Düşük şamot içerikli FFC seramik sağlık gereçleri reçetelerinin geliştirilmesi
Development of FFC ceramic sanitaryware bodies with reduced chammotte content
- Tez No: 975563
- Danışmanlar: PROF. DR. ALPAGUT KARA
- Tez Türü: Yüksek Lisans
- Konular: Seramik Mühendisliği, Mühendislik Bilimleri, Ceramic Engineering, Engineering Sciences
- Anahtar Kelimeler: Kalsine hammadde, Reolojik özellikler, Vitrifiye seramikler, Calcined material, Rheologic properties, Vitrified ceramics
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Eskişehir Teknik Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilimi ve Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Seramik sağlık gereçleri; inorganik-metalik olmayan hammaddelerin belirli oranlarda karıştırılarak akışkan bir çamur haline getirilmesi, daha sonra da alçı ve/veya sentetik reçine kalıplarda şekillendirilerek 1200–1250⁰C civarında pişirilen ürünlerdir. Fine Fire Clay (FFC) bünyeler, vitrifiye (VC) bünyelere kıyasla daha düşük deformasyon eğilimine sahip olmakla birlikte su emme oranları daha yüksektir. Düşük deformasyon gereksinimi nedeniyle bu bünyelerin kompozisyonlarında %30-%40 oranında şamot hammaddesi kullanılmaktadır. FFC ürünlerde üretim maliyetlerinde önemli bir etken olan şamot, yüksek sıcaklıkta gerçekleştirilen ısıl işlemler sonucu üretilen maliyetli bir yarı mamul olup, üretim sürecinde ortaya çıkan CO₂, karbon ayak izi açısından da olumsuz bir etkendir. Bu çalışmanın amacı, FFC reçetelerinden şamotun çıkarılması ve/veya reçete kullanım oranının düşürülmesiyle standart FFC reçetesinin teknik özelliklerine paralel ve reolojik olarak SSG üretimine uygun, düşük maliyetli reçete kompozisyonları geliştirmektir. Bu doğrultuda, sistematik bir şekilde kompozisyonlarda feldispat kullanımı kaldırılmış, şamot yerine özlü hammadde oranları artırılmış ve reçetelere wollastonit ilavesi gerçekleştirilmiştir. Yapılan kompozisyonel değişiklikler sonucunda mikroyapıda anortit ve kristobalit fazlarının oluşumu gözlemlenmiş, ayrıca malzemenin piroplastik indeks değeri düşürülmüştür. Çalışma sonucunda, şamot içermeyen ancak endüstriyel standartlara uygun FFC reçeteleri geliştirilmiştir.
Özet (Çeviri)
Sanitaryware ceramics are products manufactured by mixing inorganic, non-metallic raw materials in specific proportions to form a casting slip. This slip is then shaped in plaster and/or synthetic resin molds and subsequently fired at temperatures around 1200–1250°C. Fine Fire Clay (FFC) bodies are characterized by higher water absorption and lower deformation ratio compared to vitreous china bodies. Due to the low deformation requirement, 30-40% chamotte is used in the composition of these bodies. Chamotte, which is a significant factor in the production costs of FFC products, is an expensive semi-finished product produced as a result of thermal processes carried out at high temperatures and is also a negative factor in terms of CO₂ emissions and carbon footprint during the production process. The aim of this study is to develop low-cost recipe compositions that are parallel to the technical properties of the standard FFC recipe and suitable for CSW production in terms of rheology by removing chamotte from FFC recipes and/or reducing the recipe usage rate. In this regard, feldspar use was systematically eliminated from the compositions, the proportion of plastic raw materials was increased instead of chamotte, and wollastonite was added to the recipes. As a result of the compositional changes made, the formation of anorthite and cristobalite phases in the microstructure was observed, and the pyroplastic index value of the material was reduced. As a result of the study, FFC recipes that do not contain chamotte but comply according to industrial standards have been developed.
Benzer Tezler
- Bazı kil minerallerinin ve kil bazlı seramiklerin kuruma davranışlarının incelenmesi
The Investigation of drying behaviour of some clay based ceramics
GÜLCAN CARAN
Yüksek Lisans
Türkçe
2003
Seramik MühendisliğiDumlupınar ÜniversitesiSeramik Mühendisliği Ana Bilim Dalı
DOÇ. DR. İSKENDER IŞIK
- Obtaining renewable energy by optimization of the performance and emission responses of the diesel engine with rsm using environmentally friendly fuel blends
Çevre dostu yakıt karışımları kullanılarak dizel motorun performansı ve emisyon tepkilerinin rsm ile optimize edilmesi ile yenilenebilir enerji elde edilmesi
HAIDER NASHAAT HASSEN TAHA
Yüksek Lisans
İngilizce
2023
Makine MühendisliğiKarabük ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. SAMET USLU
- CAD/CAM yardımıyla kişiye özel hazırlanmış polietereterketon post-korların kırılma dayanımlarının değerlendirilmesi
Evaluation of the fracture strength of CAD/CAM milled custom polyetheretherketone dental post-cores
AYETULLAH DİREK
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ SAMET TEKİN
- Yaşlanmada ve nörodejenerasyonda işlevsel bağlantısallığın, emosyonel yüz ifadeleri uyaranı ve EEG olaya-ilişkin koherans yöntemi ile incelenmesi
Investigation of functional connectivity in aging and neurodegeneration by emotional face stimuli and EEG event-related coherence
SAMET HAKAN UZUNLAR
Yüksek Lisans
Türkçe
2022
Nörolojiİstanbul Medipol ÜniversitesiSinir Bilim Ana Bilim Dalı (disiplinlerarası)
PROF. DR. BAHAR GÜNTEKİN
- Şamot refrakter malzemenin mekanik, ısıl ve korozyon direnci özelliklerine hassas döküm atık kumlarının etkilerinin araştırılması
Investigation of the effect of precision casting waste sands on the mechanical, thermal and corrosion resistance properties of chamotte refractory material
VEYSEL MURAT BOSTANCI
Doktora
Türkçe
2022
Metalurji MühendisliğiNecmettin Erbakan ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. TUBA BAHTLI