Düşük ısı bozunmasının farklı içerikteki yttrium ile stabilize zirkonyaların eğilme dayanımlarına etkisi
The effect of low temperature degradation on flexural strength of stabilized zirconia with different content of yttrium
- Tez No: 723686
- Danışmanlar: DOÇ. DR. CENNET ELÇİN SAĞIRKAYA
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Zirkonya, hızlı sinterleme, hidrotermal yaşlandırma, düşük ısı bozunması, dört nokta eğme testi, Dental materyaller, Dental stres analizi, Düşük sıcaklık, Hidrotermal, Sinterleme, Yapay yaşlandırma, Zirkonyum, Zirkonyum oksit, İtriyum, Zirconia, rapid sintering, hydrothermal aging, low temperature degradation, four point bending test, Dental materials, Dental stress analysis, Low temprature, Hydrothermal, Sintering, Artificial aging, Zirconium, Zirconium oxide, Yttrium
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu tez çalışmasının amacı, farklı sinterizasyon işlemleri sonrasında hidrotermal yaşlandırmanın 4 farklı içeriğe sahip zirkonya materyallerinin eğilme dayanımlarına, faz değişimlerine ve tane boyutlarına etkisinin değerlendirilmesidir. Gereç ve Yöntem: Çalışmada 3Y-TZP (Ceramill Zolid Preshade)[Z], 4Y-TZP (Ceramill HT+ Preshade ve Ceramill Gen-X Multilayer)[H ve G] ve 5Y-TZP (Ceramill FX Multilayer)[F] olmak üzere 4 farklı CAD/CAM zirkonya materyali kullanılmıştır. Nihai boyutları 24x4x1.2 mm olacak şekilde her bir materyalden 40 adet, toplamda 160 adet örnek hazırlanmıştır. Zirkonya örnekleri, hızlı sinterleme protokolünde (1580 °C-10 dakika, n=80) ve klasik sinterleme protokolünde (1450 °C-2 saat, n=80) sinterlenmiştir. Dört nokta eğme testi, her grup örnek için yaşlandırma işlemi uygulamadan (n=10)[C] ve hidrotermal yaşlandırma uygulanarak (134°C, 0.2 MPa basınçta 10 saat, n=10)[A] sonra üniversal test cihazı ile 1mm/dk kafa hızında gerçekleştirilmiştir. Veriler üç yönlü varyans analizi (ANOVA) ve Tukey HSD testleri kullanılarak istatistiksel olarak analiz edilmiştir. Her grup için bir örneğe XRD analizi yapılmıştır. Tane boyutları taramalı elektron mikroskobu (SEM) ile incelenmiştir. Bulgular: Üç yönlü varyans analizi testi sonucunda, kullanılan materyal, sinterleme prosedürü, yaşlandırma işlemi ve etkileşimlerinin dört nokta eğme testi değerleri üzerine etkisi istatistiksel olarak anlamlı bulunmuştur (p<0.05). Tüm materyaller için en yüksek eğilme dayanımı değerleri ZSC (341,41 ± 54,47 MPa) grubunda, en düşük eğilme dayanımı değerleri ise FSA (167,97 ± 20,07 MPa) grubunda görülmüştür. Sonuç: Daha kısa sinterleme süreleri, maliyet ve zaman açısından avantajlı bir alternatif olduğundan, hızlı sinterleme, geleneksel sinterleme protokollerine geçerli bir alternatiftir.
Özet (Çeviri)
Aim: The aim of this thesis study is to evaluate the effect of hydrothermal aging on the flexural strength, phase changes and grain sizes of zirconia materials with 4 different contents after different sintering processes. Materials and Methods: In the study, 3Y-TZP (Ceramill Zolid Preshade)[Z], 4Y-TZP (Ceramill HT+ Preshade and Ceramill Gen-X Multilayer)[H and G] and 5Y-TZP (Ceramill FX Multilayer)[F] including 4 different CAD/CAM zirconia materials were used. 40 samples of each material, 160 samples in total, were prepared with final dimensions of 24x4x1.2 mm. Zirconia specimens were sintered in the high-speed sintering protocol (1580 °C-10 min, n=80) and the conventional sintering protocol (1450 °C-2 h, n=80). The four-point bending test were applied for each group of samples without aging (n=10)[C] and hydrothermal aging (10 hours at 134°C, 0.2 MPa pressure, n=10)[A] with a universal testing machine at a crosshead speed of 1mm/min. Data were analyzed statistically using three-way analysis of variance (ANOVA) and Tukey HSD tests. XRD analysis was performed on a sample for each group. The grain sizes were examined by scanning electron microscopy (SEM). Results: As a result of the three-way analysis of variance test, the effects of the material type, sintering procedure, aging process and interactions on four-point bending test values were found to be statistically significant (p<0.05). For all materials, the highest flexural strength values were showed in the ZSC group (341.41 ± 54.47 MPa), and the lowest flexural strength values were in the FSA group (167.97 ± 20.07 MPa). Conclusion: As shorter sintering times represent a cost and time efficient alternative, high-speed sintering is a valid alternative to conventional sintering protocols.
Benzer Tezler
- ALÜMİNYUM/ELMAS METAL MATRİSLİ KOMPOZİTLERİN GAZ BASINÇLI İNFİLTRASYON YÖNTEMİ İLE ÜRETİMİ VE TERMAL ÖZELLİKLERİNİN GELİŞTİRİLMESİ
FABRICATION OF ALUMINUM/DIAMOND METAL MATRIX COMPOSITE BY GAS PRESSURE INFILTRATION METHOD AND ENHANCEMENT OF THEIR THERMAL PROPERTIES
MUHAMMET EMİN KONDAKÇI
Doktora
Türkçe
2022
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NURİ SOLAK
- Yaygın gelişimsel bozukluğu (Otizm spektrumu) olan çocuklarda klinik ve elektroensefalografi bulguları.
Başlık çevirisi yok
SEMİH AYTA
Tıpta Uzmanlık
Türkçe
2006
Nörolojiİstanbul ÜniversitesiNöroloji Ana Bilim Dalı
PROF. DR. MEFKURE ERAKSOY
- Arpada B-glukan içeriği ve maltkalitesi üzerine etkileri
Başlık çevirisi yok
RECEP ÖZKARA
Yüksek Lisans
Türkçe
1997
Gıda MühendisliğiHacettepe ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DOÇ. DR. HAMİT KÖKSAL
- Enez (Ainos) kazısı Su Terazisi ve Kral Kızı bölgelerinde ele geçen camların bozulmaları üzerine arkeometrik çalışmalar
Archaeometric studies on the deterioration of glass artefacts of Su Terazisi and Kral Kızı regions in Enez (Ainos) excavation
DİDEM ÇOLAK BÜYÜKSOY
Yüksek Lisans
Türkçe
2020
Arkeometriİstanbul ÜniversitesiTaşınabilir Kültür Varlıklarını Koruma ve Onarım Ana Bilim Dalı
DOÇ. DR. HATİCE IŞIL KOCABAŞ
DOÇ. DR. ALİ AKIN AKYOL
- Çan bölgesi linyitlerinin akışkan yatak yanma sürecindeki davranımı
Fluidised bed combustion behaviour of the lignites from the Çan region
HÜSNÜ ATAKÜL