Çiğneme simülatörü ve termal yorulma cihazlarının tasarım ve imalatının yapılarak, in vitro ortamında farklı çiğneme sıcaklıkları, termal çevrim ve ön ısıtmanın üç farklı rezin kompozit malzemenin aşınma özelliklerine etkilerinin incelenmesi
The effect on the wear properties of three diffrent resin composite material of the diffrent chewing temperatures, the thermal cycle and the pre-heating in in vitro environment by design and manufacturing of the chewing simulator and thermal fatigue device
- Tez No: 434863
- Danışmanlar: PROF. DR. RECEP SADELER
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2016
- Dil: Türkçe
- Üniversite: Atatürk Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Konstrüksiyon ve İmalat Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Klinik öncesi yorulma veya aşınma çalışmalarında in vivo deney ortamının etik sorunlarının olması, çok uzun sürede gerçekleşmesi ve maliyetinin yüksek olmasından dolayı in vitro laboratuvar deney ortamı önem kazanmıştır. Ayrıca çiğneme esnasında fizyolojik duruma bağlı olarak ağız içerisinde çiğneme kuvveti ve hareketinin in vitro ortamda tekrarlanabilmesi büyük önem arz etmektedir. Bu çalışmada imal edilecek çiğneme simülatör cihazı ile yapılan deneyler, laboratuvar şartlarında yapay ağız ortamının sağlanması (in vitro ortam) ile gerçekleştirilmiştir. Türkiye'de üniversite ve devlet hastanelerinde kullanılan restoratif materyallerdeki farklı mekanik ve termal yorulma mekanizmalarının etkilerinin bilinmesi, restorasyon için hazırlanacak alanın güç dağılımı doğru şekilde hesaplanarak, hangi tip restorasyonda hangi tür malzeme kullanılması gerektiği hakkında bize bilgi verecektir. Bu araştırmada 1) Rezin kompozitte pre-heating prosedürü sonucunda dönüşüm derecesi (DC%) artışının aşınma miktarında ki etkisi, 2) Farklı ICET(İn vitro çiğneme ortamı sıcaklığı) sıcaklık faktörlerinin RTG ve PTG gruplarında hazırlanan rezin kompozit malzemelerin aşınma miktarındaki etkisi ve 3) DC% artışının hazırlanan yüzeylerin pürüzlülük miktarına etkisini incelenmiştir. Valux™ Plus, x-tra fil ve Charisma® Classic malzemeleri oda sıcaklığı (23°C) ve ön ısıtma sıcaklığında (60°C) 40 saniyelik sürede polimerize edilmişlerdir. RTG ve PTG gruplarının aşınma testleri 49 N yük ve 500.000 mekanik yükleme çevrimi ile birlikte farklı ICET(İn vitro çiğneme sıcaklığı) sıcaklık şartlarında iki eksenli çiğneme simülatörü cihazında gerçekleştirilmiştir. Bu araştırma sonucunda ICET ve ön ısıtma faktörlerinin, malzemenin mekanik davranışlarında ve yüzey pürüzlülüğünde etkili oldukları bulunmuştur.
Özet (Çeviri)
Pre-clinic fatigue or abrasion studies in vitro laboratory test environment become important because to be ethical problems of test environment in vivo, realization on long notice and high of it's cost. Also, by depending upon physiological condition in the course of masticatory, masticatory force inside mouth and repeatability of it's movement in vitro environment have importance. In this study the texts are held by produced chewing simulator device be realized with provided of artificial mouth environment (in vitro environment) on laboratory conditions. In Turkey, university and public hospitals restorative materials that used to known different mechanic and thermal fatigue mechanism's effect will give us information about which type restoration, which type of material that need to use by calculating power distribution of area that get ready for restoration. In this work: 1) Effect of increasing DC% on wear rate as a result of composites resin pre-heating procedure, 2) Influence of different in vitro Chewing Environment Temperature (5°C, 35°C, 55°C and 5/55°C) factors in the composites resin materials which were prepared in RTG (Room Temperature Group) and PTG (Pre-heating Temperature Group) on wear rate and 3) Effect of increasing degree of conversion (DC%) on the amount of surface roughness were examined. Valux™ Plus, x-tra fil and Charisma® Classic materials were polymerized at the pre-heating temperature of 60°C and at the curing time of 40s. The wear tests of RTG and PTG in ICET (In vitro Chewing Environment Temperature) conditions were performed by the dual-axis chewing simulator with 49 N load and 500,000 mechanical loading cycle. The ICET temperature and pre-heating factor for the increase in the mechanical behavior of the material and surface roughness was found to be effective.
Benzer Tezler
- Farklı hibrit ve seramik materyallerin çiğneme simülatörü ile yaşlandırma sonrası bükülme dirençlerinin değerlendirilmesi
Evaluation of flexural strength of different hybrid and ceramic materials after aging in chewing simulator
ECE BİLDİR ÇAKIN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SEMİH BERKSUN
- Comparison of fracture resistance between two monolithic and one veneered zirconia materials on molar crowns after thermomechanical fatigue
Termo-mekanik yaşlandırma sonrası uç zirkonya materyali ile restore edilen molar kuronların kırılma direncinin karşılaştırılması
FAİSAL KAYALI
Yüksek Lisans
İngilizce
2019
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ERKUT KAHRAMANOĞLU
- Braket altında oluşan mikrosızıntının dört farklı bonding tekniğinde termal siklus ve çiğneme simülatörü yöntemleri ile karşılaştırmalı olarak değerlendirilmesi
Evaluation ofthe microleakage under orthodontic brackets bonded with four different bondingtechniques and aged with thermal cyclus and chewing simulation protocols
UFUK OK
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiOrtodonti Ana Bilim Dalı
YRD. DOÇ. DR. BERZA YILMAZ
- Estetik biohpp, zirkonya ve titanyum implant dayanakları ile desteklenen CAD/CAM monolitik lityum disilikat kronların çiğneme simülatörü ve termal döngü ile yaşlandırılması sonrası kırılma dayanımlarının karşılaştırılması
Comparison of fracture strength of CAD/CAM monolithic lithium disilicate crowns supported by esthetic biohpp, zirconia and titanium implant abutments after chewing simulator and thermal cycling aging
MUHAMMET EMİN AKSAN
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiKırıkkale ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SAADET ATSÜ
- Zirkonya esaslı tam seramik ve metal destekli seramik kronların marjinal uyumlarının ve çiğneme simülatörü sonrası aşınma miktarlarının değerlendirilmesi
Evaluation of marginal discrepancy and wear behavior of zirconia based full ceramic and metal supported ceramic crowns after chewing simulator
YADEL HAZIR TEKİN
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiGaziosmanpaşa ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. YELİZ HAYRAN