analysis, Color Stability, Spectrophotometer, Dental materials, Dental restoration, Tooth discoloration, Composite materials, Spectrophotometry, In vitro
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Adnan Menderes Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Restoratif Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: İki farklı bitirme-cila sistemi (OptiDisc, Pogo) ile cilalanan, farklı doldurucu içeriğine sahip dört farklı akışkan kompozit rezin materyalinin [Supreme (Filtek Supreme XTE Flowable), Bulkfill (Filtek Bulk-Fill Flowable), Estelite (Estelite Universal Medium Flow), GaenialFlo (G-aenial Universal Flo)], üç farklı solüsyona (su, kahve, çay) maruz bırakıldıktan sonraki renk stabilitelerinin karşılaştırmalı olarak değerlendirilmesi amaçlandı. Gereç ve Yöntem: Çalışmaya dahil edilen her akışkan kompozit rezin materyalinden, 30'ar adet olmak üzere toplam 120 adet disk şeklinde (6mm çapx2mm kalınlık) örnek hazırlandı. Her kompozit grubunda bulunan 30 örnek, kullanılacak bitirme-cila sistemine göre rastgele iki alt gruba ayrılarak Optidisc veya Pogo cila sistemi ile cilalandı. Bitirme-cila işlemleri tamamlanan örnekler etüvde distile suda 37°C'de 24 saat süreyle bekletildi ve daha sonra kontakt tip spektrofotometre aracılığıyla ilk kantitatif renk ölçümleri gerçekleştirildi. İlk ölçümlerin ardından örnekler 3 alt gruba ayrılarak su, kahve veya çay olmak üzere 3 farklı solüsyonda 7 gün süreyle etüvde bekletildi. CIE Lab sistemi kullanılarak ve ölçümlerden elde edilen ortalama L, a, b, değerleri ΔE=[(ΔL)2 +(Δa)2 +(Δb)2]1/2 formülüne yerleştirilerek, renk değişimini ifade eden ΔE değerleri hesaplandı. Materyal, içecek ve cila sistemine göre ortalama ΔE değerlerinin istatistiksel analizinde Üç Yönlü Varyans Analizi ve post-hoc Tukey HSD testleri kullanıldı. Önem düzeyi p<0,05 alındı. Bulgular: Akışkan kompozit rezin materyal tipi, solüsyon ve cila sisteminin renk değişimine istatistiksel olarak anlamlı düzeyde etkisi oldu (p<0,001). Çay veya kahvede bekletilen gruplar, suda bekletilen kontrol gruplarına kıyasla anlamlı düzeyde daha yüksek renk değişimi gösterdi (p<0,05). Ancak çay ve kahvede bekletilen gruplar arasında anlamlı fark saptanmadı (p>0,05). Pogo ile cilalanan gruplar, Optidisc gruplarına kıyasla anlamlı düzeyde daha yüksek renk değişimi gösterdi (p<0,05). En yüksek ve en düşük renk değişimi sırasıyla Supreme ve Estelite akışkan kompozit rezin materyallerinde elde edildi (p<0,05). Estelite akışkan kompozit rezin materyali, hiçbir koşul altında klinik olarak kabul edilemeyecek düzeyde renk değişimi göstermedi. Sonuç: Çalışmanın sınırlamaları dahilinde en yüksek renk stabilitesi gösteren akışkan kompozit rezin materyali Estelite olarak tespit edilmiştir.
Özet (Çeviri)
Objective: It was aimed to comparatively evaluate the color stability of four different flowable composite resins with different filler content [Supreme (Filtek Supreme XTE Flowable), Bulkfill (Filtek Bulk-Fill Flowable), Estelite (Estelite Universal Medium Flow), GaenialFlo (G-aenial Universal Flo)], subjected to three beverages (water, coffee, tea) after two different finishing and polishing procedures (OptiDisc, Pogo). Material and Methods: A total of 120 disc-shaped (6mm diameter x 2mm thickness) samples were prepared by allocating 30 samples in each flowable composite resin group. The samples in each flowable composite resin group (n=30) were divided randomly into two subgroups according to the finishing-polishing system to be used and polished with Optidisc or Pogo. All samples were kept in distilled water in an incubator at 37°C for 24 hours and then initial color measurements were performed quantitatively using a contact-type spectrophotometer. After initial color measurements, the samples were divided into 3 subgroups according to the beverages and kept in the distilled water, coffee or tea in an incubator for 7 days. The ΔE values expressing the color change were calculated by using the CIE Lab system and placing the mean L, a, b, values obtained from the measurements into the formula ΔE=[(ΔL)2 +(Δa)2 +(Δb)2]1/2. Three-way Analysis of Variance and post-hoc Tukey HSD tests were used for statistical analysis of mean ΔE values at a significance level of p<0.05. Results: The main factors of the flowable composite resin material type, beverage and polishing system had a statistically significant effect on color change (p<0.001). The groups kept in tea or coffee showed a significantly higher color change compared to the control groups in water (p<0.05). However, no significant difference was found between the groups kept in tea and coffee (p>0.05). The groups polished with Pogo showed significantly higher color change compared to Optidisc groups (p<0.05). The highest and lowest color changes were obtained in Supreme and Estelite flowable composite resin materials, respectively (p<0.05). Estelite did not reveal any clinically unacceptable discoloration under any circumstances. Conclusion: Within the limitations of the study, Estelite presented the highest color stability among all flowable composite resin materials
Benzer Tezler
- Diş fırçalamanın yeni nesil akıcı kompozitlerin yüzey pürüzlülüğü ve mikrosertliğine etkisinin incelenmesi
Investigation of the effect of tooth brushing on the surface rougness and microhardness of the new generation flowable composites
MELİS BAYSAL CANYURT
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSağlık Bilimleri ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ELİF AYBALA OKTAY
- Fiberle güçlendirilmiş adeziv köprülerde, rezin esaslı farklı inorganik yapıdaki restoratif materyallerin, bükülme direncine etkisinin incelenmesi
Investigation on the effect of bending response of resin based restorative materials that have different inorganic structure on fiber reinforced adhesive bridges
ERTÜRK BİLGEÇ
Diş Hekimliği Uzmanlık
Türkçe
2016
Diş HekimliğiSağlık Bilimleri ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. FULYA TOKSOY TOPÇU
- Development of a micro-well-based microfluidic 3D cell culture for cytotoxicity assays
Sitotoksisite testı için mikro kuyu tabanlı mikro akışkan 3 buyutlu hücre kültürünün geliştirilmesi
SARAH FARAHANI
Yüksek Lisans
İngilizce
2023
Mühendislik BilimleriOrta Doğu Teknik ÜniversitesiMikro ve Nanoteknoloji Ana Bilim Dalı (disiplinlerarası)
DOÇ. DR. ENDER YILDIRIM
DR. ÖĞR. ÜYESİ ALTUĞ ÖZÇELİKKALE
- Farklı indirekt restoratif materyallerin kalınlıklarının ve içeriklerinin, rezin bazlı yapıştırma simanlarının ışıkla polimerizasyon derecelerine etkisinin araştırılması
The study of the effects of thickness and chemical composition of various indirect restorative materials on the degree of conversion of PHOTO-polymerized resin- based bonding cements
BURCU DEDAŞ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MUHARREM ERHAN ÇÖMLEKOĞLU
- Değişken sıkıştırma oranlı bir silindirli dizel motor modeli tasarımı ve simülasyonu
One cylinder diesel variable compression ratio engine model design and simulation
TÜRKAY ARSLAN
Yüksek Lisans
Türkçe
2017
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. OSMAN AKIN KUTLAR