2024-T3 alüminyum alaşımında pozitif ve negatif aşırı yüklerin çatlak ilerleme hızına etkileri
The effects of positive and negative overloads to fatigue crack growth rate in 2024-T3 aluminium alloy
- Tez No: 170732
- Danışmanlar: Y.DOÇ.DR. DİLEK TURAN
- Tez Türü: Yüksek Lisans
- Konular: Sivil Havacılık, Civil Aviation
- Anahtar Kelimeler: Yorulma, çatlak ilerlemesi, alüminyum, sabit genlikli yükleme, pozitif ve negatif aşırı yük, Fatigue, crack growth, aluminium, constant amplitude loading, positive and negative overloading
- Yıl: 2005
- Dil: Türkçe
- Üniversite: Anadolu Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Sivil Havacılık Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi 2024-T3 ALÜMİNYUM ALAŞIMINDA POZİTİF VE NEGATİF AŞIRI YÜKLERİN ÇATLAK İLERLEME HIZINA ETKİLERİ RAMAZAN KALE Anadolu Üniversitesi Fen Bilimleri Enstitüsü Sivil Havacılık Anabilim Dalı Danışman: Yard. Doç. Dr. Dilek TURAN 2005, 94 sayfa 2024-T3 Alüminyum alaşımı ile yapılan bu çalışmada pozitif ve negatif aşırı yüklerinin yorulma çatlak ilerleme hızına etkileri araştırılmıştır. Sabit genlikli yorulma deneyi 0.11 gerilme oranında yapılmıştır. Değişken genlikti yorulma deneylerinde, sabit genlikti yorulma deneyi üzerine aşırı yükler uygulanmıştır. Sırasıyla pozitif tek aşırı yük, negatif tek aşırı yük, negatif tek aşırı yükü takip eden pozitif tek aşın yük ve pozitif tek aşırı yükü takip eden negatif tek aşırı yük deneyleri yapılmıştır. Pozitif ve negatif aşırı yük oranları 1.4, 1.7 ve 2 olarak uygulanmıştır. Yapılan deneyler sonunda, belli uzunluklar arasındaki çevrim sayıları hesaplanarak sabit genlikli yorulma deneyine göre değişken genlikli yorulma deneylerindeki gecikmeler ve hızlanmalar belirlenmiştir. Negatif tek aşırı yük durumunda hızlanma gözlenirken yapılan diğer deneylerde aşırı yük oranına ve aşırı yüklerin dizilişine göre farklı oranlarda gecikmeler olmuştur.
Özet (Çeviri)
11 ABSTRACT Master of Science Thesis THE EFFECTS OF POSITIVE AND NEGATIVE OVERLOADS TO FATIGUE CRACK GROWTH RATE IN 2024-T3 ALUMINIUM ALLOY RAMAZAN KALE Anadolu University Graduate School of Sciences Civil Aviation Program Supervisor: Assist. Prof. Dr. Dilek TURAN 2005, 94 pages In this study realized with 2024-T3 Aluminium alloy, the effect of positive and negative overload on fatigue crack growth rate was investigated. The constant amplitude fatigue experiment was done at 0.11 stress ratio. In variable amplitude experiment overloads were superposed on top of constant amplitude fatigue experiment Positive single overload, negative single overload, negative single overload following positive single overload, and positive single overload following negative single overload experiments were performed in the order given. Positive and negative overload ratios were applied as 1.4, 1.7, and 2. At the end of the experiments, by calculating the number of cycles between specified lengths, retardations and accelerations in variable amplitude fatigue experiments with respect to constant amplitude fatigue experiments were determined. While in the case of negative single overload acceleration was observed; in other experiments, retardations of different ratios were realized depending on overload ratio and the sequence of overloads.
Benzer Tezler
- Detection and monitoring of small surface-breaking fatigue cracks in aluminium 2024-T3 by ultrasonic methods
2024-T3 alüminyum alaşımında yüzey yorulma çatlaklarının ultrasonik yöntemlerle tesbiti ve izlenmesi
FERHAT SONAT
Yüksek Lisans
İngilizce
2003
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. FİLİZ SARIOĞLU
DOÇ. DR. HAKAN GÜR
- 2024-T3 alüminyum alaşımının simüle edilmiş uçuş yükleri altında yorulma davranışı
Fatigue behaviour of 2024-T3 aluminium alloy under simplified flight simulation loading
DİLEK TETİK
- Aa 2024-T3 alüminyum alaşımının sürtünme karıştırma kaynağında işlem parametrelerinin mikroyapı ve mekanik özelliklere etkileri
The effects of process parameters on the microstructure and mechanical properties in friction stir welding of aa 2024-T3 aluminium alloy
ALANUR BİNAL
Yüksek Lisans
Türkçe
2006
Metalurji MühendisliğiEskişehir Osmangazi ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
YRD. DOÇ. NEDRET AYDINBEYLİ
- 2024-T3 Al alaşımının tek aşırı yük altında yorulma davranışı
The Fatigue behaviour of 2024-T3 Al alloy under single overloading
ADEM KARCI
Yüksek Lisans
Türkçe
2002
Metalurji MühendisliğiAnadolu ÜniversitesiSivil Havacılık Ana Bilim Dalı
Y.DOÇ.DR. DİLEK TURAN