Poliβ-alanin aşılı fırça tipi polimetil metakrilat sentezi ve karakterizasyonu
Synthesis and characterization of the brush type polymethyl methacrylate grafted polyβ-alanine
- Tez No: 670991
- Danışmanlar: PROF. DR. TEMEL ÖZTÜRK, DOÇ. DR. EFKAN ÇATIKER
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Naylon 3 (poliβ-alanin), metil metakrilat (MMA), fırça tipi graft kopolimer, serbest radikal polimerizasyonu (SRP), hidrojen transfer polimerizasyonu (HTP), Kopolimerler, Polimetilmetakrilat, Nylon 3 (polyβ-alanine), methyl methacrylate (MMA), brush type graft copolymer, free radical polymerization (FRP), hydrogen transfer polymerization (HTP), Copolymers, Polymethyl methacrylate
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Giresun Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Poli(metil metakrilat-g-β-alanin) fırça tipi graft kopolimerlerin sentezi, vinil grubu ihtiva eden naylon 3 (poliβ-alanin) makromonomeri ve metil metakrilat (MMA) vinil monomeri kullanılarak serbest radikal polimerizasyonu (SRP) yöntemi ile gerçekleştirildi. Kopolimerizasyonda başlatıcı olarak 2,2′-azobis(2-methylpropionitrile) ve çözücü olarak da formik asit kullanıldı. Fırça tipi graft kopolimerlerin sentezi 70 oC sıcaklıkta 50 dakika sürelerde yapıldı. Bunun için vinil grubu ihtiva eden poliβ-alanin makromonomeri hidrojen transfer polimerizasyonu (HTP) yöntemi ile sentezlendi. Poliβ-alanin, akrilamitin vinil monomer olarak kullanıldığı baz katalizli hidrojen transfer polimerizasyonu yöntemi ile elde edilmiştir. Neme ve oksijene duyarlı olan polimerizasyon susuz o-diklorobenzen içerisinde inört atmosferde yaklaşık 100 oC de 24 saat yürütülmüştür. Başlatıcı olarak tNaBuO [M]/[I]=30 oranında kullanılmıştır ve radikal polimerizasyonu önlemek için N-fenil-beta-naftilamin serbest radikal polimerizasyon inhibitörü olarak % 0,1 oranında kullanıldı. Polimerizasyon sonrasında ortama asetik asit elenerek ortam nötralleştirildi. Böylece aktif anyonik zincir uçları protonlanarak polimerizasyon sonlandırıldı. Gooch krozesi ile vakum pompası yardımıyla süzülerek ayrılan polimerler soğuk metanol ile yıkandı ve inhibitör, baz ve çözücü kalıntıları uzaklaştırıldı. Islak polimer örnekleri vakum etüvünde 49 oC de 7 saat bekletilerek mevcut çözücü ve nem kalıntıları tamamen uzaklaştırıldı. Ürünlerin spektroskopik özellikleri 1H-NMR ve FT-IR teknikleriyle, termik özellikleri TGA ve DSC teknikleriyle belirlendi. Sentezlenen polimerlerin ağırlıkça ortalama molekül ağırlıkları Dinamik Işık Saçılımı yöntemiyle tespit edildi. Morfolojik özellikleri ise SEM analizi ile incelendi.
Özet (Çeviri)
Synthesis of poly(methyl methacrylate-g-β-alanine) brush type copolymers was carried out by means of free radical polymerization (FRP) of nylon 3 (polyβ-alanine) macro monomer including vinyl group and methyl methacrylate (MMA) vinyl monomer. 2,2′-azobis(2-methylpropionitrile) as initiator and formic acid as a solvent was used at the copolymerization. Synthesis of the brush type copolymer was fulfilled at 70 oC temperature for 50 minutes. For this purpose, polyβ-alanine macro monomer including vinyl group was synthesized by hydrogen transfer polymerization (HTP). Polyβ-alanine was obtained base catalyzed HTP method of acrylamide vinyl monomer. The polymerization that was sensitive to moisture and oxygen was performed in anhydrous o-dichlorobenzene at about 100 oC for 24 hours under inert media. tNaBuO was used as an initiator ([M]/[I]=30). N-phenyl-beta-naphthylamine as free radical polymerization inhibitor was added by 0.1 % to reaction medium to prevent possible free radical polymerization. After the polymerization, acetic acid was added into the reaction medium and the medium was neutralized. Thus, the polymerization was terminated by protonating the active anionic chain-ends. The polymers which were separated by filtration using vacuum pump with Gooch crucible were washed with cold methanol. Traces of inhibitor, base and solvent were removed from the polymers. The polymer samples were kept in a vacuum oven at 49 oC for 7 hours. Then solvent and moisture residues were completely removed. The spectroscopic properties of the products were determined by 1H-NMR and FT-IR techniques, and thermal properties of them were determined by TGA and DSC techniques. The weight molecular weights of synthesized polymers were defined by Dynamic Light Scattering method. The morphological properties of the products were examined by SEM analysis.
Benzer Tezler
- Post-polymerization modification of poly(vinylene sulfide)s
Poli(vinilen sülfit)lerin post-polimerizasyon modifikasyonu
İBRAHİM ETHEM KAKAŞ
Yüksek Lisans
İngilizce
2023
Kimyaİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ UFUK SAİM GÜNAY
- Controlled delivery of chalcone via biopolyester nanohybrid
Biyopoliester nanohibrit ile kalkonun kontrollü salımı
YASEMİN KAPTAN
Doktora
İngilizce
2022
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR
- Targeting circulating breast cancer stem cells via mTOR and WNT inhibitors after bone metastasis
Sirküle meme kanseri kök hücrelerinin kemik metastazı sonrası mTOR ve WNT inhibitörleri ile hedeflenmesi̇
ÖZLEM ALTUNDAĞ ERDOĞAN
Doktora
İngilizce
2025
BiyokimyaHacettepe ÜniversitesiKök Hücre Ana Bilim Dalı
PROF. DR. BETÜL ÇELEBİ SALTIK
- Farklı azot kaynakları kullanılarak çoğaltılan cereibacter sphaeroides O.U.001'in RNA-seq bazlı transkriptom profili
Rna-seq based transcriptome profiling of cereibacter sphaeroides O.U.001 grown using different nitrogen sources
MERVE BAŞTUTAN
Yüksek Lisans
Türkçe
2025
GenetikNecmettin Erbakan ÜniversitesiMoleküler Biyoloji ve Genetik Ana Bilim Dalı
PROF. DR. GÖKHAN KARS
- Alzheimer amiloid beta peptidine ait farklı amino asid dizilerinin polielektrolitler ile konjugasyon reaksiyonlarının incelenmesi
Investigating conjugation reactions between different alzheimer's amyloid beta peptide sequences with polyelectrolytes
BAŞAK İŞCANI EROĞLU
Doktora
Türkçe
2014
BiyomühendislikYıldız Teknik ÜniversitesiBiyomühendislik Ana Bilim Dalı
YRD. DOÇ. DR. ZEYNEP AKDESTE