Üç farklı akıcı restoratif materyalin molar diş oklüzal fissürlerinde mikrosızıntı bakımından değerlendirilmesi
Evaluation of three different flowable restorative materials for microleakage in molar dental occlusal fissures
- Tez No: 757019
- Danışmanlar: DOÇ. DR. SERDAR BAĞLAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Mikrosızıntı, kendinden adezivli akışkan kompozit, kendinden asitli fissür örtücü, pit ve fissür örtücü, penetrasyon derinliği, stereomikroskop, SEM, Azı dişleri, Dental fissürler, Dental materyaller, Dental restorasyon, Dental sızma, Dental çimentolar, Dişler, Kompozit malzemeler, Mikroskopi-elektron taramalı, Çukur ve fissür örtücüler, Microleakage, self-adhesive flowable composite, self-etch fissure sealant, pit and fissure sealant, penetration depth, stereomicroscope, SEM, Molar, Dental fissures, Dental materials, Dental restoration, Dental leakage, Dental cements, Teeth, Composite materials, Microscopy-electron scanning, Pit and fissure sealants
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı; üç farklı akıcı restoratif materyalin molar diş oklüzal fissürlerinde mikrosızıntısını ve penetrasyon derinliğini değerlendirmektir. Gereç ve Yöntem: Çalışmada ortodontik veya periodontal nedenle çekilmiş çürüksüz altmış adet insan daimî molar dişi kullanıldı. Oklüzal yüzeyinde restorasyon bulunan, mine yüzeyi deformasyona uğramış veya hasarı bulunan dişler çalışma dışı bırakılmıştır. Dişler rastgele üç gruba ayrılmıştır (n=20): Grup 1 geleneksel rezin fissür örtücü 3M Clinpro™ Sealant (3M, St. Paul, ABD), Grup 2 kendinden adezivli akışkan kompozit Fusio Liquid Dentin (Pentron Clinical, ABD) ve Grup 3 kendinden asitli fissür örtücü Prevent Seal (Itena, Paris, Fransa) üretici firma talimatlarına göre uygulanmıştır. Restorasyonlar post-polimerizasyon işlemine tabi tutulmuştur. Termal yaşlandırma işleminin ardından örnekler %0.5'lik bazik fuksinde bekletilmiştir. Örneklerden alınan kesitler stereomikroskop altında mikrosızıntı ve penetrasyon derinliği açısından değerlendirilmiştir. İstatistiksel analiz tek yönlü Varyans analizi ve Kruskal-Wallis testleri kullanılarak yapılmıştır. Bulgular: Mikrosızıntı ve penetrasyon derinliği açısından gruplar arasındaki farklılık istatistiksel olarak anlamlı bulunmuştur (M: p<0,001; Pd: p=0,009). Grup 1; Grup 2 ve Grup 3'e göre mikrosızıntı açısından anlamlı düzeyde düşük bulunurken (p<0,05), Grup 2 ve Grup 3 arasında anlamlı farklılık bulunmamıştır (p>0,05). Materyallerin penetrasyon derinliği Grup 1; Grup 2 ve Grup 3 ile farklılık göstermezken (p>0,05); Grup 3 Grup 2'den anlamlı düzeyde yüksek ortalamaya sahip olduğu belirlenmiştir (p<0,05). Sonuç: Elde ettiğimiz sonuçlara göre oklüzal fissürlerde akıcı restoratif materyallerin faydalı ve kullanılabilir olduğu görülmüştür. Geleneksel rezin fissür örtücü daha düşük mikrosızıntı değeri göstermiştir. Kendinden adezivli akışkan kompozit ve kendinden asitli fissür örtücü arasında mikrosızıntı bakımından anlamlı bir farklılık olmadığı görülmüştür. Bu materyallerle ilgili in vitro ve in vivo çalışmalara ihtiyaç olduğu düşünülmektedir. Sonuç olarak ilerleyen teknoloji ve farklı yaklaşımlarla gelişmelerin devam ederek daha etkin bir materyal arayışına devam edilmesi gerekmektedir.
Özet (Çeviri)
Aim: The aim of this in vitro study;to evaluate the microleakage and penetration depth of three different flowable restorative materials in molar tooth occlusal fissures. Materials and Methods: Sixty caries-free human permanent molar teeth extracted for orthodontic or periodontal reasons were used in the study. Teeth with restoration on the occlusal surface, deformed or damaged enamel surface were excluded from the study. The teeth were randomly divided into three groups (n=20): Group 1 conventional resin fissure sealant 3M Clinpro™ Sealant (3M, St. Paul, USA), Group 2 self-adhesive flowable composite Fusio Liquid Dentin (Pentron Clinical, USA), and Group 3 self-etch fissure sealant Prevent Seal (Itena, Paris, France) was applied according to the manufacturer's instructions. The restorations were subjected to postpolymerization. After the thermal aging process, the samples were kept in 0.5% basic fuchsine. Sections taken from the samples were evaluated under a stereomicroscope in terms of microleakage and penetration depth. Statistical analysis was performed using one-way ANOVA and Kruskal-Wallis tests. Results: The difference between the groups in terms of microleakage and penetration depth was statistically significant (M: p<0.001; Pd: p=0.009). Group 1; while it was found to be significantly lower in terms of microleakage compared to Group 2 and Group 3 (p<0.05), no significant difference was found between Group 2 and Group 3 (p>0.05). Penetration depth of materials Group 1; while it did not differ with Group 2 and Group 3 (p>0.05); it was determined that Group 3 had a significantly higher mean than Group 2 (p<0.05). Conclusion: According to our results, flowable restorative materials in occlusion fissures have been found to be useful and usable. Conventional resin fissure sealant showed less microleakage value. It was seen that there was no significant difference between self -adhesive flowable composite and self-etch fissure sealant in terms of microleakage. In vitro and in vivo studies are needed for these materials. As a result,it is necessary to continue the search for a more effective material by continuing the developments with advancing technology and different approaches.
Benzer Tezler
- Süt dişi sınıf ıı kavitelerinde farklı restoratif materyallerin başarısının in vivo ve sonlu elemanlar yöntemi kullanılarak değerlendirilmesi
Comparative evaluation of restorative materials in primary teeth class ii cavities using clinical and finite element analysis
FATİH ŞENGÜL
Doktora
Türkçe
2008
Diş HekimliğiAtatürk ÜniversitesiPedodonti Ana Bilim Dalı
YRD. DOÇ. DR. TAŞKIN GÜRBÜZ
- Farklı restoratif materyaller kullanılarak restore edilen sınıf V restorasyonlar üzerindeki stres dağılımlarının 3 boyutlu sonlu elemanlar stres analiz yöntemiyle incelenmesi
Examination of stress distributions on class V restorations restored using different restorative materials via 3D finite element stress analysis method
ABDULKADİR HARMANKAYA
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiNecmettin Erbakan ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HAKAN YASİN GÖNDER
- Üç farklı kuafaj materyalinin pulpa ve dentin üzerine etkilerinin histolojik olarak incelenmesi
A histologic investigation of di̇rect pulp capping in rat molars with three different pulp capping materials
AYSUN DÜNDAR ÜNNÜ
Doktora
Türkçe
2013
Diş Hekimliğiİstanbul ÜniversitesiDiş Hekimliği Bölümü
PROF. DR. MEHMET TEVFİK AKINCI
- Farklı pit ve fissür örtücü materyallerinin kenar uyumu, aşınma ve mikrosızıntı özelliklerinin değerlendirilmesi
Evaluation of marginal adaptation, wear and microleakage characteristics of different pit and fissure sealant materials
HÜSEYİN HATIRLI
Doktora
Türkçe
2016
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. BİLAL YAŞA
YRD. DOÇ. SERDAR BAĞLAR
- Farklı protetik restorasyon materyallerinin fonksiyonel aşınmalarının karşılaştırmalı olarak invitro deneylerde incelenmesi
An In vitro comparative investigation of functional wear of different prothetic restorative materials
GAMZE MANDALI
Doktora
Türkçe
1997
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HASAN N. ALKUMRU