Zirkonya esaslı tam seramik ve metal destekli seramik kronların marjinal uyumlarının ve çiğneme simülatörü sonrası aşınma miktarlarının değerlendirilmesi
Evaluation of marginal discrepancy and wear behavior of zirconia based full ceramic and metal supported ceramic crowns after chewing simulator
- Tez No: 454028
- Danışmanlar: YRD. DOÇ. DR. YELİZ HAYRAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Zirkonya, porselen, marjinal uyum, çiğneme simülatörü, aşınma, Dental materyaller, Dental oklüzyon, Dental porselen, Dental restorasyon, Kronlar, Zirkonyum oksit, Zirconia, porcelain, marginal discrepancy, chewing simulator, wear, Dental materials, Dental occlusion, Dental porcelain, Dental restoration, Crowns, Zirconium oxide
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Gaziosmanpaşa Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Zirkonya esaslı tam seramik ve metal destekli seramik kronların marjinal uyumlarının ve çiğneme simülatörü sonrası aşınma miktarlarının değerlendirilmesi Amaç: Bu çalışmanın amacı farklı monolitik zirkonya ve metal destekli seramiklerin marjinal uyumlarının ve yaşlandırma işlemlerinden sonra aşınma miktarlarının değerlendirilmesidir. Yöntem: Çalışmamızda, Katana® UTML, Prettau®, Zenostar® T, InCoris® TZI, BruxZir® (0,5 mm, 0,8 mm, 1 mm, 1,5 mm) monolitik zirkonya ve kontrol grubu olarak metal destekli seramik kullanıldı. Her bir gruptan 10'ar adet kron elde edilerek toplam 9 grup oluşturuldu. Örneklerin simantasyonu öncesi silikon replika tekniği ile stereo mikroskop kullanılarak marjinal aralık ölçümleri yapıldı. Marjinal aralık ölçümlerinin ardından örnekler, termal siklusta (5-55 oC, 10 000 siklus) yaşlandırıldı. Aşınma testi; çiğneme simülatöründe (50N, 1 Hz, lateral hareket: 2 mm, ağız açıklığı: 2 mm) metal antagonistlerle, distile su solüsyonu içinde, 12 aylık süreyi yansıtan 240 000 siklus uygulanacak şekilde gerçekleştirildi. Örneklerin aşınmaları lazer tarayıcı ve üç boyutlu çakıştırma yapabilen yazılım programı kullanılarak değerlendirildi. Ortalamalar ve standart deviasyonlar hesaplandı. İstatistiksel analiz; tek yönlü varyans analizi ve anlamlı sonuçlanan tek yönlü varyans analizi sonrası çoklu karşılaştırma için Tukey HSD ve Tamhane T2 testi ile gerçekleştirildi (α=0,05). Bulgular: Örneklerin marjinal aralık ölçümleri arasında anlamlı bir farklılık bulundu (p<0,001). Yapılan ölçümlerde en düşük marjinal aralık değerini BruxZir® (1,5mm) monolitik zirkonya kronlar (46±9μm), en yüksek marjinal aralık değerini de Zenostar® (92±22μm) gösterdi. Örneklerin aşınma ölçümleri arasında anlamlı bir farklılık olduğu belirlendi (p<0,05). Yapılan ölçümlerde en düşük aşınma değerini BruxZir® (0,8 mm) monolitik zirkonya kronlar (0,96±0,81mm2), en yüksek aşınma değerini metal seramik kronlar (4,59±2,08 mm2) gösterdi. Sonuçlar: Monolitik zirkonya seramikler feldspatik porselenlerle karşılaştırıldığında üstün aşınma davranışı sergilediler. Metal destekli ve monolitik zirkonya seramiklerin marjinal aralık ölçümleri klinik olarak kabul edilebilir sınırlar içerisindedir.
Özet (Çeviri)
ABSTRACT Evaluation of marginal discrepancy and wear behavior of zirconia based full ceramic and metal supported ceramic crowns after chewing simulator Aim: The aim of this study is to determine the marginal fit of different monolithic zirconia and metal-supported ceramics and their wear resistance after aging. Material and methods: The present study monolithic zirconias as Katana® UTML, Prettau®, Zenostar® T, InCoris® TZI, BruxZir® (0.5mm,0.8mm,1mm,1.5mm) and metal ceramic as a control group were used. A total of 9 groups (n=9) were formed. Before the cementation of the samples, marginal gap measurements were performed using a stereo microscope with a silicon replica technique. Samples were then aged with thermal cycling (5-55 oC,10000cycles). Wear tests were performed by using chewing simulator (50N,1Hz,240000cycles,lateral movement:2mm,mouth opening:2mm) with metal antagonists in distilled water solution. The samples were evaluated using a laser scanner and a software program capable of three-dimensional registration. Statistical analysis was performed using one-way analysis of variance (ANOVA) and Tukey HSD or Tamhane T2 test for multiple comparisons (α=0.05). Results: There was a significant difference between marginal gap measurements of the samples (p<0.001). In the measurements, the lowest marginal range value was found in BruxZir® (1.5mm) monolithic zirconia crowns (46±9μm) and the highest marginal range value was detected in Zenostar® (92±22μm). A significant difference was found between the wear measurements of the samples (p<0.05). In the measurements, the lowest wear value was seen in BruxZir® (0,8mm) monolithic zirconia crowns (0.96±0.81mm2) and the highest one was found in metal ceramic crowns (4.59±2.08mm2). Conclusions: Zirconia ceramics exhibited superior wear behaviors when compared to feldspar porcelain. The marginal gap measurements of metal supported and zirconia ceramics are within clinically acceptable limits.
Benzer Tezler
- Dental uygulamalar için çinko oksit katkılı lityum silikat cam-seramik blokların üretimi ve karakterizasyonu
Production and characterization of zinc oxide doped lithium silicate glass-ceramic blocks for dental applications
AYTAÇ ÇİDEM
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiManisa Celal Bayar ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. EMRE YALAMAÇ
DOÇ. DR. MÜCAHİT SÜTÇÜ
- Farklı yöntemlerle üst yapıları hazırlanan zirkonya destekli kron restorasyonlarının kırılma dayanımlarının araştırılması
Evaluation of the fracture strength of zirconia supported crown restorations veneered with different methods
BURCU KANAT
Doktora
Türkçe
2013
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MEHMET ALİ GÜNGÖR
- İmplant destekli sabit protezlerde CAM/CAM sistemleri ile üretilen destek ve üst yapı restorasyonlarının sonlu elemanlar stres analiz yöntemi ve kırılma direnci testi ile karşılaştırmalı olarak incelenmesi
The comparatively investigation of abutment and crown restorations produced by CAD/CAM systems in implant supported fixed prostheses using the finite element stress analysis method and fracture resistance test
NAZİRE ESRA BAĞDATLI
Doktora
Türkçe
2016
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. AHMET ERSAN ERSOY
- Bilgisayar ortamında ve manuel olarak dizayn edilmiş Zirkonya esaslı alt yapılar ile metal döküm alt yapıların marjinal uyumlarının karşılaştırılması
Comparison of the marginal congruity of the computer-aided and manually designed Zirconia-based frameworks with the cast metal frameworks
ÖZGE KARATAŞLI
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. PINAR KURSOĞLU
- Zirkonya kor ve üst yapı seramiklerin makaslama bağlanma dayanımlarının farklı test tasarımlarıyla değerlendirilmesi
Evaluating shear bond strength of zirconia cores and veneering porcelain with different test designs
EMİNE SELİN ERKAN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiÇukurova ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CEM KURTOĞLU