TiB2 ve B4C takviyeli kompozitlerin toz metalurjisi yöntemiyle üretilebilirliğinin incelenmesi
Investigation of the productivity of TiB2 and B4C reinforced composites by powder metallurgy method
- Tez No: 507901
- Danışmanlar: PROF. DR. RECEP ÇALIN, DR. ÖĞR. ÜYESİ UĞUR GÖKMEN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Toz metalurjisi, Powder metallurgy
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Savunma Teknolojileri Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, toz metalurjisi (T/M) ve sıcak presleme tekniği ile seramik parçacık takviyeli metal matrisli kompozit (MMK) malzemeler üretmek ve parçacık türünün etkilerini araştırmaktır. Matris malzemesi olarak ön alaşımlı Al 5154 metal tozları, takviye elemanı olarak TiB2 ve B4C parçacıklar kullanılmıştır. Al 5154 matris içerisine ağırlıkça farklı oranlarda (%5, 10 ve 15) TiB2 ve B4C parçacıklar ilave edilmiştir. Parçacık takviyeli metal matrisli kompozit malzemelerin üretimde TiB2 ve B4C parçacıklar ile Al 5154 tozu üç boyutlu karıştırıcıda 30 dakika karıştırılmıştır. Karışım tozlar 300°C sıcaklıkta ve 200 MPa basınçta preslenmiştir. Elde edilen toz metal blok numuneler 580°C sıcaklıkta 1 saat sinterlenmiştir. Sinterleme işlemi sonrası numuneler tel erozyon yöntemi ile kesilerek standart boyutlarda çapraz kırılma test numuneleri elde edilmiştir. Yapılan ölçümler sonunda sıcak presleme ve sinterleme işlemleri ile numunelerin yoğunluğunda değişimler olduğu görülmüştür. TiB2 parçacık miktarı arttıkça yoğunluğun arttığı tespit edilmiştir. Takviye elemanın miktarındaki artışa bağlı olarak sertlik ve çapraz kırılma dayanım değerlerinde artış tespit edilmiştir. Bu çalışmada en yüksek çapraz kırılma dayanımı (151 MPa) ve en yüksek sertlik (60.2 HB) değerleri %15 TiB2 takviyeli numunelerde sağlanmıştır.
Özet (Çeviri)
Aim of this study is to produce ceramic particle reinforced metal matrix composite (MMC) materials by powder metallurgy (P/M) and hot pressing technique and to investigate the effects of particle type. In the study, pre-alloyed Al 5154 metal powders were used as a matrix material. TiB2 and B4C particles were used as reinforcement element (5-10-15% wt.). Matrix powder and reinforcement components were mixed in a three dimensional mixer for 30 minutes. Mixed powders were compacted at 300oC and 200 MPa. These blocks were sintered at 580oC for 1 hours. Then samples were cut with wire erosion method to ensure the appropriate standard dimension for transverse rupture strength (TRS) tests. The changes in the density of the samples were observed with hot pressing and sintering processes. It has been determined that as the amount of TiB2 and B4C particles increases, the density increases. Moreover, rising in hardness and transverse rupture strength values were determined depending on the increase in the amount of the reinforcing components. In the study, maximum transverse rupture strength of 151 MPa and hardness of (60.2 HB) were reached with at %15 TiB2 reinforced samples.
Benzer Tezler
- Metalotermik prosesle titanyum-bor-alüminyum alaşımlarının üretimi
Başlık çevirisi yok
ÇİĞDEM GÖZKOMAN
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ONURALP YÜCEL
- CuZnAlTiB shape memory alloys: Production, characterization and design
CuZnAlTiB şekil bellekli alaşımlarının üretimi, karakterizasyonu ve tasarımı
YUSUF ZİYA KARABAY
Yüksek Lisans
İngilizce
1998
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAKİR BOR
- Effect of cyclic deformation on shape memory behavior of CuZnAI shape memory
CuZnAL alaşımlarında döngüsel yüklemenin şekil bellek davranışına etkisi
GAMZE SARANLI
Yüksek Lisans
İngilizce
1998
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAKİR BOR
- Free and constrained pseudoelasticity in CuZnAI shape memory alloys
CuZnAI şekil bellekli alaşımlarda serbest ve kısaltılmış süperelastik davranış
ALTAY ŞEREF ÖZAYGEN
Yüksek Lisans
İngilizce
1999
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAKİR BOR