Dental zirkonyanın düşük ısı bozunmasının silika kaplama ve tekrarlanan fırınlama yöntemleriyle engellenmesi; yöntemlerin dayanıklılık ve renge etkileri
Effects of silica coating and repeated firing on treatment of low temperature degradation; flexural strength and color changes of dental zirconia ceramic
- Tez No: 461109
- Danışmanlar: DOÇ. DR. RİFAT GÖZNELİ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental porselen, Dental stres analizi, Diş renk değişikliği, Fırınlama, Zirkonyum, Zirkonyum oksit, Dental materials, Dental porcelain, Dental stress analysis, Tooth discoloration, Firing, Zirconium, Zirconium oxide
- Yıl: 2017
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı zirkonyanın fiziksel buhar biriktirme (PVD) yöntemi ile silika kaplanması ve tekrarlanan fırınlamalar uygulanması ile düşük ısı bozulmasının engellenmesi ve yüzey uygulamaların zirkonyanın dayanıklılığına ve rengine etkilerinin incelenmesi amaçlanmıştır. Gereç ve yöntem: Disk şeklinde hazırlanmış 100 adet örnek 10 deney grubuna ayrılmıştır: K: kontrol; Y: yaşlandırma; A: aşındırma-yaşlandırma; SA: sulu aşındırma-yaşlandırma; S: silika kaplama-yaşlandırma; AS: aşındırma-silika kaplama-yaşlandırma; 3F: 3 kez fırınlama-yaşlandırma; A3F: aşındırma-3 kez fırınlama-yaşlandırma; 5F:5 kez fırınlama-yaşlandırma; A5F: aşındırma-5 kez fırınlama-yaşlandırma. Yaşlandırma işlemi buhar otoklavında gerçekleştirilmiştir. Tüm gruplarda yüzey ve yaşlanma işlemlerini takiben meydana gelen monoklinik faz içeriğini tespit etmek için X-ray difraksiyon analizi yapılmıştır. Spektrofotometre cihazı kullanılarak deney gruplarının renk ölçümleri gerçekleştirilmiştir. Örneklerin bükme dayanımları biaksiyal bükme testi kullanılarak ölçülmüştür. İstatistiksel analiz, bükme dayanım değerleri için One-way ANOVA ve LSD testi, renk verileri için ise Kruskal Wallis ve Dunn's Çoklu Karşılaştırma testleri kullanılarak yapılmıştır (p<0.05). Bulgular: Silika kaplama işlemi, aşındırılmış örneklerde faz transformasyonunu azaltmıştır. Yaşlandırma sonrası en düşük monoklinik faz A3F ve A5F gruplarında görülmüştür. Aşındırma işlemi örneklerin bükülme dayanımını anlamlı olarak artırmıştır. En yüksek ∆E değerleri, yaşlandırma öncesi K-S, yaşlandırma sonrası K-5F ve aşındırma-yaşlandırma sonrası K-3F grupları arasında görülmüştür. Sonuç: Silika kaplama ve fırınlama uygulamaları sadece aşındırılmış örneklerdeki monoklinik fazı azaltmıştır. Aşındırma işlemi zirkonyanın düşük ısılarda bozunmasına olan yatkınlığını azaltıp, bükme dayanımını artırmıştır. Tekrarlayan fırınlama ve silika kaplama işlemleri örnekler üzerinde gözle görülür renk değişikliğine neden olmuştur (∆E>2).
Özet (Çeviri)
Purpose: The aim of this study was to examine the application of physical vapor deposition silica coating and multiple firing as an approach to retard low temperature degradation (LTD) and the color and flexural strength of the zirconia specimens after surface treatments. Materials and methods: 100 disc-shaped specimens were divided into 10 groups: K: control; Y: aging; A: grinding without water cooling-aging; SA: grinding with water cooling-aging; S: silica coating-aging; AS: grinding-silica coating-aging; 3F: 3 times firing-aging; A3F: grinding-3 times firing-aging; 5F:5 times firing-aging; A5F: grinding-5 times firing-aging. Aging was simulated by steam autoclave. X-ray diffraction analysis was used to estimate the amount of monoclinic phases of the groups. Color measurements of tested groups were performed with a spectrophotometer. Biaxial flexure test was used to calculate the flexural strength. Statistical analysis was conducted with One-way ANOVA and LSD test for stregth values and Kruskal Wallis and Dunn's Multiple tests for color datas (p<0.05). Results: Silica coating decreased phase transformation on ground samples. A3F and A5F groups exhibited the lowest monoclinic content. Grinding significantly increased the biaxial flexural strength values. Before aging, between groups K and S; after aging between groups K and 5F and after grinding-aging between groups K and 3F, highest color changes were seen. Conclusion: Both silica coating and repeated firing decreased the monoclinic content only in ground specimens. Grinding decreased the susceptibility of zirconia to LTD and increased the flexural strength. Silica coating and multiple firing made the visualy imperviable color changes (∆E>2).
Benzer Tezler
- Farklı monolitik zirkonya polikristalin materyalinin düşük ısı bozunmasının yüzey sertliğine ve eğilme dayanımına etkisi
The effect of low thermal degradation of different monolithic zirconia polycrystalline materials on surface hardness and flexural strength
TURAN SERVİ
Doktora
Türkçe
2024
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. İSA YÖNDEM
- Üç farklı yttria stabilize zirkonya polikristalinin düşük ısı bozunması ve bozunmanın materyalin eğilme dayanımına etkisi
Low thermal degradation of three yttria-stabilized tetragonal zirconia polycrystalline and effect of low thermal degradation on flexural strenght
ESRA TALAY ÇEVLİK
Doktora
Türkçe
2015
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. İSA YÖNDEM
- Yüzey uygulamaları ve yapay yaşlandırma işleminin Y-TZP dental seramiklerinin biaksiyel bükme dayanımı ve faz değişimi üzerine etkilerinin in-vitro olarak incelenmesi
Influence of surface treatments and accelerated aging on flexural strength and phase transformation of bilayered Y-TZP ceramics
EVRİM ÖZER BULTAN
Doktora
Türkçe
2013
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. DENİZ ŞEN
- Geçiş metali katkılı atık zirkonya esaslı toz karışımlarından sinter seramik malzemelerin geliştirilmesi ve karakterizasyonu
Development and characterization of sintered ceramic materials from waste zirconia based powder mixtures with transition metal additives
HATİCE TURGUT
Yüksek Lisans
Türkçe
2016
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA LÜTFİ ÖVEÇOĞLU
- Farklı yüzey parlatma sistemlerinin çeşitli monolitik zirkonyum materyallerinin yüzey özellikleri ve faz değişimleri üzerindeki etkisinin incelenmesi
The effect of different surface polishing systems on surface properties and phase changes of various monolithic zirconium materials
HARUN REŞİT BAL
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. NURAN YANIKOĞLU