Farklı temizleme yöntemlerinin kontamine CAD/CAM bloklarla rezin siman arasındaki bağlantı dayanımına etkisi
The effect of different cleaning methods on the resin bond strength to contaminated CAD/CAM blocks
- Tez No: 735963
- Danışmanlar: DOÇ. DR. ERSAN ÇELİK
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Kontaminasyon, temizleme yöntemi, makaslama bağlantı dayanımı, CAD/CAM bloklar, CAD/CAM, Dental bonding, Dental materyaller, Dental stres analizi, Dental çimentolar, Kirlilik, Contamination, cleaning methods, shear bond strength, CAD/CAM blocks, CAD/CAM, Dental bonding, Dental materials, Dental stress analysis, Dental cements, Pollution
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in-vitro tez çalışmasının amacı, farklı temizleme yöntemlerinin kontamine edilmiş CAD/CAM bloklarla rezin siman arasındaki bağlantı dayanımına etkisini değerlendirmektir. Gereç ve Yöntem: Çalışmada; zirkonya ile güçlendirilmiş lityum silikat seramik (Vita Suprinity) [S], lityum disilikat ile güçlendirilmiş cam seramik (IPS e.max CAD) [Ex], lösit ile güçlendirilmiş cam seramik (IPS Empress CAD) [Em], polimer infiltre seramik (Vita Enamic) [En] CAD/CAM bloklar kullanılmıştır. Nihai boyutları 5x5x1,5 mm olacak şekilde her bir materyalden 55 adet, toplamda 220 adet örnek hazırlanmıştır. Tüm örneklere %9,5 hidroflorik asit uygulanmıştır. Uygulanacak farklı temizleme yöntemlerine göre 5 alt gruba ayrılmıştır(n=10). Bir grup kontamine edilmemiş (C), diğer 4 gruptaki örnekler tükürük ve silikon ile kontamine edilmiştir. Temizlikte; hava-su spreyi (WS), %0,5 NaOCl solüsyonu (HC), %37'lik H3PO4 (PA) ve Ivoclean (CP) kullanılmıştır. Temizleme işlemleri sonrası yüzeyler taramalı elektron mikroskobu ile incelenmiştir. Örneklere sırasıyla silan (Gc Ceramic Primer II) ve universal rezin siman (Relyx U200) uygulandıktan sonra universal test cihazında 1mm/dk kafa hızında MBD testi yapılmıştır. Veriler iki yönlü varyans analizi (ANOVA) ve Tukey HSD testleri kullanılarak istatistiksel olarak analiz edilmiştir. Bulgular: İki yönlü varyans analizi testi sonucunda, kullanılan materyal, temizleme yöntemleri ve etkileşimlerinin MBD değerleri üzerine etkisi istatistiksel olarak anlamlı bulunmuştur (p<0.05). Tüm materyaller için en yüksek makaslama bağlantı dayanımı değerleri S-C (22,271±1,103 MPa) grubunda, en düşük makaslama bağlantı dayanımı değerleri ise En-CP (2,649±0,628 MPa) grubunda görülmüştür. Sonuç: Temizleme yöntemlerinin, kontamine CAD/CAM blokların bağlantı dayanım değerlerini farklı şekillerde etkilediği görülmüştür.
Özet (Çeviri)
Aim: The aim of this iv-vitro study is to evaluate the effect of different cleaning methods on the resin bond shear bond strength to contaminated CAD/CAM blocks. Materials and Methods: In the study, lithium disilicate ceramic (IPS e.max CAD) [Ex], zirconia reinforced lithium silicate ceramic (Vita Suprinity) [S], leucite reinforced ceramic (IPS Empress CAD) [Em], polymer infiltrated ceramic network (Vita Enamic) [En] including 4 CAD/CAM blocks were used. A total of 220 samples of 5x5x1,5 mm in size, 55 of each material were prepared. Lithium disilicate ceramic (IPS e.max CAD) and zirconia reinforced lithium silicate ceramic (Vita Suprinity) specimens were crystallized. Specimens were etched with a 9,5% hydrofluoric acid. The samples were divided into 5 subgroups according to the cleaning methods to be applied (n = 10). One group is uncontaminated (C), other 4 groups are contaminated with saliva and silicone. Contaminated surfaces of ceramic specimens were cleaned with either water spray (WS), with 0.5% sodium hypochlorite solution (HC), with a cleaning paste (CP) and %37 phosphoric acid (PA). Control group (C) was not cleaned. One sample from each group was examined with a scanning electron microscope. After cleaning regimens, adhesive resin cement (Relyx U200) was bonded to the samples and SBS test was applied to the samples with a universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed statistically using two-way analysis of variance (ANOVA) and Tukey HSD tests. Results: As a result of two-way analysis of variance test, the effect of material type, cleaning methods and interactions on SBS values was found to be statistically significant (p<0.05). For all materials, the highest bond strength values were shower in the S-C group (22,271±1,103 MPa) and the lowest bond strength values were in the En-CP (2,649±0,628 MPa) group. Conclusion: Cleaning methods appeared to affect the bond strength values of contaminated CAD/CAM blocks differently.
Benzer Tezler
- Kuru incirlerde küf florası ve aflatoksigenik küflerin saptanması
Başlık çevirisi yok
SİBEL BÜYÜKŞİRİN
- Temizleme yöntemlerinin tükürük ile kontamine yüksek translüsens zirkonyanın bağlanma dayanımına etkisi
The effect of cleaning methods on the bond strength of salivacontaminated HİGH translucent zirconia
AMİNE KÜBRA CENGİZ
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. GÜLİZ AKTAŞ
- Farklı dekontaminasyon yöntemlerinin implant iyileşme başlıklarının temizlenmesine ve yüzey özelliklerine etkileri
Effects of different decontamination methods on cleaning and surface properties of implant healing aps
EYŞAN ÇETİNSOY
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiEge ÜniversitesiPeriodontoloji Ana Bilim Dalı
PROF. DR. ALİ GÜRKAN
- Hemen dentin örtüleme sonrası uygulanan geçici yapıştırma simanın farklı temizleme yöntemleri ile uzaklaştırılmasının dual cure rezin simanın dentine makaslama bağlanma dayanımına etkisi
The effect of removing temporary luting cement with differentcleaning methods applied immediate dentin sealing on the shearbond strength of dual-cure resin cement to dentin
ZEYNEP AYDIN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. CEMİLE KEDİCİ ALP
- Tükürükle kontamine olmuş monolitik zirkonya seramiğin farklı yüzey işlemleri sonrası makaslama bağlanma dayanımı
Shear bond strength of saliva contaminated monolithic zirconia ceramics after different surface treatment
ÖZGE GENÇ
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NECLA DEMİR