200°C'nin üzerinde ısıl işlem uygulanan ve verniklenen odunun dış ortam koşullarında fiziksel performans özelliklerinin belirlenmesi
Determination physical properties of heated above 200°C and varnished wood after weathering
- Tez No: 498535
- Danışmanlar: PROF. DR. ERGÜN BAYSAL
- Tez Türü: Yüksek Lisans
- Konular: Ağaç İşleri, Wood Products
- Anahtar Kelimeler: Isıl İşlem, Sarıçam (Pinus Sylvestris L.), Doğu Kayını (Fagus Orientalis Lipsky), Poliüretan Vernik (PV), Selülozik Vernik (SV), Doğal Yaşlandırma, Yüzey Pürüzlülüğü, Renk, Parlaklık, Heat Treatment, Scots Pine (Pinus Sylvestris L.), Oriental Beech (Fagus Orientalis Lipsky), Polyurethane Varnish (PV), Cellulosic Varnish (CV), Surface Roughness, Color, Gloss
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Muğla Sıtkı Koçman Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Ağaç İşleri Endüstri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada ısıl işlem gören ve daha sonra verniklenen sarıçam ve Doğu kayını odununun Muğla yöresi iklim koşullarında 3 ve 6 aylık sürelerde doğal yaşlandırma işlemine tabi tutulduktan sonra yüzey pürüzlülüğü, parlaklık ve renk değişimi gibi bazı yüzey özelliklerinin belirlenmesi amacıyla gerçekleştirilmiştir. Isıl işlem sarıçam ve Doğu kayını odunu için fırında 1, 2 ve 3 saat sürede 205, 215 ve 225°C'ler de gerçekleştirilmiştir. Isıl işlemden sonra Sarıçam ve Doğu kayını odunu deney örnekleri poliüretan ve selülozik vernikle vernikleme işlemine tabi tutulmuştur. Deney sonuçlarına göre doğal yaşlandırma işlemi deney örneklerinin yüzey pürüzlülüğünde artışa sebep olmuştur. Isıl işlem gören ve daha sonra verniklenen doğu kayını ve sarıçam deney örnekleri yüzey pürüzlülüğü, parlaklık ve renk gibi yüzey özellikleri açısından sadece verniklenen deney örneklerine göre doğal yaşlandırma işleminden sonra daha olumlu sonuçlar vermiştir. Genellikle ısıl işlem süresi ve sıcaklık arttıkça sarıçam ve Doğu kayını odunu deney örneklerinin yüzey özelliklerinde olumlu yönde iyileşmeler gözlemlenmiştir. Deney sonuçlarına göre doğal yaşlandırma işlemi sonunda poliüretan vernikle verniklenen deney örnekleri yüzey pürüzlülüğü ve renk bakımından daha olumlu sonuçlar verirken, selülozik vernikle verniklenen deney örnekleri parlaklık değerleri açısından daha olumlu sonuçlar vermiştir.
Özet (Çeviri)
This study was performed to investigate some surface characteristics such as surface roughness, gloss, and color changes of heated and varnished Scots pine (Pinus sylvestris L.) and Oriental beech (Fagus orientalis Lipsky) after weathering for 3 and 6 months in Mugla Region. Heat treatment of Oriental beech and Scots pine woods were carried out by hot air in an oven for 1, 2, and 3 h at 205, 215, and 225°C. After heat treatment, Scots pine and Oriental beech wood specimens were varnished using a polyurethane and cellulosic varnish. The results showed that weathering caused increase of surface roughness of wood specimens. Heated and varnished Oriental beech wood gave better surface characteristics such as surface roughness, gloss and color characteristics than only varnished Oriental beech and Scots pine after weathering. Generally, higher duration and temperature for Scots pine and Oriental beech resulted in better surface characteristics of Oriental beech and Scots pine woods after weathering. Our results showed that while polyurethane varnished wood gave better results in terms of surface roughness and color characteristics, cellulosic varnished wood gave better results in terms of gloss values after weathering.
Benzer Tezler
- 7075 alüminyum alaşımında RRA ısıl işleminin mikroyapıya etkisi ve kinetik analiz
Effect of retrogression and reaging (RRA) heat treatment on the microstructure of the 7075 aluminium alloy and kinetics analysis
NURAN AY ÜNVER
- Makine imalat sanayi için düşük karbonlu beynitik çelikalaşım ve proses tasarımı
Alloy & process design of low carbon bainitic steel formachinery industry
BERTAN PARMAKSIZOĞLU
Yüksek Lisans
Türkçe
2022
Metalurji MühendisliğiBursa Teknik Üniversitesiİleri Teknolojiler Ana Bilim Dalı
DOÇ. DR. NAZLI AKÇAMLI
PROF. DR. ARCAN FEHMİ DERİCİOĞLU
- Production of high temperature core-sheath nanofiber proton exchange membranes via electrospinning method
Elektrodokuma yöntemi ile yüksek sıcaklık çekirdek-kılıf nanolif proton değişim membranlarının üretilmesi
SASSAN JAHANGIRI
Doktora
İngilizce
2018
Tekstil ve Tekstil Mühendisliğiİstanbul Teknik ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
DOÇ. DR. ELİF ÖZDEN YENİGÜN
- Ultrason destekli ekstraksiyon ile yer elmasından inülin üretimi
Inulin production from jerusalem artichoke by ultrasound-assisted extraction
BÜŞRA KABATAŞ
Yüksek Lisans
Türkçe
2021
Gıda Mühendisliğiİstanbul Teknik ÜniversitesiGıda Mühendisliği Ana Bilim Dalı
PROF. DR. MERAL KILIÇ AKYILMAZ
- AA7075-T6 alaşımı ve AA7075-T6 alaşımı alt tabaka üzerine HVOF termal sprey ile kaplanmış WC-10Co-4Cr kaplamanın farklı sıcaklıklardaki sürtünme ve aşınma davranışlarının incelenmesi
Investigation of friction and wear behaviors of AA7075-T6 alloy and, HVOF thermal sprayed WC-10Co-4Cr coating on AA7075-T6 alloy substrate at different temperatures
MEHMET CEVİZ
Doktora
Türkçe
2021
Makine MühendisliğiTrakya ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. CENK MISIRLI
DR. ÖĞR. ÜYESİ Sencer Süreyya KARABEYOĞLU