Dekstrin ve kumarin katkılı TiO2 filmlerin optik ve morfolojik özelliklerinin incelenmesi
Investigation of optical and morphological properties of dextrin and coumarin doped TiO2 films
- Tez No: 730662
- Danışmanlar: PROF. DR. İDRİS SORAR
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: TiO2, sol-jel, dekstrin, kumarin, optik özellikler, morfolojik özellikler, TiO2, sol-gel, dextrin, coumarin, optical properties, morphological properties
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Hatay Mustafa Kemal Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Titanyum dioksit (TiO2), parlaklık, toksik olmaması, saf beyazlığa sahip olması, fiziksel ve kimyasal kararlığa sahip olması gibi özelliklerinden dolayı yaygın şekilde kullanılan, üzerinde araştırmalar yapılan bir malzemedir. Maliyetinin düşük olması nedeniyle de çeşitli alanlarda kullanılmaktadır. Bu çalışmada sol-jel kaplama yöntemi kullanılarak mikroskop cam taşıyıcılar üzerine çeşitli fiziksel ve kimyasal koşullar altında kumarin ve dekstrin katkılı TiO2 filmler hazırlanmıştır. Kaplama işlemi için kullanılan TiO2 çözeltisi uygun miktarda titanyum (IV) n-bütoksit, asetik asit ve etanol içermektedir. Filmler taşıyıcılar üstüne döndürerek kaplama yöntemi kullanılarak hazırlanmıştır. Kaplanan filmler 550 oC de 90 dakika ısıl işleme tabi tutulmuştur ve elde edilen filmler analiz edilmiştir. Filmlerin yapısal analizi X-ışınları kırınımı (XRD) kullanılarak yapılmıştır. Filmlerin anataz yapıda olduğu belirlenmiştir. Kumarin katkılı TiO2 filmlerin yasak enerji aralığının 3.88 eV ile 3.91 eV arasında değiştiği hesaplanmıştır. Dekstrin katkılı TiO2 filmlerin yasak enerji aralığının ise 3.81 eV ile 3.87 eV arasında değiştiği hesaplanmıştır. Optik ölçümlerde dekstrin ve kumarin katkılı filmlerin yüksek geçirgenliğe ve düşük soğurmaya sahip olduğu belirlenmiştir. Kumarin ve dekstrin katkılı TiO2 ve katkısız TiO2 filmlerin yüzey yapıları Taramalı Elektron Mikroskobu (SEM) ile incelenmiştir. Hazırlanan filmlerin yüzeylerinin düzgün bir şekilde kaplandığı ve homojen dağılım gösterdiği görülmüştür. 2021, 47 sayfa
Özet (Çeviri)
Titanium dioxide (TiO2) is a widely used and researched material due to its properties such as brightness, non-toxicity, pure whiteness, physical and chemical stability. It is used in various fields due to its low cost. In this study, coumarin and dextrin doped TiO2 films were prepared on microscope slide substrates under various physical and chemical conditions using the sol-gel method. The TiO2 solution used for the coating process contains appropriate amounts of titanium (IV) n-butoxide, acetic acid and ethanol. The films were prepared using the spin coating method on substrates. The coated films were heat treated at 550 °C for 90 minutes and then they were analyzed. Structural analysis of the films was made using X-ray diffraction (XRD). It was determined that the films were in anatase structure. It was calculated that energy band gap of coumarin doped TiO2 films varied between 3.88 eV and 3.91 eV. It was calculated that energy band gap of dextrin doped TiO2 films varied between 3.81 eV and 3.87 eV. In optical measurements, it was determined that dextrin and coumarin doped films have high transmittance and low absorption. The surface structures of coumarin and dextrin doped TiO2 and undoped TiO2 films were investigated by Scanning Electron Microscopy (SEM). It was observed that the surfaces of the films were coated entirely and showed a homogeneous distribution. 2021, 47 pages
Benzer Tezler
- Dekstrin temelli polimerlerin sentezi, yüzey modifikasyonu ve biyomedikal uygulamaları
Synthesis, surface modification and biomedical application of dextrin based polymers
MELİKE KANTARCIOĞLU
- Bazı tuz tipi minerallerin yağ aglomerasyonu ile zenginleştirilmesi
Recovery of some salt type minerals by oil agglomeration
İBRAHİM SÖNMEZ
Doktora
Türkçe
2002
Maden Mühendisliği ve MadencilikCumhuriyet ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
DOÇ.DR. YAKUP CEBECİ
- α-Amilaz üreticisi yerel Bacillus soylarının izolasyonu, nitelendirilmesi ve enzim üretiminin optimizasyonu
Isolation and identification of the α-amylase producing strains from local areas the optimization of the enzyme production
MERVE TUZLAKOĞLU
Yüksek Lisans
Türkçe
2004
BiyolojiGebze Yüksek Teknoloji EnstitüsüBiyoloji Ana Bilim Dalı
PROF.DR. FÜSUN GÜMÜŞEL
- Bazı organik reaktiflerin ve metal iyonlarının pirit yüzeyinde ditiyofosfin adsorpsiyonuna etkisinin farklı elektrokimyasal koşullarda incelenmesi
Investigation of the effect of some organic reagents and metal ions on dithiophosphinate adsorption on pyrite surface under various electrochemical conditions
KEMAL ŞAHBUDAK
Doktora
Türkçe
2009
Maden Mühendisliği ve MadencilikCumhuriyet ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
DOÇ. DR. TAKİ GÜLER
PROF. ÜNAL AKDEMİR
- Toprak ve su örneklerinden amilolitik bakteri ve mayaların izolasyonu, tanımlanmaları ve bazı enzimatik özelliklerinin belirlenmesi üzerine bir araştırma
Başlık çevirisi yok
NEDİM ALBAYRAK
Yüksek Lisans
Türkçe
1993
Gıda MühendisliğiAnkara ÜniversitesiGıda Bilimi ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. SEDAT DÖNMEZ