The Development of glass ceramics from central Anatolian basalts
Orta Anadolu basaltlarından cam seramiklerin oluşturulması
- Tez No: 35464
- Danışmanlar: DOÇ. DR. ABDULLAH ÖZTÜRK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Bazalt, Bazalt Cam, Bazalt Cam-Seramik Bilimsel Dalı Sayısal Koda : 604.01.03 vı, Cam endüstrisi, Seramik endüstrisi, Basalt, Basalt Glass, Basalt Glass-Ceramic, Glass industry, Ceramic industry
- Yıl: 1994
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
öz ORTA ANADOLU BAZALTLARINDAN CAM-SERAMİKLERİN OLUŞTURULMASI C AVC AR, Melike Mihran Yüksek Lisans Tezi, Metalürji Mühendisliği Ana Bilim Dalı Tez Yöneticisi Asst Prof. Dr. Abdullah ÖZTÜRK Temmuz, 1994, 107 sayfa. Orta Anadolu bazalt kayalarından cam-seramik malzemeler oluşturulabilirliği araştırılmıştır. Bazalt 1350°C'de eritildi ve ardından cam oluşturması için laboratuvar koşulları altında oda sıcaklığına soğutulmuştur. Cam numuneler, çekirdeklenme için 700°C'de 1/2 ile 4 saate kadar ve kristal büyümesi için de 850°C ile 1000°C sıcaklıkları arasında 1/2 ile 2 saate kadar farklı ısıl işlem programlarına tabi tutulmuştur. Basalt ramının kristallenme davranışı DTA ve dilatometre kullanılarak çalışılmıştır. Kristal fazlar ve mikroyapısal değişimler X- ışınlan difraksiyon analizi, optik ve tarama elektron mikroskopları kullanarak araştırılmıştır. Isıl işlem sonucunda oluşturulan cam-seramik klinopiroksen kristalleri ile birlikte kanoif, periklas, Tschermak molekülü içermektedir. Isıl işlem pmgramiTmı oluşan fazlan etkilemediği fakat bu fazların oluşum şekillerini etkilediği bulunmuştur. Bazalt cam ve cam-seramik malzemelerin özelliklerindeki değişimleri görebilmek için yoğunluk, mikrosertlik ve kimyasal dayanım çalışmaları yapılmıştır.
Özet (Çeviri)
ABSTRACT THE DEVELOPMENT OF GLASS-CERAMICS FROM CENTRAL ANATOLIAN BASALTS CAVCAR, Melike Mfhran MS. in Metallurgical Engineering Supervisor: AssL Prof. Dr. Abdullah ÖZTÛRK Jury, 1994, 107 pages Ability of formation a glass-ceramic material from the Central Anatolian basalt rode is investigated. Basalt was melted at 1350°C and subsequently cooled to room temperature at the laboratory conditions to form glass. Glass samples were heat treated for nucleation at 700°C for 1/2 to 4 hours and for the growth of crystals at the temperature range of 850°C-1000°C for 1/2 to 2 hours. Crystallization behaviour of basalt glass was studied using DTA and a dilatometer. Crystalline phases and microstructural changes were studied using X-ray diffraction analysis, optic and scanning electron microscopies. Glass-ceramic obtained after heat treatment contains clinopyroxene crystals with kanoite, periclase, Tschermak's molecule. Heat treatment schedule did not affect the phases present but, affected the type of occurrence of these phases. Density, microhardness and chemical durability studies were done to see the changes in the properties of the basalt glass and glass-ceramic materials. in
Benzer Tezler
- Türkiye'deki yat inşa sanayii ve uluslararası rekabet gücü
Yacht building industry in Turkey and its competitiveness
AHMET ERKAN GÖKGÖZ
Yüksek Lisans
Türkçe
1995
İşletmeİstanbul Teknik Üniversitesiİşletme Ana Bilim Dalı
DOÇ. DR. LERZAN ÖZKALE
PROF. DR. YÜCEL CANDEMİR
- AT ile gümrük birliğine giderken Türk çimento, seramik ve cam sanayi
Turkish cement ceramic and glass. Industries towards the EC-Turkey castoms union
GÜRDAL KAYA
Yüksek Lisans
Türkçe
1995
İşletmeİstanbul Teknik Üniversitesiİşletme Ana Bilim Dalı
DOÇ. DR. HACER ANSAL
- Li2O - ZnO - Al2O3 camlarının kontrollü kristalizasyonu ve cam seramiklerin karakterizasyonu
The Controlled crystallization of Li2O - ZnO - Al2O3 - SiO2 glasses and the characterization of glass ceramics
ENGİN MAYTALMAN
Yüksek Lisans
Türkçe
1999
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERDEM DEMİRKESEN
- Alümina ilavesinin Li2O-ZnOSi2 cam ve cam seramiklerinin kristalizasyon davranışı, mekaniksel ve kimyasal özellikleri üzerine etkisi
Başlık çevirisi yok
ELVAN BİLGE ÇUKUR
- Yüksek titanyum içerikli albit cevherlerinin değerlendirilmesi
The Evaluation of high titanium content feldspar ories
MURAT OLGAÇ KANGAL
Yüksek Lisans
Türkçe
1998
Maden Mühendisliği ve Madencilikİstanbul Teknik ÜniversitesiCevher-Kömür Hazırlama ve Değerlendirme Ana Bilim Dalı
DOÇ. DR. ALİ GÜNEY