Yaşlandırma sonrası yüzey işlemlerinin, zirkonyum oksit seramiklerin bağlantı direnci ve sızıntı üzerine etkisi
The effect of surface treatments on bond stength and leakage of zirconium oxide ceramics after aging
- Tez No: 288914
- Danışmanlar: YRD. DOÇ. MUSTAFA ZORTUK
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Zirkonya, yüzey işlemi, Nd:YAG lazer, Dental porselen, Dental stres analizi, Dental sızma, Lazerler, Neodmiyum YAG lazer, Yüzey oluşturma, Zirkonyum oksit, Zirconia, surface conditioning, Nd:YAG laser, Dental porcelain, Dental stress analysis, Dental leakage, Lasers, Neodmiyum YAG laser, Surface construction, Zirconium oxide
- Yıl: 2011
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Zirkonya esaslı tam seramiklerde geleneksel yöntemlerle yapılan yüzey işlemleri ile ilgili çok sayıda çalışma olmasına rağmen, bu yöntemlerin Nd-YAG lazer pürüzlendirilmesiyle karşılaştırarak sızıntının değerlendirilmesi henüz değerlendirilmemiş bir konudur. Bu çalışmanın amacı farklı yüzey işlemleri uygulanmış zirkonya seramiğe rezin siman bağlantısının ve sızıntının değerlendirilmesidir.Final boyutu 10 x 10 x 2mm olan toplam 84 adet zirkonya sermik örnek ZirkonZahn(Steger, İtalya) bloklardan elde edilmiştir. Farklı yüzey hazırlıklarına tabi tutulmak üzere rastgele 14'erli 6 gruba ayrılan örneklerden 1.grup yüzey işlemi uygulanmadan kontrol grubu(Grup1) olarak ayrıldı. Kumlama Grubundaki örnekler 110 ? olan Al2O3 kumu ile pürüzlendirildi. Rocatec Grubundaki örnekler 110 ? olan Al2O3 kumu ile pürüzlendirildikten sonra silika kaplandı ve silan (ESPE-SIL) uygulandı. Lazer1 Grubundaki örnekler, Nd-YAG lazer cihazı (Fidelis Plus 3 Fotona (Ljublgana, Slovenya)) kullanılarak pürüzlendirildiler. Cihazın paneli 20 Hz, 100mJ, 2W, 100µs olacak şekilde ayarlandı. Lazer2 Grubundaki örneklerde cihaz; 20 Hz, 150mJ 3W 100µs olarak ayarlandı. Primer Grubundaki örneklere ise çift kat Zirconia Primer (Z-Prime Plus Bisco, IL, A.B.D.) uygulandı. Hava ile 10 sn kibarca kurutuldu 20 sn 800 mW / cm2 ışıkla polimerize edildi. Yüzey işlemi uygulanan her gruptan 2 örnek, sızıntı testine tabi tutulmak için ayrıldı.Yüksekliği 3mm ve çapı 3.6mm olan siman bloklar Panavia F 2.0 (Kuraray Medical Inc., Japonya) rezin simandan üretildi ve örneklere simante edildi. Örnekler 2 hafta oda sıcaklığındaki suda bekletildikten sonra termal döngü cihazında, 5-55 ºC'de, her derecede bekleme süresi 30 saniye ve bir banyodan diğerine geçiş 2sn olacak şekilde 6000 döngü uygulandı. Örnekler yarıçapı ve yüksekliği 1cm olan akrilik bloklara yerleştirilerek makaslama testine tabi tutuldular. Buna göre en yüksek değerler Rocatec Grubunda bulunmuş, bunu Lazer2 grubu takip etmiştir. En düşük değer ise kontrol grubunda bulunmuştur. Örnekler SEM ve AFM de incelenmiş, profilometre cihazında pürüzlülük değerleri ölçülmüştür.Sızıntı testine tabi tutulmuş örneklerde marjinlerde ince bir çizgi şeklinde sızıntı izlenmiş ancak gruplar arasında fark gözlenmemiştir.
Özet (Çeviri)
The aim of this study was to compare the effects of airborne-particle abrasion, tribochemical silica coating, Nd:YAG laser treatment and a primer coupling agent surface treatment methods on the bond strength of zirconium-oxide ceramic to a resin luting agent.Eigtyfour square-shaped (10 x 10 x 2mm) zirconium-oxide ceramic ZirkonZahn(Steger, İtaly) specimens and resin cement (Panavia F 2.0 -Kuraray Medical Inc., Japan) cylinders (diameter of 3.6 mm and height of 5 mm.) were prepared.The speciments divided into 6 groups (n=14) that were subsequently treated as follows: Group 1, no treatment (control); Group Air Abrasion, the ceramic surfaces were airborne-particle abraded with 110? aluminum-oxide (Al2O3) particles; Group Rocatec, after abrasion of the surfaces with 110? aluminum-oxide (Al2O3) particles, silica coating using 30? (Al2O3) particles modified by silica (Rocatec System) and application of the silane coupling agent (ESPE-SIL); Group Laser1, ceramic surfaces irritated with Nd:YAG laser(Fidelis Plus 3 Fotona (Ljublgana, Slovenia) at 20 Hz, 100mJ, 2W, 100µs; Group laser2, ceramic surfaces irritated with Nd:YAG laser at Fidelis Plus 3 Fotona (Ljublgana, Slovenia) at 20 Hz, 100mJ, 2W, 100µs; Group Primer,); application of a Zirconia Primer (Z-Prime Plus Bisco, IL,USA) agent.The resin cement cylinders were bonded to the treated ceramic surfaces. After the specimens were stored in distilled water at 37ºC for 2 weeks, groups were subjected to thermocycling for 6.000 cycles between 5 and 55 ºC in water. Their shear bonding strength was tested using a universal testing machine at a crosshead speed of 1mm/min. Debonded specimen surfaces were observed by SEM and AFM. Bond strength data were analyzed using 1-way analysis of variance and the Duncan test, (a=.05),the means of each group were analysed by one-way analysis of variance (ANOVA).The bond strength was significantly higher in Rocatec and Laser2 respectively. Lowest bond strength value was encountered in control group. For marginal leakage, score 0 was found in all groups and no statistical difference was found between the groups.
Benzer Tezler
- Tek katmanlı ve çok katmanlı monolitik zirkonya seramiklerin renk stabilitelerinin ve translusensi özelliklerinin değerlendirilmesi
Evaluation of color stabilities and translucency properties of monolayer and multilayer monolithic zirconia ceramics
EDA DÖĞÜŞCÜ
Doktora
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜL KARACAER
- Presinterize zirkonyum oksit (ZRO2) alt yapı seramiklerinin yüzey pürüzlülüğüne ve rezin simanla olan bağlantısına yüzey işlemlerinin etkileri
The effects of surface treatments on surface roughness and on bond strength of zirconium oxide substructure to resin cement
AMRO VARRAK
Doktora
Türkçe
2021
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÖZLEM CEYLAN
- Farklı yüzey işlemlerinin zirkonya ile rezin siman arasındaki bağlantı kuvveti üzerine etkisi
The effect of different surface treatments on the bond strength between zirconia and resin luting cement
GÖKHAN ÇİÇEKCİ
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiAnkara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. LALE KARAAĞAÇLIOĞLU
- CAD/CAM sistemleriyle üretilmiş iki yarı saydam, monolitik zirkonya restorasyonun klinik uyumlama prosedürlerinin materyalin optik ve mekanik özelliklerine etkilerinin değerlendirilmesi
Evaluation of the effects of clinical adaptationprocedures of two translucent, monolithic zirconium restoration manufacturedwith the use of CAD/CAM systems on the optical and mechanical properties of thematerial
CANSU TOR
Doktora
Türkçe
2022
Diş HekimliğiBiruni ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SAİP DENİZOĞLU
DR. ÖĞR. ÜYESİ EMİN ORKUN OLCAY
- Dental zirkonyanın düşük ısı bozunmasının silika kaplama ve tekrarlanan fırınlama yöntemleriyle engellenmesi; yöntemlerin dayanıklılık ve renge etkileri
Effects of silica coating and repeated firing on treatment of low temperature degradation; flexural strength and color changes of dental zirconia ceramic
TUTKU BURCU ÇAKIR
Doktora
Türkçe
2017
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. RİFAT GÖZNELİ