Ortodontik braketlerin bağlanma dayanımının ve ortodontik yapıştırıcıların polimerizasyon derecesi ve mikrosertiliğinin yeni nesil ışık cihazlarında farklı ışık gücü kullanılarak değerlendirilmesi
Evaluation of the bond strength of orthodontic brackets, degree of polymerisation and microhardness of orthodontic adhesive by using the new generation light device with di̇fferent li̇ght power
- Tez No: 515535
- Danışmanlar: YRD. DOÇ. DR. YASİN ATAKAN BENKLİ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Ordu Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Ortodonti Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Çalışmanın amacı Ligth-Emitting Diode (LED) ışık cihazının (Valo, Ultradent) standart 1000 mW/cm² (10 sn), 1400 mW/cm² (8 sn) ve 3200 mW/cm² (3 sn) güçlerindeki ışık modları kullanılarak polimerizasyonu sağlanan ortodontik yapıştırıcının (Transbond XT, 3M); polimerizasyon derecesinin (FTIR analiz), termo saykıl yöntemi kullanılarak yaşlandırılan örnekler üzerinde makaslama kuvvetinin (Sıyırma Testi) ve mikro-sertliğinin (Vickers) ölçülmesidir. İncelenecek örneklerin boyut ve çapı kullanacağımız test metodlarına göre özel olarak hazırlanmıştır. Çalışmada, 135 adet diş sıyırma testi için ve 90 adet braket yapıştırıcı örnek Vickers mikro-sertlik testi için hazırlanmıştır. Hazırlanan örnekler üzerinde başlangıç, ısısal yaşlandırma yöntemi ile 500 ve ısısal yaşlandırma yöntemi ile 10.000 döngü olmak üzere toplamda 3 zaman diliminde ölçüm yapılmıştır. Sıyırma testinden sonra örnekler stereomikroskop altında x25 büyütmede incelenerek ARI skoru kaydedilmiştir. Dayanım ve mikro-sertlik verilerinin değerlendirilmesinde İki-yönlü Varyans Analizi (Two-way ANOVA) ve Tukey çoklu karşılaştırma testi kullanılmıştır. Çalışmada en yüksek sertlik düzeyi, 10 sn'lik ışınlama yapılan kontrol grubundaki (57,08) ve 10.000 siklus termo saykıl uygulanmış (55,96) deney grubundaki dişlerde; en düşük sertlik düzeyi ise 3 sn'lik ışınlama yapılan ve 10.000 siklus termo saykıl uygulanmış (39,22) deney grubundaki dişlerde belirlenmiştir. Termo saykıl uygulanmış ve Termo saykıl uygulanmamış gruplar arasında braketlerin bağlanma dayanımları açısından anlamlı bir farklılık olmadığı görülmüştür. Çalışma gruplarını kendi içinde değerlendirdiğimizde kontrol grubunun uygulama süreleri arasında braketlerin bağlanma dayanımları açısından anlamlı bir fark görülmemiştir. 10.000 Termo saykıl uygulanmış 8 sn ve 10 sn polimerize edilmiş gruplar arasında bağlanma dayanımı açısından birbirine yakın değerler elde edilmiş iken, 3 sn polimerize edilmiş grubun değerleri daha düşük bulunmuştur. Kopma yüzeyleri açısından incelendiğinde, kontrol grubu ve deney gruplarında ışınlama sürelerine göre ARI skorlarının değişmediği belirlenmiştir. FTIR sonuçlarına baktığımızda, en düşük dönüşüm derecesi 3 sn ışınlanan örnekte görülmüştür, 8 sn ışınlanan örnekte elde edilen DC değeri, 10 sn ışınlanandan bir miktar daha yüksek bulunmuştur. Sonuç olarak; Polivawe LED ışık cihazının 10 sn ve 8 sn süre ile braket yapıştırılmasında in vitro koşullar altında Transbond XT'nin mikro-sertlik ve dönüşüm derecesi değerleri açısından yeterli bağlanmayı sağladığı görülmüştür. Ancak 3 sn uygulama yapılan gruplardaki bu değerler düşük bulunmuştur.
Özet (Çeviri)
The aim of this study is to evaluate the shear bond strength, microhardness and degree of cure of the orthodontic adhesive resin Transbond XT immediately and after 500 and 10.000 thermocycle, which is polimerized by three different modes of poliwave LED light curing unit Valo, Ultradent including standard 1000 mW/cm² (10 sn), high power 1400 mW/cm² (8 sn) and extra power 3200 mW/cm² (3 sn). The dimension and the diameter of the prepared specimen have been determined specially according to the used methods. 135 brackets were bonded for shear bond test and 90 disc shaped orthodontic adhesive resins were prepared for Vickers hardness test. The measurements were done immediately and after 500 and 10.000 thermocycle. After shear bond strength (SBS) tests ARI scores were stored by the research with a steromicroscope having a x25 magnification factor. SBS and Vickers microhardness (VHN) test datas were statistically evaluated by (Two-way ANOVA) and Tukey multiple comparision tests. 10 sn polymerized control group (57,08) and 10.000 termocycled samples (55,96) showed the highest VHN. On the other hand, 3 sn polimerized and 10.000 thermocycled experimental group samples showed the lowest VHN (39,22). The highest bond strength values were seen in control groups respectively 10 sn, 8 sn, 3 sn light cured. While similar bond strength values were being detected for 10.000 thermocycled groups light cured by 8 sn and 10 sn; 3 sn light cured groups showed lowest values. As they were researched in terms of bond failure surfaces, it was determined in the study that the ARI scores did not change in both control and experimental groups according to light curing duration. According to FTIR results; the lowest Degree of cure (DC) was seen in 3 sn light cured sample. In conclusion, it has been observed that Transbond XT has satisfied the sufficient bonding in terms of microhardness and degree of cure values under in vitro conditions by the bracket bonding during 10 and 8 sn using poliwave LED curing unit. But low values in the groups applied 3 sn have been obtained.
Benzer Tezler
- Metal ve porselen braketlerin yapıştırılmasında farklı ışık gücü uygulandığında mine yüzeyiyle olan makaslama bağlanma dayanımlarının ve mikrosertliğinin değerlendirilmesi
Evaluation of the shear bond strength and microhardness with the enamel surface when different light power is applied in the adhesive of metal and porcelain brackets
CANSU ŞEYMA AĞRILI
Doktora
Türkçe
2024
Diş Hekimliğiİstanbul Kent ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MERVE KURNAZ
- Ortodontik braketlerin konvansiyonel ve lazer destekli yüzey pürüzlendirme yöntemleriyle hazırlanan monolitik zirkonya yüzeylerine kendinden primerli tek aşamalı sistem ile bağlanma dayanımının karşılaştırmalı olarak değerlendirilmesi
Comparative evaluation of the bond strength of orthodontic brackets to monolithic zirconia surfaces prepared by conventional and laser-assisted surface roughening methods using a self-priming one-step adhesive system
FATMA SELEN ESENLİK
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiAlanya Alaaddin Keykubat ÜniversitesiOrtodonti Ana Bilim Dalı
PROF. DR. MEHMET AKIN
- Ortodontik metal ve seramik braketlerin yapıştırılmasında kullanılan primersiz tek adımlık sistemin mikrosızıntı ve bağlanma dayanımlarının farklı adeziv sistemleri ile in vitro olarak karşılaştırılması
In vitro comparison of microleakage and bond strength of one-step sysyem without primer used in bonding of orthodontic metal and ceramic brackets with different adhesive systems
HANDAN BAYAR BİLEN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiPamukkale ÜniversitesiOrtodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SERPİL ÇOKAKOĞLU
- Evaluation of shear bond strength of rebonded orthodontic brackets after different recycling methods
Farklı geri dönüşüm metodlarından sonra yeniden bağlanmış ortodontik braketlerin makaslama bağlanma dayanımının değerlendirilmesi
USAMA IBRAHIM A BSHAYA
Yüksek Lisans
İngilizce
2018
Diş Hekimliğiİstanbul Yeni Yüzyıl ÜniversitesiOrtodonti Ana Bilim Dalı
PROF. DR. İLTER UZEL
- Porselen yüzeylere yapıştırılan yeni ve farklı metotlarla geri dönüştürülmüş seramik braketlerin bağlanma dayanımlarının değerlendirilmesi
Evaluation of bond strength of new and recycled with different methods ceramic brackets bonded to porcelain surfaces with different surface roughening methods
EMİNE KARSLI ÇAĞLAR
Doktora
Türkçe
2023
Diş Hekimliğiİstanbul ÜniversitesiOrtodonti Ana Bilim Dalı
DOÇ. DR. SÜLEYMAN EVREN ÖZTAŞ