In vitro evaluation of the effect of monobond etch and prime mep application on shear bond strength and bonding between resin cement and lithium disilicate glass ceramic

MEP (Monobond etch & prime) uygulamasının lityum disilikat seramik ve rezin siman arasındaki makaslama bağlanma dayanımına etkisinin değerlendirilmesi

PDF İndir

  1. Tez No: 574176
  2. Yazar: MUSTAFA MEGHLAJ
  3. Danışmanlar: PROF. DR. YASEMİN ÖZKAN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental porselen, Dental stres analizi, Dental çimentolar, Lityum, Dental bonding, Dental materials, Dental porcelain, Dental stress analysis, Dental cements, Lithium
  7. Yıl: 2019
  8. Dil: İngilizce
  9. Üniversite: Marmara Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Amaç: Bu çalışmanın amacı MEP uygulamasının rezin siman ve lityum disilikat seramik arasındaki makaslama bağlanma dayanımı üzerine etkisinin değerlendirilmesidir. Gereç ve Yöntemler: Altmış adet ısıyla preslenmiş lityum disilikat diskler 2 gruba ayrıldı (n = 15) (IPS E-max Pres ve GC LiSi Pres). İki grubun yuzeyıne 4.5% HF asid uygulandı ve 7 mm Kompozit Çubuk Tetric N-Ceram ve G-ænial posterior (Variolink Esthetic LC ve G-CEM LinkForce DC) ile kaplandı. Diğer iki gruba ise MEP uygulandı ve aynı yapıştırma simanı kullanıldı. Polimerizasyon için ve LED cihaz 1200 mW / cm2 kullanıldı. Sonrasında 5 ° C ve 55 ° C sıcaklıklarda 20000 termal döngü yapıldı. Kırılma dayanımı değerleri universal test cihazı (shimadzu universal machine) ile ölçüldü. Verilerin istatistiksel analizi SPSS istatistik programı kullanılarak yapıldı. Ölçüm sonuçlarından elde edilen değişim değerlerinin istatistiksel olarak değerlendirilmesinde ANOVA testi kullanıldı. (P <0.05). Bulgular: Seramiklerin bağlama kuvveti üzerindeki etkisi istatistiksel olarak anlamlı bulunmadı (p = 0.699). SBS gösterdi, HF asidi ve GC siman en yüksek değeri 315,15 ± 90,6, ardından sırası ile variolink siman ile MEP 292,55 ± 84,38, variolink siman ile HF asidi, 274,06 ± 61,59 olduğu görüldü. MEP ve GC siman en düşük değeri (235,49 ± 79,3) göstermiştir. Sonuç: HF asitli GC siman tüm gruplar arasında en iyi sonucu göstermiştir. Variolink siman bulunan MEP sistemi, diğer gruplarla kıyaslayınca daha iyi sonuçlar göstermiştir. Simantasyon işlemlerinde MEP intraoral olarak basit ve güvenli bir şekilde kulanılabilir.

Özet (Çeviri)

Aim: This study aims to evaluate the effect of monobond etch and prime (MEP) application on shear bond strength between resin cement and ceramics. Materials and Methods: Sixty heat-pressed lithium disilicate discs were divided into four groups (n=15) (IPS E-max Press and GC Initial LiSi Press). Two groups were fabricated and surface treated by HF acid 4.5% and cemented to 7 mm diameter Composite bars of Tetric N-Ceram and G‐ænial posterior by (Variolink Esthetic LC and G-CEM LinkForce DC). The other two groups were treated by MEP and carried out with the same cement sequence. LED device 1200 mW/cm2 used for the curing and thermocycling procedure was carried out in 5°C and 55°C temperatures for 20000 thermal cycles. Shear bond strength values were measured by a universal testing machine (shimadzu universal machine). Statistical analysis of the data was performed using the SPSS statistical program. ANOVA test will be used for statistical evaluation of the change values obtained from the measurement results (P <0.05). Results: The effect of ceramic on the binding force was not statistically significant (p=0.699). SBS showed, HF acid and GC cement yielded the highest value of 315,15 ± 90,6, then MEP with variolink cement yielded 292,55 ± 84,38, HF acid with variolink cement yielded 274,06 ± 61,59 and MEP with GC cement presented the lowest value of 235,49 ± 79,3. Conclusion: GC cement with HF acid significantly showed the best result among all groups. MEP system with variolink cement showed more desirable results in comparison to the remaining groups. Cementation steps can be done simply and safely intraorally with MEP.

Benzer Tezler

  1. Tez No

    311159

    Silan bağlanma ajanlarının self adeziv rezin siman- cam fiber post arasındaki mikrotensil bağlanma dayanımı üzerine olan etkisinin in-vitro incelenmesi.

    In-vitro evaluation of the effect of silane coupling agents on microtensile bond strength between self adhesive resin cements and glass fiber posts.

    ÇAĞLAR YAŞA

    Yüksek Lisans

    Türkçe

    Türkçe

    2011

    Diş HekimliğiYeditepe Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    PROF. DR. MÜBİN SOYMAN

  2. Tez No

    625679

    Farklı kompozit rezin korların epoksi rezin ve metakrilat matriks yapısındaki cam fiber postlara bağlanmasında silanın etkisinin incelenmesi

    The evaluation of the bond strength between resin cores and glass fiber posts with different matrices, and the effect of silanization

    İLKNUR USTA KUTLU

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2015

    Diş HekimliğiAtatürk Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. NURAN DİNÇKAL YANIKOĞLU

  3. Tez No

    535801

    In-vitro evaluation of the effect of two surface treatment techniques and three adhesive systems on the shear bond strength of aged composite resin repair

    İki değişik yüzey hazırlığı ve üç farklı adeziv sistem uygulamasının yaşlandırılmış kompozitlerde yapılan tamir işleminin makas kuvvetlere karşı dayanımının in vitro incelenmesi

    AML AL MAGTOF MOHAMED SHABAN

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Diş HekimliğiYeditepe Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ALİ KAĞAN GÖKÇE

  4. Tez No

    82577

    In vitro experimental evaluation of the effect of diferent lining materials and alloy shape on fracture resistance of class II amalgam restorations

    Değişik taban maddelerinin ve amalgam alaşım tiplerinin sınıf II amalgam restorasyonların kırılma direnci üzerine etkilerinin in vitro şartlarda deneysel olarak incelenmesi

    NESLİHAN EMİNKAHYAGİL

    Yüksek Lisans

    İngilizce

    İngilizce

    1999

    Mühendislik BilimleriOrta Doğu Teknik Üniversitesi

    Mühendislik Bilimleri Ana Bilim Dalı

    DOÇ. DR. YUSUF ORÇAN

  5. Tez No

    748689

    An in vitro evaluation of the effect of different ceramic type, ceramic thickness and aging on color and translucency changes of lithium disilicate, zirconia reinforced lithium silicate, leucite reinforced and feldspathic ceramic veneers.

    Farklı seramik tipi, seramik kalınlığı ve yaşlandırmanın lityum disilikat, zirkonya ile güçlendirilmiş lityum silikat, lösit ile güçlendirilmiş cam seramik ve feldspatik seramiklerin renk stabilitesi ve translüsensi üzerine etkisinin ın vitro olarak incelenmesi

    ŞEYMA TUNA ÜNAL

    Doktora

    İngilizce

    İngilizce

    2022

    Diş HekimliğiYeditepe Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    PROF. DR. ESRA CAN EROĞLU

Geri Dön