Sabit restorasyonlarda kullanılan temel metal alaşımına uygulanan farklı yüzey işlemlerinin ve yapıştırıcı simanların bağlantı direnci üzerine etkilerinin değerlendirilmesi
An evaluation of the effects of various surface treatments procedures applied on the base metal alloys on the bonding stregth of luting cements used in fixed restorations
- Tez No: 129853
- Danışmanlar: PROF. DR. BENGÜL YURDUKORU
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Metal-siman bağlantısı, Rocatec, Tribokimyasal silika kaplama, Bağlantı direnci, Yapıştırıcı sunanlar, Metal-cement bonding, Rocatec, Tribochemical silica coating, Bond strength, dental luting cement
- Yıl: 2003
- Dil: Türkçe
- Üniversite: Ankara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
91 ÖZET Sabit Restorasyonlarda Kullanılan Temel Metal Alaşımına Uygulanan Farklı Yüzey İşlemlerinin ve Yapıştırıcı Sunanların Bağlantı Direnci Üzerine Etkilerinin Değerlendirilmesi Mekanik ve kimyasal retansiyon, dental restorasyonun klinik başarısı için son derece önemli bir faktördür. Buna bağlı olarak metal-siman arasındaki bağlantıda önemli bir problem ortaya çıkmaktadır. Metal alaşım ile siman arasındaki bağlantının desteklenmesi klinik olarak önemlidir. Eğer bu iki materyal arasında ayrılma varsa bu bölgedeki kırık ve çatlaklar mikroorganizmalar ve plak için elverişli bir ortam hazırlar. 50 um'lik AI2O3 ile pürüzlendirme, 250 um'lik AI2O3 ile pürüzlendirme, elektrolitik pürüzlendirme ve Rocatec sistem gibi 4 farklı yüzey retansiyon arttırıcı uygulamalar yapılan metal örneklerle, Bayer çinkofosfat siman, Rely-X Luting Vitremer rezin modifiye cam iyonomer siman ve Panavia F rezin siman gibi 3 farklı simanın fonksiyonel kuvvetler karşısındaki bağlantısının incelenmesi ve metal-siman arasında meydana gelecek olan fraktürlerin önce ışık mikroskobunda daha sonra yüzey tarama elektron mikroskobunda (SEM) değerlendirilmesi amaçlanmıştır. Araştırmamızda, 10 mm çapında 2 mm kalınlığında bir diskin merkezinden 90°'lik açıyla çıkan 20 mm uzunluğunda ve 2 mm çapında uzantısı olan Cr-Co temel metal alaşımından 240 adet örnek hazırlanmıştır. 50 um'lik AI2O3 ile pürüzlendirme, 250 um'lik AI2O3 ile pürüzlendirme, elektrolitik pürüzlendirme ve Rocatec Tribokimyasal Sistem, gibi 4 farklı yüzey retansiyon arttırıcı uygulamalar yapılan metal örneklere, Bayer çinko fosfat siman, Rely-X Luting Vitremer rezin modifiye cam iyonomer siman ve Panavia F rezin simanın fonksiyonel kuvvetler karşısındaki bağlantısını in vitro olarak incelenmiştir. 50 um'lik AI2O3 ile pürüzlendirme, 250 um'lik AI2O3 ile pürüzlendirme ve Rocatec Sistem uygulanan yüzeylerde Panavia F yapıştırıcı simanın en başarılı olduğu, çinkofosfat simanın ise en başarısız olduğu belirlenmiştir (p<0.01).92 Elektroliz işlemi uygulandığında yine Panavia F simanı en başarılı olurken (p<0.01) çinkofosfat siman ve Vitremer siman arasında bir farklılık bulunmamıştır. Çinkofosfat siman kullanıldığında yüzey retansiyon arttırıcı işlemler arasında istatistik olarak önemli bir fark bulunmamıştır. Ancak Vitremer siman ve Panavia F simanda Rocatec uygulanan örnekler en yüksek çekme direncine sahip olduğu, Elektroliz uygulanan yüzeylerde ise Vitremer siman ve Panavia F siman en düşük çekme direncine sahip olduğu tespit edilmiştir. Araştırmamızda ayrıca, metal-siman ara yüzeylerinin ışık mikroskobunda ve yüzey tarama elektron mikroskobunda incelenmesi sonucu, çinkofosfat siman ile yapıştırılan tüm örneklerde ağırlıklı olarak adeziv başarısızlık, Vitremer siman ile yapıştırılan Rocatec sistem uygulanmış örneklerde koheziv başarısızlık, 50 um'lik AI2O3 ile pürüzlendirme, 250 um'lik AI2O3 ile pürüzlendirme ve elektrolitik pürüzlendirme, yapılan örneklerde ağırlıklı olarak koheziv başarısızlık, Panavia F rezin siman ile yapıştırılan Rocatec sistem uygulanmış örneklerde tamamen koheziv başarısızlık, yine 50 um'lik AI2O3 ile pürüzlendirme ve 250 um'lik AI2O3 ile pürüzlendirme yapılan örneklerde de ağırlıklı olarak koheziv başarısızlık tespit edilmiştir.
Özet (Çeviri)
93 SUMMARY An Evaluation Of The Effects Of Various Surface Treatments Procedures Applied On The Base Metal Alloys On The Bonding Strength Of Luting Cements Used In Fixed Restorations Obtaining a reliable mechanical and chemical retention between restorative metal alloys and luting cements is one of the most important factor affecting the clinical success of a dental restoration. Failure in the bonding between a fixed restoration and the luting cement in the forms of fractures and cracks may allow accumulation of microorganisms and formation of plaque in these areas. The purpose of this study was to evaluate bond strengths between base metal alloy surfaces subjected to 4 different surface treatments and 3 different luting cements under functional loadings and also to investigate the type and nature of the failures by means of a light microscope and scanning electron microscope (SEM). In the present study 240 samples were prepared from Co-Cr base metal alloy. Grametrically the samples were compound of a disk 2 mm in thichness and 10 mm in diameter and a rod descending from the center of the disk with an angle of 90°. The rod was designed to standardize the position of the disk for the universal testing machine. Metal surfaces were subjected to 4 different surface treatments namely sandblasting with 50um and 250um AI2O3, electrolytic etching and the Rocatec tribochemical system in order to increase the retention to metal surfaces. 3 different luting cements, namely Bayer zinc phosphate cement, Rely X Luting Vitremer resin modified glass ionomer cement and Panavia F resin cement, were then applied to the metal samples. Tensile bond strengths of this luting agents were evaluated in vitro. Among the luting materials tested, Panavia F was found to obtain the most successful bondings on the surfaces treated with sandblasting 50um and 250um AI2O3 and the Rocatec system, while the zinc phophate was found to show the least successful bondings (p<0.01).94 When surfaces were treated using the electrolytic system, Panavia F showed the most successful bonding (p<0.01). No difference was observed between zinc phosphate cement and Vitremer. For zinc phosphate cement, no statistically significant differences were detected between 4 different surface treatments in terms of bond strengths. However, Vitremer and Panavia F luting agents demonstrated the highest tensile strength values, when surfaces of the samples were treated with the Rocatec system. On the electrolytically etched surfaces, Vitremer cements and Panavia F were detected to show the lowest tensile strength values. Investigations of the surfaces of the samples after tensile tests by means of light microscope and SEM revealed that the samples luted with the zinc phosphate cements showed adesive failures. The samples luted with Vitremer demonstrated cohesive failures sandblasting with 50um and 250um AI2O3 and electrolytically etching. Panavia F showed cohesive failures on the samples treated with the Rocatec. For the samples sandblasted with 50um and 250um AI2O3, cohesive failures were mostly observed.
Benzer Tezler
- Sabit protetik restorasyonlarda kullanılan nikel içerikli alaşımların serum immünoglobulin düzeylerine etkisi
Başlık çevirisi yok
REMZİ NİGİZ
Doktora
Türkçe
1991
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ.DR. S. NİLÜFER DENLİ
- Sabit protetik restorasyonlarda kullanılan farklı fiberle güçlendirilmiş kompozit yapıların yüzey sertliği, yüzey pürüzlülüğü ve sitotoksisitelerinin karşılaştırmalı olarak incelenmesi
Evaluation of surface hardness, surface roughness and cytotoxicity of different fiber reinforced composites used in fixed partial dentures
AYKUT TUNÇEL
Doktora
Türkçe
2005
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ.DR. ALİ KEMAL ÖZDEMİR
- İmplant üstü sabit protetik restorasyonlarda kullanılan farklı kaplama materyallerinin, stres dağılımına etkisi
The Effect of stress distribution of the veneering materials on the implant supported fixed prosthetic restorations
YALÇIN ÇİFTÇİ
Doktora
Türkçe
1998
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ŞENAY CANAY
- Titanyum destekli porselen restorasyonlarda mikrosızıntının incelenmesi
Evaluation of microleakage in titanium porcelain restorations
BÜLENT KAMA
- Protetik restorasyonlarda kullanılan değişik metal alaşımlarından, in vitro biyolojik ortamlarda, hızlandırılmış yöntemle serbestleşen bazı elementlerin belirlenmesi ve stotoksik etkilerinin hücre kültüründe incelenmesi
Accelerated release of elements from dental casting alloys into in vitro biological environments and their cytotoxicity assessed by MTT assay
NESLİHAN FADILOĞLU EFEOĞLU
Doktora
Türkçe
2004
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF.DR. BERRAN ÖZTÜRK