Plazmanın zirkonya indirekt kompozit rezin bağlantısına ve yüzey özelliklerine etkilerinin değerlendirilmesi
Evaluation of the effects of plasma on zirconia– indirect composite resin bonding and surface properties
- Tez No: 998784
- Danışmanlar: DOÇ. DR. ÜLKÜ TUĞBA KALYONCUOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Zirkonya, İndirekt kompozit, Lazer, Plazma, Islanabilirlik, Bağlanma dayanımı, Zirconia, Indirect composite, Laser, Plasma, Wettability, Bond strength
- Yıl: 2026
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Gülhane Diş Hekimliği Fakültesi (ankara)
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, 3Y-TZP zirkonya üzerine uygulanan soğuk atmosferik plazma (CAP) ve ytterbium fiber lazerin (YFL) yüzey ıslanabilirliği ile diş eti renginde indirekt kompozit rezinin zirkonya ile olan makaslama bağlanma dayanımı (SBS) üzerindeki etkilerini incelemek ve bu bağlantıya termal yaşlandırmanın etkisini değerlendirmek karşılaştırmaktır. Gereç ve Yöntem: Toplam 60 adet zirkonya örneği (KATANA Zirconia HT; Kuraray Noritake, Japonya) hazırlanmış, başlangıç temas açısı ve yüzey pürüzlülüğü ölçülmüştür. Örnekler kontrol, CAP ve YFL olmak üzere üç yüzey işlem grubuna ayrılmış; uygulamalar sonrası temas açıları ve yüzey pürüzlülüğü yeniden ölçülmüştür. Ardından tüm örneklere MDP içeren universal primer (G-Multi Primer; GC Corporation) uygulanmış ve diş eti renkli indirekt kompozit rezin (Gradia Plus Gum Shades Heavy Body GHB-2; GC Europe) silindirik kalıp kullanılarak zirkonya yüzeyine uygulanmıştır. Örnekler termal yaşlandırma uygulanmış ve uygulanmamış olmak üzere iki alt gruba ayrılmıştır. SBS testleri universal test cihazı ile gerçekleştirilmiş, kırık tipleri stereomikroskop altında analiz edilmiştir. Veriler bağımsız t-testi, tek yönlü varyans analizi (ANOVA) ve eşleştirilmiş (paired) t-testi kullanılarak analiz edilmiştir. Bulgular: Başlangıç temas açısı (o) değerleri gruplar arasında anlamlı olarak farklıdır (p=0,037). İşlem sonrası kontrol grubu, CAP ve YFL gruplarının temas açıları sırasıyla 50,310°, 10,119° ve 15,278° olup fark anlamlıdır (p=0,001). İşlem öncesi–sonrası analizleri CAP ve YFL gruplarında anlamlı düşüş göstermiştir (p=0,001). YFL grubunda yüzey pürüzlülüğü başlangıca göre anlamlı derecede artmıştır (p=0,001). Yaşlandırma yapılmayan kontrol, CAP ve YFL grupları için SBS değerleri sırasıyla 8,337 MPa, 5,580 MPa ve 10,683 MPa; yaşlandırma yapılan gruplarda ise 7,988 MPa, 6,685 MPa ve 13,066 MPa'dır. Yaşlandırma işlemi yalnızca YFL grubunda anlamlı artış göstermiştir (p=0,028); kontrol (p=0,725) ve CAP (p=0,124) gruplarında anlamlı farklılık yoktur. Sonuç:YFL yüzey işlemi SBS'yi artırırken, CAP uygulaması temas açısını düşürmesine rağmen bağlanma dayanımını arttırmamıştır. Bulgular, YFL'nin zirkonya–indirekt kompozit arayüzünde etkili bir yüzey işlemi yöntemi olduğunu göstermektedir. Termal yaşlandırma YFL grubunda anlamlı artış gösterirken, diğer gruplarda anlamlı değişiklik oluşturmamıştır.
Özet (Çeviri)
Aim: This in vitro study aimed to investigate the effects of cold atmospheric plasma (CAP) and ytterbium fiber laser (YFL) applied to 3Y-TZP zirconia on surface wettability and on the shear bond strength (SBS) between zirconia and a gingiva- colored indirect composite resin, as well as to evaluate the influence of thermal aging. Materials and Methods: Sixty zirconia specimens (KATANA Zirconia HT; Kuraray Noritake, Japan) were prepared, initial contact angles and surface roughness were measured. The specimens were assigned to three surface treatment groups: control, CAP, and YFL. After treatments, contact angles and surface roughness were remeasured. An MDP-containing universal primer (G-Multi Primer; GC Corporation) was applied, and gingiva-colored indirect composite resin (Gradia Plus Gum Shades Heavy Body GHB-2; GC Europe) was built onto the zirconia surface using a cylindrical mold. The specimens were divided into subgroups with and without thermal aging. SBS was measured using a universal testing machine, and failure types were analyzed under a stereomicroscope. Data were evaluated using independent t- test, one-way ANOVA, and paired t-test. Results: Pre-treatment contact angle values differed significantly among the groups (p = 0.037). Post-treatment contact angles for the control, CAP, and YFL groups were 50.310°, 10.119°, and 15.278°, respectively (p = 0.001). CAP and YFL groups showed significant decreases after treatment (p = 0.001). In the YFL group, the surface roughness increased significantly compared to the pre-treatment (p = 0.001). Non-aged SBS values for the control, CAP, and YFL groups were 8.337 MPa, 5.580 MPa, and 10.683 MPa, respectively; aged SBS values were 7.988 MPa, 6.685 MPa, and 13.066 MPa. Thermal aging significantly increased SBS only in the YFL group (p = 0.028), with no significant change in the control (p = 0.725) or CAP (p = 0.124) groups. Conclusion: YFL surface treatment enhanced SBS, whereas CAP reduced the contact angle but did not increase bond strength. These findings indicate that YFL is an effective surface treatment method for improving bonding at the zirconia–indirect composite interface.
Benzer Tezler
- Soğuk plazma uygulamasının dental zirkonyanın yüzey özelliklerine ve rezin simanla bağlantısına etkilerinin araştırılması
Evaluation of the effects of non-thermal atmospheric plasma treatment on surface properties and shear bond strength of zirconia ceramics
MERVE ALTUNTAŞ
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZLEM ÇÖLGEÇEN
- Soğuk plazma uygulamasının sabit protetik restorasyonların tamirindeki etkinliğinin incelenmesi
Investigation of the effectiveness of non-thermal plasma application on repair of fixed prosthetic restorations
MEHMET KÖSE
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZLEM ÇÖLGEÇEN
- Investigating the effects of micro arc oxidation (MAO) process on thermal and elevated temperature mechanical properties of AZ91 MG alloy
AZ91 MG alaşımlarının termal ve yüksek sıcaklık mekanik özelliklerine mikro ark oksidasyon (MAO) prosesinin etkilerinin incelenmesi
EKİN SELVİ
Doktora
İngilizce
2023
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
- Titanyum oksit ilaveli alümina zirkonya kompozitlerinin spark plazma sinterleme yöntemi ile üretimi ve karakterizasyonu
Production and characterization of the addition of TiO2 on alumina zirconia composites prepared by spark plasma sintering
ÖZDEN ORMANCI
Yüksek Lisans
Türkçe
2012
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLTEKİN GÖLLER
- Atmosferik plazma sprey yöntemiyle üretilmiş %6 – 8 YSZ termal bariyer kaplamaların porozitesinin yapay sinir ağları ile modellenmesi
Artificial neural networks modeling of porosity of 6 - 8% YSZ thermal barrier coatings produced with atmospheric plasma spray method
UTKU ORÇUN GEZİCİ
Yüksek Lisans
Türkçe
2017
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL YILMAZ TAPTIK