Sulfonated styrene-co-maleic acid and its derivatives as superplasticizers in concrete
Betonda süperakışkanlaştırıcı olarak sülfonlanmış stiren-co-maleik asit ve türevlerinin kullanımı
- Tez No: 177299
- Danışmanlar: PROF. DR. LEYLA ARAS
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Süperakıskanlastırıcılar, Polikarboksilikler, Poli(4-stirensülfonik asit-co-maleik asit)sodyum tuzu, Yayılma, Zeta Potansiyel, Polimer beton, Superplasticizers, Polycarboxylates, Poly(4-styrenesulfonic acidco-maleic acid)sodium salt, Fluidity, Zeta Potential, Polymer concrete
- Yıl: 2008
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Bölümü
- Bilim Dalı: Kimya Ana Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Geçen 30 yılda, süperakıskanlastırıcı adı verilen, yeni bir grup olan katkımaddeleri beton endüstrisine sunuldu. Birçok avantajları olması nedeniyleyaygın kabul gördü. Betona süperakıskanlastırıcıların katkısı betonunislenebilirligini ve mukavemetini arttırır. Bu çalısmada, yeni birsüperakıskanlastırıcı olan sülfonik ve karboksilik asit grupları içeren poli(4-stirensülfonik asit-maleik asit)sodyum tuzunun kimyasal yapısının etkisianaliz edildi. Bu suda çözünebilen kopolimere farklı agırlıkkompozisyonlarında, iki farklı moleküler agırlıkta olan PEG (polietilen glikolmonometil eter) asılandı. Sentezlenen kopolimerlerin yapıları FTIR ve NMRanalizleri ile dogrulandı. Farklı yan zincir uzunlukları olan asılanmıskopolimerlerin molekül agırlık farklılıgı seyreltik solüsyon viskositesi ilesaptandı. Asılanmıs kopolimerlerin kimyasal yapısının çimento pastasınınakıskanlıgına etkileri ve betonun mekanik özellikleri arastırıldı. Zetapotansiyel ölçümleri çimento parçacıkları ile polikarboksilik tipsüperakıskanlastırıcıların etkilesimlerini açıga çıkardı. Maksimum yayılma,3:3 agırlık oranında PEG asılanmıs kopolimer için saglandı. Bu kopolimerinmekanik özellikleri diger kopolimerlere göre en yüksek bükülme ve basınçmukavemeti gösterdi.Çesitli Li tuzlarının SSAMA ya katkısı iyonik ortamı etkiledi ve böyleceçimento pastasının yayılma performansı ve betonun mekanik özelliklerigelisti. 1:1 mol oranında LiCl: SSAMA karısımı diger Li tuzlarına vekompozisyonlarına göre maksimum yayılma gösterdi. Bu karısım en yüksekbükülme mukavemeti verdi fakat Li2CO3 ın 1:1 kompozisyonu diger tuzkarısımları içinde en yüksek basınç mukavemeti verdi.
Özet (Çeviri)
In the past three decades, a new group of concrete admixtures, termed?superplasticizers?, were introduced to the concrete industry. They havegained wide acceptance because of their many advantages. The addition ofsuperplasticizers to concrete improves the workability and strength ofconcrete. In this study, the effect of the chemical structure of poly (4-styrenesulfonic acid-co-maleic acid) sodium salt (SSAMA), which containsboth sulfonic and carboxylic acid groups, which is a new superplasticizer,was analyzed. Two different molecular weights of PEG (polyethylene glycolmonomethyl ether) were grafted to this water-soluble copolymer at differentweight compositions. The structures of synthesized copolymers were verifiedby FTIR and NMR analyses. The molecular weight difference of the graftedcopolymers with different side chain lengths was determined by dilutesolution viscosimetry. The effects of chemical structure of grafted copolymerson the fluidity of cement paste and the mechanical properties of the mortarswere investigated. The zeta potential measurements revealed theinteractions between the cement particles and polycarboxylate typesuperplasticizers.The maximum fluidity was achieved for the PEG grafted copolymer with theweight ratio 3:3. The mechanical properties of this copolymer showed thehighest flexural and compressive strength compared to other copolymers.The addition of various Li salts to SSAMA affected the ionic medium,therefore, the dispersion performance of cement paste and the mechanicalproperties of the mortars improved. The mixture of LiCl: SSAMA in 1:1 molratio exhibited the maximum fluidity compared to other Li salts and theircompositions. This mixture gave the highest flexural strength but the mixtureof Li2CO3 in 1:1 composition gave the highest compressive strength in eachsalt mixtures.
Benzer Tezler
- Miscibility studies on methylmetacrylate co-methacrylic acıd with ionomers of styrene co-sulfonated styrene
Metilmetakrilat-metakrilik asit kopolimeri ile sülfonlaşmış polistiren iyonomerlerinin karışabilirlik çalışması
NEBEHAT YURTSEVEN
Yüksek Lisans
İngilizce
1993
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. LEYLA ARAS
- Kinetic studies for the production of tertiary ethers used as gasoline additives
Benzin katkı maddesi olarak kullanılan tersiyer eterlerin üretimi üzerine kinetik çalışmalar
NEZAHAT BOZ
Doktora
İngilizce
2004
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. TİMUR DOĞU
PROF. DR. GÜLŞEN DOĞU
- Poli (stiren) esaslı reçineler üzerinde sekonder amin sentezi ve aldehit ayrılması
Başlık çevirisi yok
BAHİRE FİLİZ ŞENKAL
- Production and characterization of activated carbon from sulphonated styrene divinyl benzene copolymer
Sülfonlanmış stiren divinil benzen kopolimerinden aktif karbon üretimi ve karakterizasyonu
WİSAM ABDALLAH
Yüksek Lisans
İngilizce
2004
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. HAYRETTİN YÜCEL
DR. CEVDET ÖZTİN
- Miscibility of halogenated and methylated poly (Phenylene oxide) with polystyene based ionomers and material haractristics of particle filled polyproplene
Halojenlenmiş ve metillenmiş poli (Fenilen oksit) lerin sülfonlanmış polistiran ve iyonomerleri ile karışabilirliği ve mineral parçacık dolgulu polipropilenin materyal karakteristikleri
MERYEM MIH
Yüksek Lisans
İngilizce
1997
KimyaOrta Doğu Teknik ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. LEYLA ARAS