Styrene-acrylonitrile copolymer impregnated cement bonded particle board
Sitiren-akrilonitril kopolimer emdirilmiş çimentolu yonga levha
- Tez No: 15507
- Danışmanlar: PROF.DR. GÜNGÖR GÜNDÜZ
- Tez Türü: Yüksek Lisans
- Konular: Kimya Mühendisliği, Chemical Engineering
- Anahtar Kelimeler: Basınç dayanımı, Darbe dayanımı, Eğilme dayanımı, Yonga levha, Çimentolu yonga levha, Particle board, cement bonded particle board, polymer impregnated cement bonded particle board, impregnation, compressive strength, tensile strength, flexural strength, impact strength, thickness swelling, Impact strength, Bending strength
- Yıl: 1991
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET SİTÎREN-AKRİLONtrRIL KOPOLÎMER EMDİRİLMİŞ ÇÎMENTOLU YONGA LEVHA ÎLTER, Emel Yüksek Lisans Tezi, Kimya Mühendisliği Bölümü Tez Yöneticisi : Prof. Dr. Güngör Gündüz. Eylül 1991, 49 Sayfa Bu araştırmada, çimentolu yonga levhaya sitiren-akrilonitril monomer karışımı emdirilmiş ve polimer emdirilmiş çimentolu yonga levha olarak adlandırılan yeni bir tür yapı malzemesi elde edilmiştir. Polimer emprenyesinin çimentolu yonga levhanın dayanıklılığı ve kalınlığına şişmesi üzerine etkileri incelenmiştir. Polimerleşme ısı-katalizor yardımı ile 60 °C de %3 benzoil peroksit kullanılarak yapılmıştır. Emdirme süresi 8 saat, çimentolu yonga levhaya yüklenen polimer % 18.3 bulunmuştur. Normal çimentolu yonga levhaya göre polimer emdirmesi basınç dayanımım 2.825 kez, çekme dayanımını ise 2.56 kez artırmaktadır. Eğilme dayanımı 4.63 kez artmıştır.Darbe dayanımındaki artış 1.68 kez olarak bulunmuştur. Normal çimentolu yonga levha ile karşılaştırıldığında polimer emdirilmişçimentonlu yonga levhaların kalınlığına şişmesinin daha az olduğu gözlenmiştir. Anahtar Sözcülükler: Yonga levha, çimentolu yonga levha, polimer emdirilmiş çimentolu yonga levha, emdirme, basınç dayanımı, çekme dayanımı, eğilme dayanımı, darbe dayanımı, kalınlığına şişme. Bilim Dalı Sayısal Kodu : 603. 03. 05 VI
Özet (Çeviri)
ABSTRACT STYRENE-ACRYLONTTRILE COPOLYMER IMPREGNATED CEMENT BONDED PARTICLE BOARD ; İLTER, Emel M.Sc. in Chemical Engineering Supervisor: Prof. Dr. Güngör Gündüz September 1991, 49 pages In the present research, the cement bonded particle board was impregnated with styrene, acrylonitrile copolymer and a new type of composite material which is called polymer impregnated cement bonded particle board was obtained. The effects of polymer impregnation on the strengths and also on the thickness swelling of these boards were investigated. The co-monomer was polymerized by termo catalytic means using 3% benzoyl peroxide as initiator at 60 °C. The impregnation time and polymer loading were found 8 hours and 18.3% respectively. Ill?t Compressive strength and tensile strength were increased by 2.825 and 2.56 times respectively. Polymer impregnation increased the flexural strength of cement bonded particle boards 4.63 times. The increase in impact strength was found 1.68 times. Also thickness swelling of polymer impregnated cement bonded particle board was found less compared to ordinary cement bonded particle board.
Benzer Tezler
- Saf ve cam elyaf takviyeli naylon 6 numunelerinin kalıplanması ve bazı özelliklerinin incelenmesi
Molding and determination of some properties of nylon 6 with and without glass fiber reinforcement
NİHAT AYDIN
- Correlation between hardness and chain statistics in weakly crosslinked styrene-acrylonitrile copolymer
Zayıf çapraz bağlı stiren-akrilonitril kopolimerinin sertliği ve bunun zincir istatistiğine bağımlılığı
MOUSTAFA DERNAİKA
Yüksek Lisans
İngilizce
2000
Kimya MühendisliğiOrta Doğu Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. GÜNGÖR GÜNDÜZ
- Stiren akrilonitril kopolimerlerinin fiziksel ve termodinamik özelliklerinin incelenmesi
Başlık çevirisi yok
MUSTAFA HAMDİ KARAGÖZ
- Syntheses and characterization of multi-functional initiators for star, block and cationic ring-opening polymerizations
Yıldız, blok ve katyonik halka-açılması polimerizasyonu için yeni çok-fonksiyonlu başlatıcıların sentezi ve karakterizasyonu
YUSUF ZİYA MENCELOĞLU
- Siklobütan Halkalı 2-hidroksietil metakrilat monomer ve polimerlerinin sentezi ve karakterizasyonu
Synthesis, characterization of monomer and polymers 2-hydroxyethyl metracrylate containing cyclobutane ring
KADİR DEMİRELLİ