Farklı renk, kalınlık ve materyallerle üretilen lamina venerlerin renk maskeleme özelliklerinin in vitro incelenmesi
Effect of thickness and material shade on the color masking ability of laminate veneers
- Tez No: 560381
- Danışmanlar: PROF. DR. CAN DÖRTER
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: discolored teeth, dental veneers, dental porcelain, dental esthetics, CADCAM, CAD/CAM, Dental estetik, Dental materyaller, Dental porselen, Dental restorasyon, Dental restorasyon-sürekli, Diş kaplamaları, Diş renk değişikliği, renkleşmiş dişler, lamina vener, porselen, estetik dişhekimliği, CADCAM, CAD/CAM, Dental aesthetics, Dental materials, Dental porcelain, Dental restoration, Dental restoration-permanent, Dental veneers, Tooth discoloration
- Yıl: 2019
- Dil: Türkçe
- Üniversite: İstanbul Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı 4 farklı CAD/CAM materyali ile yapılan farklı kalınlıklardaki porselen lamina venerlerin renkleşmiş bir substratı maskeleme yeteneğini ölçmektir. C2 rengindeki kompozit reçineden (Filtek Z550) paslanmaz çelik kalıp ile 12x14 mm boyutlarında ve 4 mm kalınlığında 150 adet substrat oluşturulmuştur. Substratların rengi VITA Easyshade spektrofotometreyle ölçülmüştür. Lamina venerler elmas kesme diski ile IPS e.max MT ve LT (EMX-MT, EMX-LT), IPS Empress LT (EMP), Celtra DUO LT (CD), VITA Suprinity T (VS) CAD/CAM bloklardan 0.3, 0.5 ve 0.8 mm kalınlıklarda kesilmiştir (n=10). Variolink II ışıkla sertleşen reçine siman ile lamina venerler substratlar üzerine üretici firmanın direktifleri doğrultusunda simante edilmiştir. Simantasyon esnasında örneklerin üzerine 1 kg ağırlık konmuştur. 20 sn sonra ağırlık kaldırılıp, taşan siman temizlenerek 10 sn ışık uygulanmıştır. Örneklerin rengi tekrar ölçülmüştür. Elde edilen iki renk değeri arasındaki fark ΔE formülüyle hesaplanmıştır. Elde edilen bulgular Pearson Korelasyon Analizi, One-way ANOVA testi, Tukey HDS testi ve Tamhane's T2 testi ile karşılaştırıldı (p<0.05). Elde edilen bulgulara göre VS hariç tüm materyallerde kalınlık ve renk maskeleme yeteneği arasında pozitif korelasyon bulunmuştur. Materyallerin kalınlığa göre ΔE değerlerinin hesaplanmasında tüm gruplarda en düşük ΔE'yi VS göstermiştir. En yüksek ΔE ise 0.3 mm'de EMX-MT, 0.5 mm'de CD ve 0.8 mm'de CD olmuştur. Tüm materyallerde kalınlık arttıkça ΔL artmıştır. Bu çalışmanın renkleşmiş dişlere porselen lamina vener yapılması konusunda kliniğe rehber olması hedeflenmektedir.
Özet (Çeviri)
The aim of this study was to investigate the shade masking ability of laminate veneers made from 4 different CAD/CAM materials. To mimic the discolored tooth, C2 shade of Filtek Z550 composite resin was used. A stainless steel mold containing 12x14 mm slots with 4 mm thickness was used to prepare 150 substrates. Shade of the substrates was measured with VITA Easyshade spectrophotometer. Laminate veneer samples of 0.3 mm, 0.5 mm and 0.8 mm layers were cut with a low-speed diamond disc from IPS e.max CAD MT and LT (EMX_MT, EMX-LT), IPS Empress CAD (EMP), Celtra DUO LT (CD), VITA Suprinity T (VS) blocs. Substrates and laminate veneers were cemented using Variolink II light curing resin cement. During the procedure, a 1 kg weight was placed on top of the veneer. After 20 seconds the weight was removed and the excess cement was cleared away. The shade of the samples was measured again. The difference between two shades was calculated using the ΔE formula. The statistical analyses were performed by Pearson Correlation Analysis, One-way ANOVA, Tukey HDS and Tamhane's T2 test (p<0.05). According to the results, thickness and shade masking ability of all materials except VS were in positive correlation. Lowest ΔE values in every thickness was shown by VS. EMX-MT shows the highest ΔE value in 0.3 mm and CD in 0.5 mm and 0.8 mm. In all materials, ΔL is increased with thickness. This study targets to be a guide for clinicians about masking dark-colored teeth with laminate veneers.
Benzer Tezler
- Zein esaslı yenilebilir filmlerin üretiminde plastikleştirici olarak derin ötektik çözücü kullanımı
Use of deep eutectic solvent as a plasticizer in the production of zein based edible film
EBUBEKİR KUL
Yüksek Lisans
Türkçe
2022
Gıda MühendisliğiBursa Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
DOÇ. DR. FURKAN TÜRKER SARICAOĞLU
- Tekrarlanan fırınlama sonrasında farklı altyapı hazırlama tekniklerinin ve üstyapı kalınlıklarının renk değişimine etkisi
The effect of different porcelain thicknesses and framework fabrication techniques on color changes after repeating firings
MEHMET GÖKBERKKAAN DEMİREL
Doktora
Türkçe
2019
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ALİ RIZA TUNÇDEMİR
- Kalınlık farklılıklarının zirkonya esaslı alt yapı metaryalinin kırılma dayanımına olan etkisi
The impact of thickness differences to the breaking resistance of zirconia based infrastructure material
ECE TATAR SIDAL
Doktora
Türkçe
2013
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Valorization of pea by-products: Development of protein-enriched biodegradable films
Bezelye yan ürünlerinin değerlendirilmesi: Proteinle zenginleştirilmiş biyobozunur filmlerin geliştirilmesi
NİHAL SULTAN BAYAR
Yüksek Lisans
İngilizce
2025
Gıda Mühendisliğiİstanbul Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. NEŞE ŞAHİN YEŞİLÇUBUK
- Farklı sıvılarda bekletilen üç farklı protez kaide materyalinin termal siklus uygulanarak renk stabilitesi ve yüzey pürüzlülüğünün karşılaştırılması
A comparison of color stability and surface roughness of three different denture base materials using thermocycling and after storage in different solutions
ÖYKÜ PIRNAR YILMAZ
Doktora
Türkçe
2023
Diş HekimliğiSağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SİBEL DİKİCİER