Activity-composition relations in MnCr2O4 solid solutions and stabilities of MnCr2O4 and CoCr2O4
MnCr2O4-CoCr2O4 katı çözeltilerinde aktivite-kompozisyon ilişkileri, MnCr2O4 ve CoCr2O4'ten kararlılıkları
- Tez No: 29256
- Danışmanlar: PROF. DR. MUHARREM TİMUÇİN
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Termodinamik, Kati Çözeltiler, Mangan, Kobalt, Kromit, Manganez, Çözeltiler, Thermodynamics, Solid Solutions, Manganese, Cobalt, Chromites, Chromite, Solutions
- Yıl: 1993
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
MnO-CoO-Cr2C>3 sistemindeki oksit ve spinel eriyiklerinde CoO aktiviteler 1300 °C de spinel fazlarının termodinamik özellikleri hakkında bilgi üretmek amacıyla ölçüldü. Sistemdeki faz bölgelerinden seçilen sentetik numuneler, 1 atmosferdeki oksijen kısmi basıncı bilinen gaz fazı ile dengeye getirildi. Aynı zamanda MnO-CoO çiftli sisteminde kobalt oksit aktiviteleri emf metodu ile ölçüldü. Kobalt oksit aktiviteleri ile ilgili bilgiler, oksit ve spinel eriyikleri arasındaki denk faz bağ çizgilerinin yönleri, 1300 °C'de spinel katı çözeltisindeki aktivite-kompozisyon ilişkilerinin belirlenmesinde kullanıldı. MnCr204-CoCr204 katı çözeltileri bu sıcaklıkta pozitif sapma gösterir. CoCr204 'tin standard serbest oluşum enerjisi -37636 J/mol olarak ölçüldü ve MnCr204 tınki -42278 J/mol olarak hesaplandı. Stokiometrik spinel kati çözeltilerinden elde edilen aktiviteler katyon dağılım modellerinden belirlenenlerlekarşılaştırıldı. CoCr204 ve MhO^Cty taki katyon dağılımı x-ışınları difraksiyon metodları ile hesaplandı.
Özet (Çeviri)
Activities of CoO were measured in the oxide and spinel solutions of the system MnO-CoO-Cr203 at 1300 °C with the aim of deriving information on the thermodynamic properties of spinel phases. Synthetic samples in selected phase assemblages of the system were equilibrated with a gas phase of known oxygen partial pressures at a total pressure of one atm. Activities of cobalt oxide along the MnO-CoO binary were also measured by emf the method. The data on CoO activities and the directions of conjugation lines between coexisting oxide and spinel phases were used to establish the activity- composition relations in spinel solid solutions at 1300 °C. The MnCr204 - CoCr204 solid solutions exhibit positive deviation from ideality at this temperature. The standard free energy of formation of CoCr204 from its components (CoO + Cr203) at 1300 °C was measured as -37,636 J/mole, and that illof MnCr204 was calculated as -42,278 J/mole. The activities determined in the stoichiometric spinel solid solutions were compared with those predicted from cation distribution models. The cation distribution in CoCr204 and MnCr204 were calculated by x-ray diffraction methods.
Benzer Tezler
- Phase equilibria and thermodynamic studies in the system iron-nicked-oxygene at 1300 C
Fe-Ni-O sisteminin 1300'C'deki denge fazları ve termodinamik özellikler
İBRAHİM ÇAM
Doktora
İngilizce
1996
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. MUAMMER TİMUÇİN
- Görsel anlatımda zıtlık ve denge
In Visual expressing contrast and balance
LEYLA ŞENTÜRK VARLIK
Sanatta Yeterlik
Türkçe
1999
Güzel SanatlarAnadolu ÜniversitesiResim Ana Sanat Dalı
PROF. ABDULLAH DEMİR
- Türkiye'de mimarlık bürolarında tasarlamada karar verme durumunun belirlenmesi
Exploration of design decision making situation in architectural offices in Turkey
NUR ESİN
- Enformal sektör enformal istihdam ve enformal ekonomi
Başlık çevirisi yok
YASEMİN GÜNGÖR (YÜCESOY)
Yüksek Lisans
Türkçe
1993
Çalışma Ekonomisi ve Endüstri İlişkileriAnkara ÜniversitesiDOÇ.DR. MURAT ŞEKER
- Mimarlıkta söylemin temsili belirlemesi ve iki yirminci yüzyıl örneği: Pürizm ve neo-plastizm
Başlık çevirisi yok
KAMİL GÜRER