Production of biocompatible mica glass ceramics for dental applications
Bio uyumlu mika cam seramiklerin diş uygulamaları için üretimi
- Tez No: 75738
- Danışmanlar: DOÇ. DR. ABDULLAH ÖZTÜRK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Cam seramik, endosteal implantasyon, mika, vollastonit, flogopit, biouyum, işlenebilirlik. iv, Cam seramikler, Protezler ve implantlar, Volastonit, Glass ceramics, endosteal implantation, mica, wollastonite, phlogopite, biocompatibility, machinability, Prostheses and implants
- Yıl: 1998
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZ BİO UYUMLU MİKA CAM SERAMİKLERİNİN DİŞ UYGULAMALARI İÇİN ÜRETİMİ DER, Hakan Yüksek Lisans, Metalürji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Doçent Dr. Abdullah ÖZTÜRK ' Eylül 1998, 110 sayfa Diş uygulamalarından biri olan endosteal implantasyon için, kimyasal bileşim olarak Si02, Al203l CaO, MgO, K20, ve F1 dan oluşan ayrıca çekirdeklendirici olarak P205, Zr02l veya Ti02 den birini içeren cam seramikleri, aynı kimyasal bileşime sahip camların kontrollü olarak kristalleştirilmesi sonucu üretilmiştir. Kristalleşme işlemi sırasında uygulanan çekirdeklenme sıcaklığı 600 veya 620 °C dane büyüme sıcaklığı ise 900, 950 veya 1010 °C; her bir sıcaklıkta tutma süresi de 6, 8 ve 10 saat olarak değiştirilmiştir. İstenilen özelliklerin elde edilebilmesi için uygulanan ısıl işlem programına göre mikroyapıda oluşan değişiklikler belirlenmiştir. XRD ve SEM çalışmaları, elde edilen mika cam seramiklerin, kimyasal bileşimine ve uygulanan ısıl işlem programına bağlı olarak; hem malzemeye işlenebilirlik özelliği sağlayan flogopit kristallerini hem de biouyum kazandıran vollastonit kristallerini içerdiğini ortaya çıkarmıştır.
Özet (Çeviri)
ABSTRACT PRODUCTION OF BIOCOMPATIBLE MICA GLASS CERAMICS FOR DENTAL APPLICATIONS DER, Hakan M.S., Department of Metallurgical and Materials Engineering Supervisor: Assoc. Prof. Dr. Abdullah ÖZTÜRK September 1998, 110 pages Glass ceramics have been produced by crystallization of the glasses for endosteal (endosseous) implantation from the system Si02, Al203, CaO, MgO, K20, and F. Also, P205, Zr02, or Ti02 have been added as nucleating agents Nucleation and grain growth temperatures were between 600-620 °C and 900, 950, 1010 °C, respectively. The time for holding at the tempera tures varied between 6 to 10 hours. The heat treatment schedule and mi crostructure relations were determined to obtain the desired properties. The XRD and SEM studies revealed that these mica glass ceramics posses not only synthetic fluormica crystals called phlogopite which provides machinability, but also wollastonite crystals which provide biocompatability as a function of chemical composition and heat treatment schedule.
Benzer Tezler
- Synthesis of polyhydroxybutyrate and its copolymers by alcaligenes latus and alcaligenes eutrophus
Polihidroksibütirat ve kopolimerlerinin alcaligenes latus ve alcaligenes eutrophus ile sentezlenmesi
ZEYNEP GÜMÜŞYAZICI
Yüksek Lisans
İngilizce
1999
BiyoteknolojiOrta Doğu Teknik ÜniversitesiBiyoteknoloji Ana Bilim Dalı
PROF. DR. GÜRDAL ALAEDDİNOĞLU
- Ekstraktif etanol fermentasyonunda çözücü seçimi
Solvent selection in extractive ethanol fermantation
HAMDİ KAPUCU
- Osteokondral defektlerin tamirinde kültür kondrosit greftlerin kullanımı
Başlık çevirisi yok
CEMİL YILDIZ
Tıpta Uzmanlık
Türkçe
1997
Ortopedi ve TravmatolojiGataOrtopedi ve Travmatoloji Ana Bilim Dalı
PROF. DR. ETHEM GÜR
- Hassas döküm ile üretilen femoral nakillerin ısıl sprey yöntemleri ile geliştirilmesi
Development studies of precision casted femoral implants by thermal spray coating methods
TEZER BATTAL
- Ekstraktif sitrik asit fermentasyonu
Extractive citrit acid fermentation
AYTEN ATEŞ
Yüksek Lisans
Türkçe
1998
Kimya MühendisliğiAnkara ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÜLKÜ MEHMETOĞLU