Geleneksel, CAD-CAM, 3D baskılı ve ışıkla sertleşen protez kaide materyallerinin yapay dişler ile olan bağlanma dayanımlarının karşılaştırılması
Comparison of the bond strengths of conventional, CAD-CAM, 3D printed and light-cured denture base materials with artificial teeth
- Tez No: 978661
- Danışmanlar: PROF. DR. FAİK TUĞUT
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Belirtilmemiş.
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Sivas Cumhuriyet Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada geleneksel ve güncel yöntemlerle üretilen kaide materyallerinin farklı yapay dişler arasındaki bağlanma dayanımlarının karşılaştırılması amaçlanmaktadır. Çalışmada 4 farklı yöntemle üretilen (Geleneksel, CAD-CAM, 3D yazıcı ve ışıkla sertleşen UDMA) protez kaide materyali ve 3 farklı yapay diş (akrilik, izosit ve 3D reçinesi ile üretilen diş) kullanıldı. Tüm kaide örnekleri 5,0 mm çapında ve 2,5 mm kalınlığında disk şeklinde üretildi. Yapay diş örnekleri ise üst 1. Molar diş olarak seçilip her birinin oklüzal yüzey tarafı otopolimerize akrilik reçine içerisine gömüldü. Bağlantı yüzeyine ise 4 farklı kaide materyaline özgün yapıştırma metodu uygulanarak diş ile kaide bağlantısı sağlandı. Bağlanma işlemi tamamlanan tüm örneklere termal siklus cihazında 5-55°C'de 5000 devir yapıldı. Termal siklus işleminden sonra örneklere universal test cihazında 5 mm/dk kafa hızında makaslama bağlanma dayanım testi uygulanıp değerler megapaskal (MPa) olarak kaydedildi. Kopma tipleri (adeziv, koheziv ve kombine kopma) yönünden değerlendirildi. Çalışmada elde edilen veriler SPSS (ver: 23.0) programına yüklenerek verilerin değerlendirilmesinde parametrik test varsayımları yerine getirilmediğinden (Shapiro-Wilk), bağımsız ikiden fazla gruptan elde edilen ölçümler karşılaştırılırken Kruskal Wallis testi, analiz sonucunda farklılık yapan grup ya da grupları bulabilmek için Mann Whitney U testi uygulandı. Yanılma düzeyi 0,05 olarak alındı. Tüm gruplara ait bağlanma dayanımı ölçümleri karşılaştırıldığında gruplar arası farklılık önemli bulundu (p<0,05). Çalışmanın sonucunda en yüksek bağlanma dayanımı değeri CAD-CAM kaide-izosit diş grubunda (13,95 ± 0,94 MPa) görüldü. En düşük değerler ise 3D kaide-akrilik diş (0,88 ± 0,12 MPa) ve 3D kaide-izosit diş (0,81 ± 0,11 MPa) gruplarında görüldü. Tüm gruplarda adeziv kopma tipi yaygın olarak gözlemlendi. Kaide üretim yönteminin veya yapay diş içeriğinin değişmesinin kaide-diş arasındaki bağlanma dayanımına etkisinin olduğu belirlendi.
Özet (Çeviri)
This study aims to compare the bonding strength of base materials produced using traditional and modern methods between different artificial teeth. The study used 4 different methods of production (traditional, CAD-CAM, 3D printer, and light-cured UDMA) for the prosthetic base material and 3 different types of artificial teeth (acrylic, isosite, and 3D resin teeth). All base samples were produced in the form of disks with a diameter of 5.0 mm and a thickness of 2.5 mm. The artificial tooth groups were selected as upper first molars, and the occlusal surface of each tooth was embedded in self-curing acrylic resin. The tooth was bonded to the base using a bonding method specific to each of the 4 different base materials. All samples with completed bonding were subjected to 5000 cycles at 5-55°C in a thermal cycling device. After the thermal cycling process, shear bond strength tests were performed on the specimens in a universal testing machine at a head speed of 5 mm/min, and the values were recorded in megapascals (MPa). The specimens were evaluated in terms of fracture types (adhesive, cohesive, and combined fracture).The data obtained in the study were loaded into the SPSS (version 23.0) program. Since the assumptions of parametric tests were not met (Shapiro-Wilk), the Kruskal-Wallis test was used to compare measurements obtained from more than two independent groups, and the Mann-Whitney U test was applied to identify the group or groups that differed in the analysis results. The difference level was set at 0.05. When comparing the bond strength measurements of all groups, a significant difference was found between the groups (p<0.05). The study results showed that the highest bond strength value was observed in the CAD-CAM base-isosit tooth group (13.95 ± 0.94 MPa). The lowest values were observed in the 3D base-acrylic tooth (0.88 ± 0.12 MPa) and 3D baseisosit tooth (0.81 ± 0.11 MPa) groups. Adhesive failure was commonly observed in all groups. It was determined that changes in the base production method or artificial tooth content affected the bond strength between the base and tooth.
Benzer Tezler
- Fabrıcatıon of 3D prınted flexıble polyurethane nanocomposıte
3b baskili esnek poliüretan nanokompozit imalati
ALİCAN MERT
Yüksek Lisans
İngilizce
2025
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiNanobilim ve Nanomühendislik Ana Bilim Dalı
DOÇ. DR. BİRGÜL BENLİ
- Yeşil sentez gümüş nanopartikül katkılı nanofiber ile güçlendirilmiş polimetilmetakrilat (PMMA) rezin kompozitlerin üretilmesi ve antimikrobiyal ve mekanik aktivitelerinin değerlendirilmesi
Production of polimethylmethacrylate (PMMA) resin composites with green synthesis silver nanoparticles doped nanofiber and evaluation of their antimicrobial and mechanical activities
MERYEM ERDOĞDU
Doktora
Türkçe
2024
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ALİ RIZA TUNÇDEMİR
- Farklı fırınlama sayılarının CAD-CAM ve 3D yazıcı ile üretilen zirkonyanın faz değişimi, optik ve mekanik özelliklerine etkisinin incelenmesi
Investigation of the effect of different firing numbers on phase change, optical and mechanical properties of CAD-CAM and 3D printed zirconia
FURKAN KARATAŞ
Doktora
Türkçe
2024
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ALPER ÖZDOĞAN
- CAD/CAM tekniği ve 3 boyutlu yazıcılarla hazırlanan üst hareketli tam protezlerde kaide plağı kalınlığının dinamik mekanik özelliklerle ilişkisinin incelenmesi
Evaluation of the dynamic mechanic properties of upper removable complete dentures manufactured by CAD/CAM milling and 3D printing techniques
BEGÜM AYŞE BUZBAŞ
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. HAYRUNNİSA CANAN BURAL ALAN
- Farklı CAD/CAM protez kaide materyallerinin mekanik özelliklerinin incelenmesi
Investigation of mechanical properties of different CAD/CAM denture base materials
SEÇİL SAKARYA
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. FUNDA BAYINDIR