A Metallographic study of centrifugally cast naphtha cracking tubes
Savurma döküm tekniği ile üretilmiş nafla parçalama tüpleri üzerine metalografik bir çalışma
- Tez No: 23291
- Danışmanlar: PROF. DR. ERDOĞAN TEKİN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Mikroyapı, X-ışını Kırınımı, Sertlik Deneyi, Çekme Deneyi, Darbe Deneyi, Faz Dönüşümü, Darbe dayanımı, Faz dönüşümleri, Metalografi, Nafta parçalama tüpleri, Sertlik, X ışını kırınımı yöntemi, Çekme dayanım testi, Microstructure, X-Ray Diffraction, Hardness Test, Tension Test, Impact Test, Phase Transformation, Impact strength, Phase transformations, Metallography, Naphta cracking tubes, Hardness, X ray diffraction method, Tensile strength test
- Yıl: 1992
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET SAVURMA DÖKÜM TEKNÎ?Î ÎLE ÜRETÎLMÎŞ, NAFTA PARÇALAMA TÜPLERİ ÜZERÎNE METALOGRAFÎK BÎR ÇALIŞMA DO?AN, Ümran Bülent Yüksek Lisans Tezi, Metalürji Mühendisliği Bölümü Tez Yöneticisi: Prof.Dr. Erdoğan TEKÎN Mayıs 1992,92 Sayfa Bu tezde, PETKÎM' de kullanılmakta olan, savurma döküm tekniği ile üretilmiş, yüksek sıcaklığa dayanıklı tüplerden numuneler alınmış ve üzerlerinde metalografik bir çalışma yapılmıştır. Optik metalografi ve SEM teknikleri kullanılarak, ısıl işlem görmüş ve görmemiş Alloy 800 tüp numunelerinin ve serviste kullanılmış HK 40 tüp numunesinin mikroyapıları açıklanmış, bu numunelerde bulunan fazlar ve elektrolitik karbür çıkarımı yöntemi ile elde edilen çökeltiler SEM- EDX ve X- ışını kırınım analizi ile belirlenmiştir. Tüm numunelerin sertlikleri ölçülmüş, çekme ve darbe deneyleri sadece ısıl işlem görmemiş Alloy 800 ve serviste kullanılmış HK 40 tüp numunelerineuygulanmıştı r.Cr7C3 ?> Cr23c6 faz dönüşümü tartışılmış ve mikroyapı-mekanik özellik ilişkisi açıklanmıştır.
Özet (Çeviri)
ABSTRACT A METALLOGRAPHIC STUDY OF CENTRIFUGALLY CAST NAPHTHA CRACKING TUBES DO?AN, Ümran Bülent M.S. in Metallurgical Engineering Supervisor: Prof.Dr. Erdoğan TEKÎN May 1992,92 pages A metal lographic study was performed on the samples which were taken from the centrifugally cast pyrolysis tubes used in PETKÎM. The microstructures of the as cast and of the heat treated tube specimens which have Alloy BOO alloy composition; and of the used tube sample that has HK 40 alloy composition; were examined by optical metallography and by SEM, and the phases present were analysed by EDX which is attached to SEM. X-ray diffraction analysis of the powders, extracted electrolytically from the related samples, were carried out. Hardness test was applied to all the specimens, while tension and impact tests wereapplied to the as cast and to the used tube specimens. The phase transformation of Cr-jC^ to Cr23C6 is discussed and microstructure - mechanical property (hardness) relation is expained.
Benzer Tezler
- Yaşlandırma ile sertleştirilebilen magnezyum-alüminyum alaşımlarının özelliklerinin geliştirilmesi
The Development of magnesium-aluminium alloys age hardened
HANIM DOĞAN
- A Metallographic study of carbides in chromium modified hadfield steels
Başlık çevirisi yok
NEDİM EŞLİSOY
- Sabit devirli bir numune yüzey zımparalama cihazının tasarımı ve imalatı
The Design and production of a prototip surface grinding machine with stationary rotation
AHMET KÜÇÜK
Yüksek Lisans
Türkçe
1999
Eğitim ve ÖğretimSakarya ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ. DR. FEHİM FINDIK
- Çelikte metalik olmayan kalıntıların oluşumu, etkileri ve mikroskopik yöntemlerle değerlendirilmesi
Formation of non-metallic inclusions in steels, their effects and evaluation with microscopical methods
FUAT ÖZEK