Farklı yöntemlerle üretilen alümina örneklerin veneer seramik ile makaslama bağlanma dayanımlarının ve mekanik özelliklerinin in vitro karşılaştırılması
In vitro comparison of veneer ceramic shear bond strength and mechanical properties of alumina samples produced by different methods
- Tez No: 743557
- Danışmanlar: PROF. DR. LEVENT NALBANT
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Alümina, Dental porselen, Dental stres analizi, Diş kaplamaları, Mekanik özellikler, İn vitro, Alumina, Dental porcelain, Dental stress analysis, Dental veneers, Mechanical properties, In vitro
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Eklemeli üretim, geleneksel yöntemlere göre yeni bir üretim yöntemidir. Malzeme israfının önlenmesi, insan müdahalesini en aza indiren dijital iş akışı, üretim kolaylığı gibi avantajları sayesinde son yıllarda tercih edilen bir yöntem olmuştur. Çalışmanın amacı geleneksel slip casting yöntemiyle ve eklemeli yöntemle (stereolithografi) üretilen alumina seramiklerin, üst yapı veneer seramikle olan makaslama bağlanma dayanımlarını ve bükülme dayanımı, yüzey sertliği, kırılma tokluğu gibi mekanik özelliklerini in vitro olarak karşılaştırmaktır. Her iki yöntemle üretilen alumina seramiklerin üst yapı seramiğine bağlanma dayanım testi sonrası oluşan kopma türleri, optik mikroskopta değerlendirilmiştir. Örneklerin istatistiksel analizi bağımsız t testi ile yapılmış, istatistiksel anlamlılık p<0,05 olarak kabul edilmiştir. Makaslama bağlanma dayanım testi sonucu her iki grup arasında istatistiksel olarak anlamlı bir fark bulunmamıştır (p>0,05). Bükülme dayanım testi, Vickers sertlik testi ve kırılma tokluğu testinde; eklemeli yöntemle üretilen örneklerin değerleri sayısal olarak daha yüksek olmasına rağmen, slip casting yöntemiyle üretilen seramikler ile istatistiksel olarak anlamlı bir fark oluşturmamıştır (p>0,05). Sonuç olarak; üç boyutlu yazıcılarla üretilen alumina seramiklerin üst yapı veneer seramik ile olan makaslama bağlanma dayanımı ve mekanik özelliklerinin geleneksel yöntemlerle benzer olduğu tespit edilmiştir. Alumina seramiklerin üretiminde; geleneksel yöntemlerin yanında, eklemeli üretim yöntemlerinin de kullanılabileceği sonucuna varılmıştır.
Özet (Çeviri)
Additive manufacturing is a new production method compared to traditional methods. It has become a preferred method in recent years, thanks to its advantages such as preventing material waste, minimizing human intervention, digital workflow, and ease of production. The aim of the study is to compare the shear bond strength and mechanical properties such as flexural strength, surface hardness and fracture toughness of alumina ceramics produced by traditional slip casting method and additive method (stereolithography) with superstructure veneer ceramics in vitro. The rupture types formed after the bond strength test of the alumina ceramics produced by both methods to the superstructure ceramic were evaluated under the optical microscope. Statistical analysis of the samples was made with independent t-test and statistical significance was accepted as p<0.05. There was no statistically significant difference between the two groups in shear bond strength test results (p>0.05). Although the values of the samples produced by the additive method in the bending strength test, Vickers hardness test and fracture toughness test were numerically higher, there was no statistically significant difference between them and the ceramics produced by the slip casting method (p>0.05). As a result; it has been determined that the shear bond strength and mechanical properties of alumina ceramics produced with three-dimensional printers with superstructure veneer ceramics are similar to traditional methods. In the production of alumina ceramics; it has been concluded that additive production methods can also be used besides traditional methods.
Benzer Tezler
- Litografi ile sinterize edilen seramik yapının kırılma mekaniği, mikroyapısı ve elemental kompozisyonu açısından değerlendirilmesi
The evaluation of fracture mechanics, microstructure and elemental composiotion of lithography sintered ceramic
İPEK AYSAN MERİÇ
Doktora
Türkçe
2014
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. YURDANUR UÇAR
- Production of antibacterial biobased blends for biomedical use
Biyomedikal alanlarda kullanılmak üzere antibakteriyel özellikli biyobazlı harmanların eldesi
METE DERVİŞCEMALOĞLU
Yüksek Lisans
İngilizce
2023
Biyoteknolojiİstanbul Teknik ÜniversitesiMoleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı (disiplinlerarası)
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR
- Seydişehir alüminasının termolüminesans özelliklerinin karakterizasyonu ve doz-cevap özelliklerinin araştırılması
Characterization of thermoluminescent properties of Seydişehir alumina and investigation of properties of dose response
ERDEM UZUN
Doktora
Türkçe
2008
Fizik ve Fizik MühendisliğiYıldız Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. YASEMİN YILDIZ YARAR
- Yüzey işlemlerinin ve ataşman bağlama materyallerinin titanyum kepler ile farklı tekniklerle üretilen kaide materyalleri arasındaki bağlanma dayanımına etkisinin in vitro olarak incelenmesi
In-vitro investigation of the effect of surface treatments and attachment luting materials on bond strength between titanium caps and base materials fabricated by different techniques
BİLGEHAN KOTTAŞ
Doktora
Türkçe
2026
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- 3 boyutlu yazıcılar ve geleneksel yöntemlerle kullanılan geçici kron materyallerinin kırılma dayanımlarının değerlendirilimesi
Başlık çevirisi yok
AYTAN SHAHMALIYEVA
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiAkdeniz ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ULVİYE ŞEBNEM BÜYÜKKAPLAN