Nano malzemeli çimento bağlayıcılı kompozitlerin yüksek sıcaklık dayanıklılığının incelenmesi
Investigation of high temperature resistance of cementitious composites containing nanomaterials
- Tez No: 712263
- Danışmanlar: PROF. DR. HARUN TANYILDIZI
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Basınç dayanımı, Eğilme dayanımı, Nanomateryaller, Yüksek sıcaklık, Çimento esaslı kompozit, İyileşme, Compressive strength, Bending strength, Nanomaterials, High temperature, Cementitious composite, Convalescence
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Malzemeleri Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasında, nano silis (NS) ve karbon nano tüp (KNT) içeren çimento esaslı kompozitlerin (ECC) yüksek sıcaklık dayanıklılığı ve kendiliğinden iyileşme performansı incelenmiştir. Karışımlarda, bağlayıcı yerine NS ve KNT kütlece %0, %0.25, %0.50 ve %0.75 oranlarında kullanılmıştır. NS ve KNT içeren bu karışım oranları ile 505050 mm boyutlarında küp, 5075360 mm boyutlarında prizmatik ve Ø100200 mm boyutlarında silindir numuneler üretildikten sonra plastik torbalarda 23±2 °C'de 28 gün süreyle kür edilmiştir. Bu kür süresinden sonra, oda sıcaklığına (20±2 ℃) ve 100 ℃, 200 ℃, 300 ℃ ve 400 ℃ sıcaklıklara maruz bırakılan numuneler üzerinde basınç dayanımı ve eğilme dayanımı deneyleri gerçekleştirilmiştir. Ayrıca, bu sıcaklıklara maruz bırakılan silindir numunelerden kesilen Ø10050 mm silindir numuneler üzerinde, ön yükleme ile çatlaklar oluşturulmuştur ve ıslanma/kuruma döngüsüyle bu çatlakların kendiliğinden iyileşme davranışı incelenmiştir. Islanma/kuruma döngülerinden sonra iyileşen numuneler üzerinde yarmada çekme dayanımı, hızlı klorür geçirgenliği ve ultrasonik ses geçirgenliği deneyleri gerçekleştirilmiştir. Dahası, iyileşen numunelerden alınan örnekler üzerinde, kendiliğinden iyileşme ürünlerinin morfolojik özelliklerini incelemek için SEM, EDS, XRD ve FTIR analizleri gerçekleştirilmiştir. ECC numunelerinin basınç dayanımı ve eğilme dayanımı deney sonuçları incelendiğinde, en iyi sonuçlar NS içeren ECC numunelerinden elde edilmiştir. ECC numunelerinin kendiliğinden iyileşme performansı incelendiğinde ise en iyi iyileşen numunenin %0.75 NS içeren ECC numunesi olduğu görülmüştür.
Özet (Çeviri)
In this thesis, high temperature durability and self-healing performance of cement-based composites (ECC) containing nano silica (NS) and carbon nano tube (CNT) were investigated. In the mixtures, NS and CNT were used at the rates of 0%, 0.25%, 0.50% and 0.75% by mass instead of binder. After producing samples of 505050 mm cube in size, 5075360 mm prismatic in size and Ø100200 mm cylindrical with these mixing ratios containing NS and CNT, they were cured in plastic bags at 23±2 °C for 28 days. After this curing period, compressive strength and flexural strength tests were carried out on the samples exposed to room temperature (20±2 ℃) and temperatures of 100 ℃, 200 ℃, 300 ℃ and 400 ℃. In addition, cracks were formed by preloading on Ø10050 mm cylindrical samples cut from the cylindrical samples exposed to these temperatures, and the self-healing behavior of these cracks with the wetting/drying cycle was investigated. After the wetting/drying cycles, splitting tensile strength rapid chloride permeability and ultrasonic pulse velocity tests were carried out on the recovered samples. Moreover, SEM, EDS, XRD and FTIR analyzes were performed on the samples from the healed specimens to examine the morphological characteristics of the self-healing products. When the compressive strength and flexural strength test results of ECC samples were examined, the best results were obtained from ECC samples containing NS. When the self-healing performance of ECC samples was examined, it was seen that the best healing sample was the ECC sample containing 0.75% NS.
Benzer Tezler
- Yüksek sıcaklık ve sülfat hücumuna maruz kalmış çimento esaslı lifli kompozitlerin mühendislik özelliklerinin makine öğrenmesi yöntemleriyle incelenmesi
Investigation of engineering properties of cement-based fibrous composites exposed to high temperature and sulfate attack using machine learning methods
NECİM KAYA
Doktora
Türkçe
2024
İnşaat MühendisliğiBatman Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DOÇ. DR. SERHAT DEMİRHAN
- Nikel (II) ve demir (III) nitrit komplekslerinin sulu ortamdaki ardışık oluşumunun potansiyometrik ve spektrofotometrik yöntemle incelenmesi
Potentiometric and spectrophotometric studies on the stepwise formation of cmoplexes of nicel (II) and iron (III) nitrites in aqueous solution
F. BEDİA ERİM
- Glucose oxidase enzimi substrat, inhibitör ve aktivatörlerine ait kinetik parametrelerin tayini
Başlık çevirisi yok
TEVFİK ATALAY
- Çift ton çok frekanslı işaretlerin üretilmesi ve çift ton çok frekanslı işaret alıcısındaki sayısal filtrelerin tasarımı
Dual tone multifrequency (DTMF) signal generation and realization of digital filters in the DTMF receiver
ERSOY CEYLAN
Yüksek Lisans
Türkçe
1990
Elektrik ve Elektronik Mühendisliğiİstanbul Teknik ÜniversitesiPROF.DR. AHMET DERVİŞOĞLU
- Naftalinin seryum (IV) ile oksidasyon kinetiği ve mekanizması
Oxidation of kinetic of naphtalene by CE (IV)
B.FİLİZ ŞENKAL