Harçlarda kullanılan bazı puzolanik malzemelerin tane boyutunun alkali-silika reaksiyonuna ve basınç dayanımına etkisinin araştırılması
Investigation of the effect of difference in particle size of some pozzolinic materials used in mortars on alkali-silica reaction and pressure strength
- Tez No: 576634
- Danışmanlar: PROF. DR. BAHRİ ERSOY
- Tez Türü: Yüksek Lisans
- Konular: Maden Mühendisliği ve Madencilik, Mining Engineering and Mining
- Anahtar Kelimeler: Alkali agrega, Alkali silika reaksiyonu, Doğal zeolit, Uçucu kül, Alkali aggregate, Alkali silica reaction, Natural zeolite, Fly ash
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Afyon Kocatepe Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, beton harcının alkali silika reaksiyonuna (ASR) bazı puzolinik madde olarak kullanılan mineral katkıların tane boyutunun etkisi araştırılmıştır. Bu kapsamda Soma termik santrali dip külü (taban külü) ve Gördes zeoliti beş farklı öğütme süresi (0, 30, 60, 180 ve 240 dk) kullanılarak öğütme işlemi gerçekleştirildi ve beş farklı tane boyut grubuna sahip mineral katkı elde edildi. Her bir tane boyutundaki katkılardan sırasıyla %10, 20 ve 30 oranında çimento yerine ikame edilerek beton harçları hazırlandı. Harç hazırlamada agrega olarak Doğancık köyü (Sultandağı/Afyonkarahisar) deresinden alınan doğal ince agrega ve CEM-I 42,5 çimentosu kullanıldı. Hazırlanan harç çubuklarına TS 13517'ye göre hızlandırılmış harç çubuğu yöntemiyle ASR'den kaynaklı genleşme miktarları belirlenmiştir. Çalışmalar sonucunda, alkali silika reaksiyonunu bastırması ve genleşmeyi engellemesi bakımından en iyi sonuçları dip külü için 240 dk. öğütülmüş (d50:16,79 µm) ürünün %30 ikamesi ile elde edilmiştir. Bu ürün katkısız üretilen harca göre genleşme oranını %85,86 oranında azalttığı ve basınç dayanımında ise önemli oranda bir azalmaya (%2,45) neden olmadığı saptanmıştır. Zeolit ile yapılan çalışmalarda ise en iyi sonucun 240 dk. öğütülmüş (d50:10,49 µm) ürünün %10 ikamesi ile elde edilmiştir. Zeolitin %10 ikamesi ile üretilen harçlarda genleşmelerin mineral katkısız harçlarla hazırlananlara göre yaklaşık %98 azaldığı, ancak basınç dayanımında da yaklaşık %29 oranında bir azalma olduğu saptanmıştır.
Özet (Çeviri)
In this research, the effect of the particle size of mineral additive used as some pozzolanic substance on the alkali silica reaction (ASR) of the concrete mortar was investigated. In this context, Soma thermal power plant bottom ash (floor ash) and Gördes zeolite were grinned using five different grinding times (0, 30, 60, 180 and 240 min) and a mineral additive with five different particle size was obtained. Concrete mortars were prepared by substituting respectively 10%, 20 and 30 of cement from each particle size additive. The natural thin aggregate and CEM-I 42.5 cement taken from Doğancık village (Sultandağı / Afyonkarahisar) stream were used as aggregate in the preparation of mortar. Percent expansion values of the mortars resulting from ASR were determined by accelerated mortar bar method according to TS 13517. As a result of the studies, the best results for suppressing alkali silica reaction and preventing expansion for bottom ash, 240 min. (d50:16,79 µm) obtained with a 30% substitution of the product obtained. This product, according to the mortar produced without additive, decreased the rate of expansion by 85,86% and compressive strength did not cause a significant decrease (2.45%). In the studies with zeolite, the best result was obtained with a 10% substitution of the product obtained at the grinding time of 240 min (d50:16,79 µm). The decrease by ~ 98% in the expansion compared to those prepared with mineral additive, but in the pressure strength the decrease by ~29% was determined in the mortars produced with 10% substitution of zeolite.
Benzer Tezler
- Mitigating alkali silica reaction using waste glass powder
Alkali silika reaksiyonunun azaltılması için atık cam tozu kullanımı
ABED ALİOGLU
Yüksek Lisans
İngilizce
2024
İnşaat Mühendisliğiİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZGÜR EKİNCİOĞLU
- Patates çeşitlerinin dondurulmasında ön işleme teknikleri ve kaliteye etkileri
Başlık çevirisi yok
Y.BİROL SAYGI
Yüksek Lisans
Türkçe
1984
Gıda MühendisliğiEge ÜniversitesiGıda Teknolojisi Ana Bilim Dalı
YRD. DOÇ. DR. SUZAN KINCAL
- İki melez pamuk populasyonunda verim ve verimle ilgili özellikler üzerinde araştırma
Başlık çevirisi yok
MEVLÜT TOS
Yüksek Lisans
Türkçe
1986
ZiraatEge ÜniversitesiTarla Bitkileri Ana Bilim Dalı
PROF. DR. ŞÜKRÜ HAZIM EMİROĞLU
- Halı ipliği yapımında kullanılan yünlerin teknolojik özellikleri üzerinde araştırmalar
Investigations on the technological properties of wools which are used in woollen carpet yarn production
BEKİR YILMAZ
Doktora
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTarım Ürünleri Teknolojisi Ana Bilim Dalı
PROF. DR. MUSTAFA HARMANCIOĞLU