Cu-%25 Mn-%11 Al alaşımının mekaniksel ve elektriksel özellikleri üzerine ısıl işlem etkilerinin incelenmesi
Investigation of mechanical and electrical properties of Cu-%25 Mn-%11 Al alloy on heat treatment
- Tez No: 184279
- Danışmanlar: PROF.DR. TAHSİN NURİ DURLU
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Çökelme sertleşmesi, zor-zorlanma, akma dayanımı, elektriksel direnç, taramalı elektron mikroskobuii, Precipitation hardening, stress-strain, yield strength, electricalresistivity, scanning electron microscopy.iv
- Yıl: 2006
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZETCu-%25Mn-%11Al ALAŞIMININ MEKAN KSEL VE ELEKTR KSELÖZELL KLER ÜZER NE ISIL ŞLEM ETK LER N N NCELENMESYILDIZ, Yasin GöktürkKırıkkale ÜniversitesiFen Bilimleri EnstitüsüFizik Anabilim Dalı, Yüksek Lisans TeziDanışman: Prof. Dr. Tahsin Nuri DURLUŞubat 2006, 46 sayfaBu çalışmada, Cu-%25Mn-%11Al alaşımında oluşan austenite fazıiçerisindeki çökelti fazları Taramalı Elektron Mikroskobu (SEM) ile, bu çökeltifazlarının kütle oranları Enerji Dağılımlı X-Işınları Spektroskobisi (EDS)sistemi ile belirlenmiştir. Ayrıca alaşımın mekanik dayanımının belirlenmesiiçin zor-zorlanma, elektriksel özelliklerinin incelenmesi için elektriksel ölçümteknikleri kullanılmıştır. Elektron mikroskop incelemeleri sonunda Cu-%25Mn-%11Al alaşımında austenite tane yapısı ve çökelme sertleşmesi görülmüştür.Gözlenen bu fazların alaşıma uygulanan ısıl işleme ve soğutma hızına bağlıolduğu görülmüştür.Çökelme fazı gözlenen numune ile austenite fazı gözlenen numunekarşılaştırıldığında mekaniksel ve fiziksel olarak farklılıklar görüldü.iBu farklılıklara bakıldığında; içinde çökelme fazı gözlenen numuneninakma dayanımının, saf austenite faz yapısına sahip numunenin akmadayanımından %23.5 kadar daha yüksek olduğu görülmüştür. Bu iseçökelme sertleşmesinin austenite tane yapısına göre, alaşıma %23.5oranında bir sertlik kazandırdığını göstermiştir. Bunun yanında elektrikseldirence bakıldığında; çökelme fazı, austenite faza göre alaşıma %30 kadarelektriksel direnç kazandırmıştır.
Özet (Çeviri)
ABSTRACTINVESTIGATION OF MECHANICAL AND ELECTRICAL PROPERTIES OFCu-%25Mn-%11Al ALLOY ON HEAT TREATMENTYILDIZ, Yasin GöktürkKırıkkale UniversityGraduate School of Natural and Applied SciencesDepartment of Physics, M. Sc. ThesisSupervisor: Prof. Dr. Tahsin Nuri DURLUFebruary 2006, 46 PagesIn this work, precipitation phases in an austenite phase in Cu-%25Mn-%11Al alloy were investigated by means of Scanning Electron Microscope(SEM) and mass ratios of these precipitate phases were determined byEnergy Dispersion X- Ray Spectroscopy (EDS). In addition, in order todetermine the mechanical strength of the alloy and its electrical properties,stress-strain and electrical measurement techniques were performedrespectively. The results of SEM measurements revealed that there are theaustenite grain structure and the precipitation hardening in Cu-%25Mn-%11Al alloy. It was also observed that the properties of these phasesdepend on the heat treatment and the cooling rate.iiiA comparision of the sample with the precipitation phase and austenitephase showed that there are differences in their mechanical and physicalproperties.During consideration of obtained different results, it was observed thatthe yield strength of the sample which contains precipitation was %23.5higher than the yield strength of the sample that was in pure austenite phase.Therefore, precipitation hardening has %23.5 higher contribution to theoverall alloy hardening. Furthermore precipitation phase contribute theoverall electrical resistivity %30 higher than the austenite phase.
Benzer Tezler
- Paslanmaz çeliklerin Türkiye'de tercihli uygulama alanlarına göre optimum kullanım önerilerinin hazırlanması
The Optimum suggestions for using of stainless steels according to application fields in Turkey
ÜMİT ALDEMİR
Yüksek Lisans
Türkçe
2000
Makine MühendisliğiUludağ ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. HALİM DEMİRCİ
- Konya ili çevre yollarında yetişen bazı doğal bitkilerde ağır metal birikiminin araştırılması
The investigation of heavy metals accumulation on some nature plants in Konya highways
AHMET SAİD KURCA
Yüksek Lisans
Türkçe
2005
BiyolojiSelçuk ÜniversitesiBiyoloji Ana Bilim Dalı
Y.DOÇ.DR. MURAD AYDIN ŞANDA
- Susam, susam yağı ve tahinde fiziksel kimyasal analizler ve yağ asitleri bileşiminin belirlenmesi
Başlık çevirisi yok
MUSA ÖZCAN
Yüksek Lisans
Türkçe
1993
Gıda MühendisliğiSelçuk ÜniversitesiGıda Bilimi ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. ATİLLA AKGÜL
- Manganez bronzlarında ısıl işlemle sertleşme mekanizması ve faz dönüşümleri
The Phase transformation and hardening mechanism by heat treatment of cast manganese bronzes
ABDULLAH OTUZBİR
- Karbotermik ferrobor üretim parametrelerinin optimizasyonu
The optimization of parameters for the carbothermic production of ferroboron
ONURALP YÜCEL