Perlit ve pomza agregalı uçucu kül bazlı geopolimer harcın mekanik özellikleri üzerine kenevir lifi ilavesinin etkisi ve yaşam döngüsü değerlendirmesi
Effect of hemp fiber addition on mechanical properties and life cycle assessment of fly ash-based geopolymer mortar with perlite and pumice aggregate
- Tez No: 978554
- Danışmanlar: DOÇ. DR. SERHAN İLKENTAPAR
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Geopolimer, Kenevir lifi, Genleştirilmiş Perlit, Pomza, Kıtık, Mekanik özellikler, Mikro Yapı, Yaşam Döngüsü Değerlendirmesi, Geopolymer, Hemp fiber, Expanded Perlite, Pumice, Hemp shiv, Mechanical properties, Microstructure, Life Cycle Assessment
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Erciyes Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
İnşaat sektörü ve yapı malzemeleri, küresel ölçekte ciddi çevresel etkilere sahiptir. Özellikle çimento, dünya genelindeki CO₂ salınımının yaklaşık %8'ini oluşturmaktadır. Avrupa Yeşil Mutabakatı gibi uluslararası politikalar doğrultusunda, yapı sektöründe karbon salımının azaltılması hedeflenmektedir. Bu kapsamda, alternatif bağlayıcı sistemler olarak geopolimerler giderek daha fazla önem kazanmaktadır. Bu tez çalışmasında, genleştirilmiş perlit, pomza ve kenevir kıtığı gibi hafif agregalar kullanılarak uçucu kül bazlı geopolimer harçlar üretilmiş; sodyum hidroksit aktivatör olarak tercih edilmiştir. Ayrıca, bu harçlara farklı oran ve uzunluklarda kenevir lifi ilave edilerek lif katkısının performans üzerindeki etkileri araştırılmıştır. Harçlar 90 °C'de 24, 48 ve 72 saat kürlenmiştir. Kür sonrası işlenebilirlik, birim ağırlık, UPV, eğilme ve basınç dayanımı, yüksek sıcaklık dayanımı (300 °C, 600 °C, 900 °C), iç yapı (FESEM, EDX, Mapping, XRD) ve yaşam döngüsü analizleri yapılmıştır. Yaşam döngüsü değerlendirmesi kapsamında, en yüksek küresel ısınma potansiyeli (GWP) değeri tamamen kırtık agregalı PO-W100 ve MO-W100 harçlarında tespit edilirken, en düşük GWP değeri ise pomza ve kenevir lifi içeren M-3-0.75% karışımında elde edilmiştir. Sonuçlar, lif katkısının mekanik özellikleri iyileştirdiğini, çevresel etkileri ise azalttığını göstermiştir. Bu yönüyle çalışma, yapı malzemeleri alanına çevreci ve yenilikçi katkılar sunmaktadır.
Özet (Çeviri)
The construction sector and building materials have significant environmental impacts on a global scale. In particular, cement accounts for approximately 8% of global CO₂ emissions. In line with international policies such as the European Green Deal, reducing carbon emissions in the construction sector has become a primary goal. In this context, geopolymer binders have gained increasing importance as alternative systems. In this thesis study, fly ash-based geopolymer mortars were produced using lightweight aggregates such as expanded perlite, pumice, and hemp shiv, with sodium hydroxide selected as the alkaline activator. Additionally, hemp fibers of varying lengths and dosages were incorporated into the mortars to investigate their influence on performance. The mortars were cured at 90 °C for 24, 48, and 72 hours. Following curing, workability, unit weight, ultrasonic pulse velocity (UPV), flexural and compressive strength, high-temperature resistance (300 °C, 600 °C, and 900 °C), microstructural characteristics (FESEM, EDX, Mapping, XRD), and life cycle assessments (LCA) were conducted. Within the LCA scope, the highest global warming potential (GWP) values were observed in PO-W100 and MO-W100 mixtures containing 100% hemp shiv aggregate, while the lowest GWP was recorded in the M-3-0.75% mix with pumice and hemp fiber. The results revealed that fiber incorporation enhanced mechanical performance and reduced environmental impacts. Thus, the study offers innovative and eco-friendly contributions to the field of construction materials.
Benzer Tezler
- Yalıtımlı hafif beton kiremit üretimi
Production of lightweight insulating concrete roof tile
TAMER EFE
Yüksek Lisans
Türkçe
2011
Maden Mühendisliği ve MadencilikSüleyman Demirel ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. LÜTFULLAH GÜNDÜZ
- Kendiliğinden yerleşen taşıyıcı hafif betonun mekaniksel ve durabilite özelliklerinin araştırılması
Investigation of properties of durability and mechanical of self compacting structural lightweight concrete
TAHİR GÖNEN
- Hafif agregalı kendiliğinden yerleşen harçların mekanik ve durabilite özellikleri
Mechanical and durability properties of self compacting mortar with ligthweight aggregate
BİLAL BALUN
Yüksek Lisans
Türkçe
2013
İnşaat MühendisliğiFırat Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MEHMET KARATAŞ
- Hafif agregalı betonun boşluk yapısının mekanik ve fiziksel özelliklere etkisi
The effect of pore structure on mechanical and physical properties of lightweight aggregate concrete
NİHAT KABAY
Doktora
Türkçe
2009
İnşaat MühendisliğiYıldız Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. FEVZİYE AKÖZ
- Pomza ve perlit agregası içeren mineral katkılı taşıyıcı hafif betonların enerji performansı açısından değerlendirilmesi
Evaluation of mineral additives added structural lightweightconcrete containing pumice and perlite aggregates in terms ofenergy performance
SAFA NAYIR
Doktora
Türkçe
2021
İnşaat MühendisliğiKaradeniz Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. ŞAKİR ERDOĞDU